Effect of fluid resins on the surface roughness and topography of resin composite restorations analyzed by atomic force microscope

The aim of the study was to verify the influence of surface sealants on the surface roughness of resin composite restorations before and after mechanical toothbrushing, and evaluate the superficial topography using atomic force microscope. Five surface sealers were used: Single Bond, Opti Bond Solo Plus, Fortify, Fortify Plus and control, without any sealer agent. The lowest values of surface roughness were obtained for control, Single Bond and Fortify groups before toothbrushing. Fortify and Fortify Plus were the sealer agents that support the abrasive action caused by the toothbrushing although Fortify Plus group remained with high values of surface roughness. The application of specific surface sealants could be a useful clinical procedure to maintain the quality of resin-based composite restorations. (C) 2010 Elsevier Ltd. All rights reserved.

Assessing the surface roughness of a posterior resin composite: effect of surface sealing

This study assessed the in vitro influence of surface sealing on the surface roughness of a posterior resin composite before and after tooth-brushing. Thirty. specimens (13 nun diameter x 1 mm high) were fabricated from Filtek-P60 resin composite and randomly assigned to three groups (n=10): a non-sealed control and two groups sealed with one of the tested materials-a surface-penetrating sealant (Protect-it!-PI) and a one bottle adhesive system (Single Bond-SB). The samples were subjected to a surface roughness reading to determine the initial roughness, then submitted to simulated toothbrushing with 35,600 cycles for 100 minutes. Specimens were then cleaned and a post-abrasion surface roughness reading accomplished. Means (pm), recorded before (B) and after (A) toothbrushing, and standard deviations were: Control-(B): 0.032 (+/-0.005), (A): 0.054 (+/-0.005); PI-(B): 0.034 (+/-0.005), (A): 0.060 (+/-0.034); SB (B): 0.031 (+/-0.004), (A): 0.047 (+/-0.007). Data were tabulated and submitted to two-way ANOVA. No statistically significant difference was observed when the control and experimental groups were compared. However, a significant difference (p<0.05) was found between the measurements performed before and after toothbrushing. Based on these results, it may be concluded that using either a surface penetrating sealant or a one bottle adhesive system did not provide the optimization of superficial integrity. The use of a dentifrice and toothbrush resulted in significant alterations to the surface smoothness of the resin composite.

In vitro evaluation of surface roughness of 4 resin composites after the toothbrushing process and methods to recover superficial smoothness.

OBJECTIVE: This study evaluated the efficiency of repolishing, sealing with surface sealant, and the joining of both in decreasing the surface roughness of resin-based composites after a toothbrushing process. METHOD AND MATERIALS: Ten specimens of each composite (Alert, Z100, Definite, and Prodigy Condensable), measuring 2 mm in thickness and 4 mm in diameter, were made and submitted to finishing and polishing processes on both sides of the specimens using the Sof-Lex system. The specimens were then subjected to toothbrushing (30,000 cycles), and surface roughness (Ra) was analyzed with a Surfcorder SE 1700 profilometer. The upper surface of each composite was etched with 37% phosphoric acid, and the surface-penetrating sealant Protect-it was applied on 1 surface. The roughness of these surfaces was again measured. On the other side, the surface of the specimen was repolished, and the efficiency of this procedure was measured using the profilometer. The surface roughness resulting from the joining of the 2 methods was verified by applying, in the final stage, the surface-penetrating sealant on the repolished surface. Data were analyzed with analysis of variance and Tukey test (P <.05). RESULTS: Results showed that the lowest surface roughness values were obtained for Definite, Z100, and Prodigy Condensable after the repolishing process and after the repolishing plus sealing. For Alert, the joining of repolishing plus sealing promoted the lowest values of surface roughness. CONCLUSION: Of the resin-based composites, Alert demonstrated the highest values of surface roughness in all the techniques tested.

Estudo da dureza e da resistência à compressão de resinas compostas para dentes posteriores após a imersão em água destilada. Efeito da aplicação de selante superficial

Novos compósitos têm surgido no mercado especificamente destinados à confecção de restaurações estéticas posteriores. Entretanto, embora tais materiais apresentem resultados iniciais animadores, há a necessidade de comprovações adicionais para que possam ser utilizados com segurança. Resinas compostas posteriores são submetidas a estresses complexos de compressão e abrasão durante a mastigação e a aplicação de selantes superficiais tem sido relatada como forma de aumentar a resistência ao desgaste destes materiais. O presente trabalho teve como propósito avaliar a dureza e a resistência à compressão das resinas compostas Alert (Jeneric/Pentron), Ariston (Vivadent), Definite (Degussa), P60 (3M), Solitarie (Kulzer), Surefil (Dentsply) e Z100 (3M) após 90 dias de imersão em água destilada, recobertas com selante Protect It (Jeneric/Pentron) e submetidas à ciclagem mecânica (10.000 ciclos, 600N, 5Hz). Os ensaios de dureza (n=8) foram realizados em aparelho Wolpert, com diamante Vickers e peso de 50gf aplicado por 30 segundos, antes e após períodos de imersão de 30, 60 e 90 dias. Os ensaios de resistência à compressão (n=8) foram realizados somente após 90 dias, em corpos-de-prova cilíndricos medindo 8mm de altura por 4mm de diâmetro. Apenas os espécimes destinados à compressão foram ciclados mecanicamente. Os ensaios foram realizados em máquina MTS 810, equipada com célula de carga de 10kN (ciclagem) e 100kN (compressão) e velocidade de 0,5mm/min. Após análise de variância (p<0,05), os resultados mostraram, previamente à imersão, maiores valores de dureza para os materiais Z100 (74,253VHN) e Ariston (71,308VHN). A seguir, com valor semelhante à resina Ariston, mas inferior à resina Z100, apresentou-se o material Surefil (69,969VHN)...(Resumo completo, clicar acesso eletrônico abaixo)

Influence of surface sealant on the translucency of composite resin: effect of immersion time and immersion media

This study evaluated the effect of surface sealant on the translucency of composite resin immersed in different solutions. The study involved the following materials: Charisma, Fortify and coffee, Coca-Cola®, tea and artificial saliva as solutions. Sixty-four specimens (n = 8) were manufactured and immersed in artificial saliva at 37 ± 1 °C. Samples were immersed in the solutions for three times a day and re-immersed in artificial saliva until the translucency readings. The measurements were carried out at nine times: T1 - 24 hours after specimen preparation, T2 - 24 hours after immersion in the solutions, T3 - 48 hours and T4 to T9 - 7, 14, 21, 30, 60 and 90 days, respectively, after immersion. The translucency values were measured using a JOUAN device. The results were subjected to ANOVA and Tukey's test at 5%. The surface sealant was not able to protect the composite resin against staining, the coffee showed the strongest staining action, followed by tea and regarding immersion time, a significant alteration was noted in the translucency of composite resin after 21 days.

Effect of the composite surface sealant application moment on marginal sealing of compactable composite resin restoration

An analysis was carried out to observe whether the application or not of a composite surface sealant (CSS), as well the moment for CSS application were able to reduce marginal microleakage in compactable composite resin restoration. All the preparations were restored with a compactable composite resin. The restored teeth were randomly assessed. G1 (control group): finished and polished; G2: finished, polished, etched and cover with CSS; G3: immediately after the restoration done the CSS was applied, then finished and polished; G4: CSS applied immediately after the restoration was done, the finished and polished, etched, and covered with CSS. The specimens were isolated with nail polish, thermocycled, immersed in aqueous solution of silver nitrate, and followed in a photo developing solution. The microleakage scores obtained from the occlusal and cervical walls were analyzed with the Kruskall-Wallis nonparametric test. No microleakage was found at the enamel margins. Comparing the microleakage scores at dentin/cementum margins (p < 0.05) it was found that G3 (p = 0.0162) and G4 (p = 0.0187) were able to reduce microleakage when compared with group G2. However the results were not statistically different from the control group. The application of CSS was not able to completely eliminate marginal microleakage at the dentin/cementum margins.

Measurement of sealant surface area by clinical/computerized analysis: 11-year results.

OBJECTIVE: To analyze the clinical behavior of 2 pit and fissure sealants through clinical/computerized evaluation. METHOD AND MATERIALS: Occlusal sealants were placed on maxillary and mandibular first and second premolars according to a split-mouth design. All premolars were sealed with either Concise (3M Espe) or Prisma Shield (Caulk/Dentsply) sealant agents. A hematoxylin-based staining solution was applied on the occlusal surface 7 days, 18 months, 36 months, and 11 years after occlusal sealing to allow checking of the sealant material on the surface. At each analysis time all occlusal surfaces were photographed, and the photographs corresponding to each time period were analyzed with SigmaScan 4.0 Software. The alterations of the sealed area of each sealant were analyzed with the software and recorded. Next, the measurements of the areas were tabulated and analyzed according to each period. Analysis of variance (ANOVA), with parts subdivided into time, and the t test, with a significance level of 5%, were used. RESULTS: The greatest sealed area was maintained by the sealant Concise. However, over the course of 11 years, all sealants began to show the same level of alteration in sealed area. CONCLUSION: The sealing materials showed alteration in sealed area over time, but they were efficient in controlling caries lesion formation on premolar pits and fissures.

Fluorescence Intensity of Composite Layering Combined with Surface Sealant Submitted to Staining Solutions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Relationship between DIAGNOdent values and sealant penetration depth on occlusal fissures

The aim of this in vitro study was to evaluate the relationship between laser fluorescence values and sealant penetration depth on occlusal fissures. One hundred and sixty-six permanent molars were selected and divided into four groups, which were each treated using a different sealant (two clear and two opaque). The teeth were independently measured twice by two experienced dentists using two laser fluorescence devices-DIAGNOdent (LF and LFpen)-before and after sealing, and then thermoclycled. After measuring, the teeth were histologically prepared and assessed for caries extension. Digital photographs of the cut sealed sites were assessed, and the sealant penetration depth was measured. All 166 sites were measured by one of the examiners taking as limits the outer and inner surface of the sealant into the fissure. For each device (LF and LFpen) and each group, the difference between the values at baseline and after sealing was plotted against the sealant penetration depth and scatter plots were provided. It could be observed that most of the points were concentrated around the zero line, for both LF and LFpen in the four groups. In conclusion, there is no relation between changes in DIAGNOdent values and increasing of depth sealant penetration within the occlusal fissures.

Use of one-bottle adhesive as an intermediate bonding layer to reduce sealant microleakage on saliva-contaminated enamel

Purpose: To evaluate the influence of three different adhesives, each used as an intermediary layer, on microleakage of sealants applied under condition of salivary contamination. Materials and Methods: Six different experimental conditions were compared, 3 with adhesives and 3 without. After prophylaxis and acid etching of enamel, salivary contamination was placed for 10 s. In Group SC the sealant was applied after saliva without bonding agent and then light-cured. In Group SCA, after saliva, the surface was air dried, and then the sealant was applied and cured. In Groups ScB, SB and PB, a bonding agent (Scotchbond Dual Cure/3M, Single Bond/3M and Prime & Bond 2.1/Dentsply, respectively) was applied after the saliva and prior to the sealant application and curing. After storage in distilled water at 37°C for 24 hrs, the teeth were submitted to 500 thermal cycles (5°C and 55°C), and silver nitrate was used as a leakage tracer. Leakage data were collected on cross sections as percentage of total enamel-sealant interface length. Representative samples were evaluated under SEM. Results: Sealants placed on contaminated enamel with no bonding agent showed extensive microleakage (94.27% in SC; 42.65% in SCA). The SEM revealed gaps as wide as 20 μm in areas where silver nitrate leakage could be visualized. In contrast, all bonding agent groups showed leakage less than 6.9%. Placement of sealant with a dentin-bonding agent on contaminated enamel significantly reduced microleakage (P< 0.0001). The use of a bonding agent as an intermediary layer between enamel and sealant significantly reduced saliva's effect on sealant microleakage.

Effect of 10% carbamide peroxide dental bleaching on microhardness of filled and unfilled sealant materials

Purpose: The purpose of this study was to quantitatively evaluate the effect of 10% carbamide peroxide on the microhardness of pit and fissure sealant materials. Methods: Fluroshield, Vitroseal Alfa, and one unfilled (Clinpro) sealants were placed in Teflon matrices (4 mm in diameter by 2 mm in height) and polymerized for 40 seconds. A total of 20 specimens were prepared for each material, in which half were assigned as the control group (stored in artificial saliva and no bleaching treatment). For the remaining half, Clarigel Gold bleaching agent (10% carbamide peroxide) was placed over the specimen surface for 4 hours/day during 4 weeks. When specimens were not under bleaching treatment, they were kept in artificial saliva. Afterwards, specimens were subjected to Knoop microhardness testing using a 25-g load for 5 seconds. Five measurements were made on the sealants' surfaces and then calculated in Knoop hardness values. The data were statistically analyzed by two-way analysis of variance and Tukey's tests with a 5% confidence level. Results: The results of this in vitro study showed that the application of a carbamide peroxide-based bleaching material significantly affected the microhardness values of filled sealant materials. The bleaching agent did not affect the microhardness of the unfilled sealant. CLINICAL SIGNIFICANCE: The results of this in vitro study suggest that the bleaching agents altered the surface hardness of filled sealant restorative materials. This could possibly lead to increased wear and surface roughness. © 2006, Copyright the authors.

Influence of surface sealants on microleakage of composite resin restorations

Purpose: The purpose of this study was to verify the influence of surface sealants and dentin adhesive systems on the microleakage of composite restorations. Methods: Class V cavities were made on the buccal faces of 100 permanent third molars and restored with Z250. After 24 hours, they were submitted to polishing and finishing processes. The teeth were divided into groups according to the sealant agent: group 1 - Single Bond; group 2 - Opti Bond Solo Plus; group 3 - Fortify; group 4 - Fortify Plus; and group 5 - control without sealant. The analysis of immediate microleakage was performed in 10 restorations from each group, soon after the sealing. The other 10 specimens from each group were submitted to tooth-brushing and thermal cycles. The teeth were isolated and immersed in 2% methylene blue solution, washed in tap water, and sectioned in the buccolingual direction. The percentage of marginal leakage was calculated using an image analysis program, and results were submitted to analysis of variance and Tukey's test. Results: All the sealed groups demonstrated lower microleakage values compared to the control group. Group 3, sealed with Fortify, presented the lowest mean microleakage values. Conclusion: The application of surface sealants effectively decreased the microleakage in composite resin restorations.