Hydrogen embrittlement in an AISI 1045 steel component of the sugarcane industry

This paper will present a failure analysis of a chain component, manufactured with AISI 1045 steel and used for sugarcane transport. During the fabrication process, this component is submitted to induction hardening, just on one surface, before the galvanizing process. The occurrence of surface cracks, during storage, disables the usage of these components. Chemical and metallographic analyses, tensile, fracture toughness, and hardness tests, and fractography were conducted in order to determine the causes of failure. The steel chemical composition was in accordance with AISI 1045. The metallographic analyses and fractography did not exhibit the presence of zinc into the cracks; this is an indication that the cracks occurred after the galvanizing process. Tensile and fracture toughness test results are as expected. The crack surface and the fracture toughness specimen surfaces showed two different fracture micromechanisms: dimples and intergranular. The delayed fracture associated with the predominance of intergranular fracture micromechanism at the induction hardened layer and the high hardness level is a clear indication of the hydrogen embrittlement. (c) 2008 Elsevier Ltd. All rights reserved.

Interaction between recrystallization and strain-induced precipitation in a high Nb- and N-bearing austenitic stainless steel: influence of the interpass time

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Manufatura enxuta voltado para industrias siderúrgicas que utilizam sistemas de produção sob encomenda: um estudo de caso de uma empresa siderúrgica nacional

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of electroless nickel interlayer on the fatigue strength of chromium electroplated AISI 4340 steel

Deposition of wear-resistant hard chromium plating leads to a decrease in the fatigue strength of the base material. Despite the effective protection against wear and corrosion, fatigue life and environmental requirements result in pressure to identify alternatives or to improve conventional chromium electroplating mechanical characteristics. An interesting, environmentally safer and cleaner alternative for the replacement of hard chronic plating is tungsten carbide thermal spray coating, applied by high velocity oxyfuel (HVOF) process.To improve the fatigue strength of aeronautical steel chromium electroplated, shot peening is a successfully used method. Multiple lacer systems of coatings are considered to have larger resistance to crack propagation in comparison with simple layer.The aim of this study was to analyze the effect of nickel underplate on the fatigue strength of hard chromium plated AISI 4340 steel in two mechanical conditions: HRc 39 and HRc 52.Rotating bending fatigue tests results indicate that the clectroless nickel plating underlayer is responsible for the increase in fatigue strength of AISI 4340 steel chromium electroplated. This behavior may be attributed to the largest toughness/ductility and compressive residual stresses which, probably, arrested or delayed the inicrocrack propagation from the hard chromium external layer. The compressive residual stress field (CRSF) induced by the electroplating process was determined by X-ray diffraction method. The evolution of fatigue strength compressive residual stress field CRSF and crack sources are discussed and analyzed by SEM. (c) 2006 Elsevier Ltd. All rights reserved.

Effects of surface treatments on the fatigue strength of AISI 4340 aeronautical steel

Internal residual stresses significantly influence the fatigue strength of coated materials. It is well known that chromium plating is the most used electrodeposited coating for important industrial applications. However, pressure to identify alternatives or to improve the chromium electroplating process have increased in recent years, related to the reduction in fatigue strength of the base material and to environmental requirements. The high efficiency and fluoride free hard chromium electroplating there called accelerated) is an improvement to the conventional process. One environmentally safer and cleaner alternative to hard chromium plating is tungsten carbide thermal spray coating applied by the High Velocity Oxy-Fuel (HVOF) process. To increase the fatigue strength of chromium plated materials, coating thickness and microcracks density are important parameters to be controlled. Techniques as compressive residual stresses induced by shot peening and multilayers, are also used. The aim of this study was to analyse the effects on AISI 4340 steel, in the rotating bending fatigue behaviour, of the: tungsten carbide thermal spray coating applied by HP/HVOF process; chemical nickel underplate, and shot peening process applied before coating deposition, in comparison to hard chromium electroplatings. Rotating bending fatigue test results indicate better performance for the conventional hard chromium plating in relation to the accelerated hard chromium electroplating. Tungsten carbide thermal spray coating and accelerated hard chromium plate over nickel resulted in higher fatigue strength when compared to samples conventional or accelerated hard chromium plated. Shot peening showed to be an excellent alternative to increase fatigue strength of AISI 4340 steel hard chromium electroplated. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Evaluation of WC-17Co and WC-10Co-4Cr thermal spray coatings by HVOF on the fatigue and corrosion strength of AISI 4340 steel

It is known that chromium electroplating is related to the reduction in the fatigue strength of base metal. However, chromium results in protection against wear and corrosion combined with chemical resistance and good lubricity. Environmental requirements are an important point to be considered in the search for possible alternatives to hard chrome plating. Aircraft landing gear manufactures are considering WC thermal spray coating applied by the high-velocity oxygen-fuel (HVOF) process an alternative candidate, which shows performance at least comparable to results, obtained for hard chrome plating. The aim of this study is to compare the influence of WC-17Co and WC-10Co-4Cr coatings applied by HVOF process and hard chromium electroplating on the fatigue strength of AISI 4340 steel, with and without shot peening. S-N curves were obtained in axial fatigue test for base material, chromium plated and tungsten carbide coated specimens. Tungsten carbide thermal spray coating results in higher fatigue strength when compared to hard chromium electroplated. Shot peening prior to thermal spraying showed to be an excellent alternative to increase fatigue strength of AISI 4340 steel. Experimental data showed higher axial fatigue and corrosion resistance in salt fog exposure for samples WC-10Co-4Cr HVOF coated when compared with WC-17Co. Fracture surface analysis by scanning electron microscopy (SEM) indicated the existence of a uniform coverage of nearly all substrates. (C) 2004 Elsevier B.V. All rights reserved.

Effect of cerium (IV) ions on the anticorrosion properties of siloxane-poly(methyl methacrylate) based film applied on tin coated steel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steel

Despite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental requirements causes one to search for possible alternatives. To improve the fatigue and corrosion resistance of AISI 4340 steel, an experimental study has been made for an intermediate electroless nickel layer deposited on base metal. The objective of this study was to analyze the effect of nickel underplate on the fatigue and corrosion strength of hard-chromium-plated AISI 4340 steel. Deposition of the conventional wear-resistant hard chromium plating leads to a decrease in mechanical properties of the base metal, especially the fatigue strength. Rotating bending fatigue tests results indicate better performance for conventional hard chromium plating. Good corrosion resistance in salt fog exposure was obtained for the accelerated hard chromium plating. Experimental data showed higher fatigue and corrosion resistance for samples prepared with accelerated hard chromium plate over electroless nickel plate, when compared with samples without electroless nickel underplate.

Analysis of diametrical wear of grinding wheel and roundness errors in the machining of steel VC 131

Due to the high industrial competitiveness, the rigorous laws of environmental protection, the necessary reduction of costs, the mechanical industry sees itself forced to worry more and more with the refinement of your processes and products. In this context, can be mentioned the need to eliminate the roundness errors that appear after the grinding process. This work has the objective of verifying if optimized nozzles for the application of cutting fluid in the grinding process can minimize the formation of the roundness errors and the diametrical wear of grinding wheel in the machining of the steel VC 131 with 60 HRc, when compared to the conventional nozzles. These nozzles were analyzed using two types of grinding wheels and two different cutting fluids. Was verified that the nozzle of 3mm of diameter, integral oil and the CBN grinding wheel, were the best options to obtain smaller roundness errors and the lowest diametrical wears of grinding wheels.

Production of an axial piston: Impacts resulting from the substitution of steel by a polymer-based material

The substitution of steel as a raw material in the production of axial pistons for pressure washers by polyphthalamide, polytetrafluoroethylene and glass fiber-based composite was studied. The new production process with composite consists of only two steps, while the production of the steel piston is to comprise of thirteen steps. This replacement would result in an estimated reduction of 80% of water consumption, 83% of electricity consumption, 73% of the total cost and 88% of the final mass. With regard to the main mechanical properties required for the end product, the composite was found to withstand the critical axial loads and it shows acceptable wear resistance in an environment without lubrication, an additional advantage of this replacement. © 2012 Elsevier Ltd. All rights reserved.

Influence of shot peening on the fatigue strength of Custom 465 stainless steel for aeronautic application

This project was originated from the national aircraft industry requirements to reduce the use of coated materials with electroplated chromium or cadmium that produce waste, which is harmful to health or the environment. The selected material is a Custom 465 stainless steel used in the aeronautical field due to its high mechanical strength. Considering the load sustained by the wheel axis of the landing gear, the Custom 465 is tested in axial fatigue. The objective is to compare the behavior of the Custom 465 with plated AISI 4340 steel coated with cadmium. X-ray diffraction method was used to determine the residual stress field induced by shot peening.