Femtosecond nonlinear optical properties of lead-germanium oxide amorphous films

The nonlinear (NL) response of lead-germanium oxide amorphous films was investigated using a Ti:saphire laser delivering pulses of approximate to 150 fs at 800 nm. The Kerr shutter technique was employed to reveal the time response of the nonlinearity that is smaller than 150 fs. The sign and magnitude of the nonlinearity were obtained using a novel technique called thermally managed eclipse Z scan which allows the simultaneous characterization of cumulative and noncumulative NL effects. The NL refractive index of electronic origin, n(2)approximate to 2x10(-17) m(2)/W, and the NL absorption coefficient, alpha(2)approximate to 3x10(3) cm/GW, were determined. (c) 2007 American Institute of Physics.

Spectroscopic properties and upconversion mechanisms in Er3+-doped fluoroindate glasses

Fluorindate glasses containing 1,2,3,4 ErF3 mol % were prepared in a dry box under argon atmosphere. Absorption, Stokes luminescence (under visible and infrared excitation), the dependence of 4S3/2, 4I11/2, and 4I13/2 lifetimes with Er concentration, and upconversion under Ti-saphire laser excitation at λ=790 nm were measured, mostly at T=77 and 300 K. The upconversion results in a strong green emission and weaker blue and red emissions whose intensity obeys a power-law behavior I∼Pn, where P is the infrared excitation power and n=1.6, 2.1, and 2.9 for the red, green, and blue emissions, respectively. The red emission exponent n=1.5 can be explained by a cross relaxation process. The green and blue emissions are due to excited state absorption (ESA) and energy transfer (ET) processes that predict a factor n=2 and n=3 for the green and blue emissions, respectively. From transient measurements we concluded that for lightly doped samples the green upconverted emission is originated due to both processes ESA and ET. However, for heavily doped samples ET is the dominant process.