Crystallization kinetics in phosphate sodium-based glass studied by DSC technique

In this work, differential scanning calorimetry (DSC) was used to study the mechanism of crystallization of 5OP(2)O(5-)27.8Na(2)O-16ZnO-6.2Al(2)O(3) glass. DSC measurements were performed on bulk and powdered glasses with different particle size. The curve for bulk glass shows one crystallization peak while powdered glasses presented two distinct crystallization peaks. Based on DSC studies, the activation energies obtained were 336 +/- 6 and 213 +/- 3 U mol(-1), associated with first and second crystallization peaks, respectively. Analyzing the DSC parameters as a function of particle size, the Avrami n parameter suggests that the peak at low temperature may be associated with surface crystallization while the peak at high temperature is associated with bulk crystallization. (C) 2002 Elsevier B.V. Ltd. All rights reserved.

Influence of 0.05% sodium fluoride solutions on microhardness of resin-modified glass ionomer cements

This study aimed to evaluate the influence of fluoride-containing mouthrinse solutions (Fluorgard and Oral B) on the superficial microhardness of two resin-modified glass ionomer cements (Vitremer and Fuji II LC). Fifteen discs-shaped specimens of each glass ionomer cement (0 10 mm; 2 mm thick) were prepared, thereby forming two groups. After 24-hour storage in artificial saliva, the microhardness was measure and the data were recorded. Next, each group was divided into three subgroups (n = 5), according to the solution to be immersed in. Control specimens were kept in artificial saliva along the whole experiment. The test specimens were kept in mouthrinse solution for 30 days. Vickers surface microhardness was analyzed at predetermined evaluation periods: 24 h, 48 h, 7, 14, 21 and 30 days after specimens' preparation. Data were subjected to three-way ANOVA and to Tukey test (p < 0.05). A better behavior of Fuji II LC was observed and Fluorgard affected most the characteristics of the tested materials. It may be concluded that fluoride-containing solutions influenced the tested characteristics of materials, mainly of Vitremer.

Glass foam of macroporosity using glass waste and sodium hydroxide as the foaming agent

Glass foams using float glass waste and sodium hydroxide were produced. The influence of the sodium hydroxide amount in the foam formulation was studied. Titanium dioxide was used as a strengthening agent. The variations of temperature, heating rate and sintering time were investigated during the synthesis process. Open porosity was estimated using mercury porosimetry. The morphology of the glass foams was evaluated using scanning electron microscopy, phase formation was studied using X-ray diffraction, and chemical composition was estimated using X-ray fluorescence. As a result, glass foams with macroporosity were obtained. Since the glass foams used glass waste as reactant, the results suggest the development of an alternative route for glass recycling. © 2012 Elsevier Ltd and Techna Group S.r.l.

Thermoluminescence of aluminophosphate glasses in the metaphosphate composition

Potassium aluminum phosphate (KAP) glasses in the system xKPO(3)-(100-x)AI(PO3)3 with x = 10, 30 and 50 mol% were prepared in the metaphosphate composition. The glasses were doped with MnO2 and their thermoluminescent (TL) response was investigated. Raman spectra showed that these glasses did not undergo structural changes with the substitution of manganese ions. The glass composition x = 50 mol% doped with 1.0 mol% of MnO2 presented the best TL response. The material displayed good sensitivity for gamma-rays, X-rays and UV light. The emission curves exhibited two TL peaks, one at a low temperature (similar to 150 degrees C) and the other at a high temperature (similar to 365 degrees C), whose positions were dependent on the type of exciting radiation applied. The results of the present study indicated that the high temperature peak is a good candidate for TL dosimetric investigations. (c) 2006 Elsevier B.V. All rights reserved.

Fracture strength of incisor crowns after intracoronal bleaching with sodium percarbonate

Objectives: To compare the fracture resistance of bovine teeth after intracoronal bleaching with sodium percarbonate (SPC) or sodium perborate (SP) mixed with water or 20% hydrogen peroxide (HP). Materials and methods: Fifty extracted bovine teeth were divided into four experimental groups (G1G4) and one control (n = 10) after endodontic treatment. Following root canal obturation, a glass ionomer barrier was placed at the cementoenamel junction. After that, the pulp chambers were filled with: G1 SP with water; G2 SP with 20% HP; G3 SPC with water; and G4 SPC with 20% HP. No bleaching agent was used in the control group. Coronal access cavities were sealed with glass ionomer and specimens were immersed in artificial saliva. The bleaching agents were replaced after 7 days, and teeth were kept in artificial saliva for an additional 7 days, after which the pastes were removed and the coronal access cavities were restored with glass ionomer. Crowns were subjected to compressive load at a cross head speed of 0.5 mm min-1 applied at 135 degrees to the long axis of the root by an EMIC DL2000 testing machine, until coronal fracture. Data were statistically analysed by anova and Tukey test. Results: No differences in fracture resistance were observed between the experimental groups (P > 0.05). However, all experimental groups presented lower fracture resistance than the control group (P < 0.05). Conclusion: SPC and SP led to equal reduction on fracture resistance of dental crowns, regardless of being mixed with water or 20% HP.

Different particle size silicas from water glass.

Non-crystalline silica was obtained with different particle sizes. Samples were prepared from soluble sodium silicate (water glass) and sulfuric acid solutions. Dialysis was performed for sodium sulfate elimination. Products were dried in a microwave oven, milled and characterized by X-ray powder diffraction, infrared spectrum and sedigraphic analysis. Products milled for more than 120 minutes showed uniform particle size distribution with average silica particle size of 4.5 mu m.

Effects of different treatments on purity of silica from soluble sodium silicate

Noncrystalline silica was obtained with low iron, sodium, and nitrate ions concentrations from soluble sodium silicate (water glass) and nitric acid solution. Extractions with nitric acid solution and/or deionized water and/or dialysis were carried out to eliminate soluble metal ions. Products were dried in a microwave oven and characterized by chemical analysis, XRD, and IR. Dialysis seems to be the best treatment for the elimination of sodium and nitrate ions. Silica purified by nitric acid and water extractions followed by dialysis yields the purest silica sample.

Preparation of zinc sodium polyphosphates glasses from coacervates precursors. Characterisation of the obtained glasses, and their applications

A soft chemistry route is described to obtain glasses in the P2O5-Na2O-ZnO-H2O. It is based on the addition of zinc salts to coacervates prepared from sodium polyphosphate. The processing of these coacervates leads to polyphosphate glasses with the same properties as those of glasses prepared in the classical way. So far, little work has been implemented in this system using 'coacervate route'. However, it makes an attractive method for coating and joining processes on the industrial scale. As the anion associated to zinc may take part in the adhesion mechanism, coacervate formation has been studied using zinc chloride, nitrate and sulphate as starting materials. The physical properties of the glasses obtained by this method are reported and potential applications of zinc and silver coacervate are described. (C) 2002 Academie des sciences / Editions scientifiques et medicales Elsevier SAS.

Effect of temperature on glass-ceramic films prepared by impregnation of commercial float glass surfaces with oxide powders under pressure

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Enhanced luminescence of Tb3+/Eu3+ doped tellurium oxide glass containing silver nanostructures

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Osteoconductivity of modified fluorcanasite glass-ceramics for bone tissue augmentation and repair

Modified fluorcanasite glasses were fabricated by either altering the molar ratios of Na 2O and CaO or by adding P 2O 5 to the parent stoichiometric glass compositions. Glasses were converted to glass-ceramics by a controlled two-stage heat treatment process. Rods (2 mm x 4 mm) were produced using the conventional lost-wax casting technique. Osteoconductive 45S5 bioglass was used as a reference material. Biocompatibility and osteoconductivity were investigated by implantation into healing defects (2 mm) in the midshaft of rabbit femora. Tissue response was investigated using conventional histology and scanning electron microscopy. Histological and histomorphometric evaluation of specimens after 12 weeks implantation showed significantly more bone contact with the surface of 45S5 bioglass implants when compared with other test materials. When the bone contact for each material was compared between experimental time points, the Glass-Ceramic 2 (CaO rich) group showed significant difference (p = 0.027) at 4 weeks, but no direct contact at 12 weeks. Histology and backscattered electron photomicrographs showed that modified fluorcanasite glass-ceramic implants had greater osteoconductivity than the parent stoichiometric composition. Of the new materials, fluorcanasite glass-ceramic implants modified by the addition of P 2O 5 showed the greatest stimulation of new mineralized bone tissue formation adjacent to the implants after 4 and 12 weeks implantation. © 2010 Wiley Periodicals, Inc.

Glass-ceramic material from the SiO 2-Al 2O 3-CaO system using sugar-cane bagasse ash (SCBA)

Brazil is the world's largest producer of alcohol and sugar from sugarcane. Currently, sugarcane bagasse is burned in boilers to produce steam and electrical energy, producing a huge volume of ash. The major component of the ash is SiO 2, and among the minor components there are some mineralizing agents or fluxing. Published works have shown the potential of transforming silicate-based residues into glass-ceramic products of great utility. This work reports the research results of SCBA use to produce glass-ceramics with wollastonite, rankinite and gehlenite as the major phases. These silicates have important applications as building industry materials, principally wollastonite, due to their special properties: high resistance to weathering, zero water absorption, and hardness among others. The glasses (frits) were prepared mixing ash, calcium carbonate and sodium or potassium carbonates as flux agents, in different concentrations. X-ray fluorescence was used to determine the chemical composition of the glasses and their crystallization was assessed by using thermal analysis (DTA/DSC/TGA) and X-ray diffraction. The crystallization kinetics was evaluated using the Kissinger method, giving activation energies ranging from 200 to 600 kJ/mol. © 2011 Ceramic Society of Japan.

Physicothermal properties of aqueous sodium chloride solutions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comparison of Different Dentin Pretreatment Protocols on the Bond Strength of Glass Fiber Post Using Self-etching Adhesive

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)