Study of the thermomechanical and electrical properties of conducting composites containing natural rubber and carbon black

This work describes the preparation and characterization of composite materials obtained by the combination of natural rubber (NR) and carbon black (CB) in different percentages, aiming to improve their mechanical properties, processability, and electrical conductivity, aiming future applications as transducer in pressure sensors. The composites NR/CB were characterized through optical microscopy (OM), DC conductivity, thermal analysis using differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMA), thermogravimetry (TGA), and stress-strain test. The electrical conductivity varied between 10(-9) and 10 S m(-1), depending on the percentage of CB in the composite. Furthermore, a linear (and reversible) dependence of the conductivity on the applied pressure between 0 and 1.6 MPa was observed for the sample with containing 80 wt % of NR and 20% of CB. (C) 2007 Wiley Periodicals, Inc.

Conductive composites of natural rubber and carbon black for pressure sensors

Composites of natural rubber and carbon black have attracted great interest due to their technological applications. In this work natural rubber (NR) and carbon black (CB) were compounded, aiming the development of composites with good mechanical properties, processability and electrical conductivity for use as pressure sensors. The electrical conductivity changes from 10(-11) to 10(-2) S.cm(-1) depending on the percentage of CB in the composite. It was also observed that the conductivity varies reversibly and linearly with the applied pressure. The latter demonstrates that this material can be used as pressure sensors.

Preparation of ceramic membranes from surface modified tin oxide nanoparticles

The preparation of crack-free SnO2 supported membranes requires the development of new strategies of synthesis capable to allow controlled changes of surface chemistry and to improve the processability of supported layers. In this way, the controlled modification of the SnO2 nanoparticle surface by adding capping molecules like Tiron(R) ((OH)(2)C6H2(SO3Na)(2)) during the sol-gel process was studied, aiming to obtain high performance membranes. Colloidal suspensions were prepared by hydrolyzing SnCl4.5H(2)O aqueous solution with NH4OH in presence of Tiron(R). The effect of the amount of Tiro(R) (from I to 20 wt.%) on the structural features of nanoparticles, powder redispersability and particle-solution interface properties was investigated by X-ray powder diffraction (XRPD), extended X-ray absorption fine structure (EXAFS), quasi-elastic light scattering and electrophoretic mobility measurements. XRPD and EXAFS results showed that the addition of Tiron(R) up to 20 wt.% to colloidal suspensions does not affect the crystallite size of SnO2 primary particles, determined around 2-3 nm. This value is comparable to the hydrodynamic size measured after redispersion of powder prepared with amount of Tiro(R) higher than 7.5 wt.%, indicating the absence of condensation reactions between primary particles after the initial precipitation step. As a consequence the powder with amount of Tiron(R) > 7.5 wt.%, can be fully redispersed in aqueous solution at pH greater than or equal to I I until a nanoparticle concentration of 6 vol.%. The electrophoresis measurements showed a decrease of the isoelectric point by increasing the amount of grafted Tiron(R) at the SnO2 nanoparticle surface, resulting in negatively charged particle-solution interface in all the studied pH range (2-11). These features govern the gelation process favoring the preparation of crack-free SnO2 supported membranes. The control exercised by Tiron(R) modifying agent in the aggregation process allows the fine-tuning of the porosity, from 0.124 to 0.065 cm(3) g(-1), and mean pore size, from 6.4 to 1.9 nm, as the amount of grafted molecules increases from 0 to 10 wt.%. In consequence, the membrane cut-off determined by filtration of polyethylene glycol standard solutions can be screened from 1500 to 3500 g mol(-1). (C) 2002 Elsevier B.V. B.V. All rights reserved.

Electrical behavior of PU/POMA blends

The incorporation of conducting polymer into a conventional polymer matrix has received attention because of the possibility of combining the good processability and mechanical performance of the conventional polymer with the electrical and optical properties of conducting polymer. In this work, flexible films of polyurethane (PU) and Poli(o-metoxyaniline)(POMA) blends were obtained by casting and investigated using thermally stimulated depolarisation current (TSDC) measurements. Two relaxation peaks were found in the range of-20°C to 90°C. The first one at T=24°C was attributed as α relaxation associated to the glass transition of PU/POMA blend and the second one located at T=60°C can be attributed to space charge.

Study of the thermo-mechanical and electrical properties of conducting composites containing natural rubber and carbon black

This work shows the preparation and characterization of composites obtained by mixing natural rubber (NR) and carbon black (CB) in different percentages aiming suitable mechanical properties, processability and electrical conductivity for future applications as transducers in pressure sensors. The composites NR/CB are characterized through dc conductivity, thermal analysis using differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMA), thermogravimetry (TGA) and stress-strain test. The electrical conductivity changed from 10-9 to 10 Sm-1 depending on the percentage of CB in the composite. Besides, it was found a linear (and reversible) dependence of the conductivity on the applied pressure in the range from 0 to 1.6 MPa for the sample 80/20 (NR/CB wt%).

Preparação e caracterização de blendas de poliuretano derivado do óleo de mamona e poli (o-metoxianilina) e sua avaliação como sensor

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação e caracterização do compósito poli (fluoreto de vinilideno) / polianilina com partículas de níquel

Pós-graduação em Ciência dos Materiais - FEIS

Efficiency comparison of hyperbranched polymers as toughening agents for a one-part epoxy resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)