Enzymeless Hydrogen Peroxide Sensor Based on Mn-containing Conducting Metallopolymer

The [(Mn4O5)-O-IV(terpy)(4)(H2O)(2)](6+) complex, show great potential for electrode modification by electropolymerization using cyclic voltammetry. The voltammetric behavior both in and after electropolymerization process were also discussed, where the best condition of electropolymerization was observed for low scan rate and 50 potential cycles. A study in glass electrode for better characterization of polymer was also performed. Electrocatalytic process by metal centers of the conducting polymer in H2O2 presence with an increase of anodic current at 0.85 V vs. SCE can be observed. The sensor showed great response from 9.9 x 10(-5) to 6.4 x 10(-4) mol L-1 concentration range with a detection limit of 8.8 x 10(-5) mol L-1, where the electrocatalytic mechanism was based on oxidation of H2O2 to H2O with consequently reduction of Mn-IV to Mn-III. After, the Mn-III ions are oxidized electrochemically to Mn-IV ions. (C) 2012 Elsevier Ltd .... Selection and/or peer-review under responsibility of the Symposium Cracoviense Sp. z.o.o.

Electropolymerization mechanism in aqueous solution of the oxo-manganese complex biomimicking of the enzymatic center present on the photosystem II

The [Mn4 IVO5(terpy)4(H 2O)2]6+ complex, show great potential for electrode modification by electropolymerization using cyclic voltammetry. The electropolymerization mechanism was based on the electronic transfer between dx2-y2 orbitals of the center metallic and pπ orbital of the ligand, which show great complexity of the system due to orbitals overlap present in octahedral complex of the metal-μ-oxo. The voltammetric behavior both in and after electropolymerization process were also discussed, where the best condition of electropolymerization was observed for low scan rate and 50 potential cycles. A study in ITO/glass electrode for better characterization of polymer was also performed. ©The Electrochemical Society.

The potential of novel primers and universal adhesives to bond to zirconia

Objectives: To investigate the adhesive potential of novel zirconia primers and universal adhesives to surface-treated zirconia substrates.Methods: Zirconia bars were manufactured (3.0 mm x 3.0 mm x 9.0 mm) and treated as follows: no treatment (C); air abrasion with 35 mu m alumina particles (S); air abrasion with 30 mu m silica particles using one of two systems (Rocatec or SilJet) and; glazing (G). Groups C and S were subsequentially treated with one of the following primers or adhesives: ZP (Z-Prime Plus), AZ (AZ Primer); MP (Monobond Plus); SU (ScotchBond Universal) and; EA (an Experimental Adhesive). Groups Rocatec and SilJet were silanized prior to cementation. Samples form group G were further etched and silanized. Bars were cemented (Multilink) onto bars of a silicate-based ceramic (3.0 mm x 3.0 mm x 9.0 mm) at 90 degrees angle, thermocycled (2.500 cycles, 5-55 degrees C, 30 s dwell time), and tested in tensile strength test. Failure analysis was performed on fractured specimens to measure the bonding area and crack origin.Results: Specimens from group C did not survive thermocycling, while CMP, CSU and CEA groups survived thermocycling but rendered low values of bond strength. All primers presented a better bond performance after air abrasion with Al2O3 particles. SilJet was similar to Rocatec, both presenting the best bond strength results, along with SMP, SSU and CEA. G promoted intermediate bond strength values. Failure mode was predominately adhesive on zirconia surface combined to cohesive of the luting agent.Conclusions: Universal adhesives (MP, SU, EA) may be a considerable alternative for bonding to zirconia, but air abrasion is still previously required. Air abrasion with silica particles followed by silane application also presented high bond strength values. (C) 2013 Elsevier Ltd. All rights reserved.

Microwave-assisted hydrothermal synthesis of magnetite nanoparticles with potential use as anode in lithium ion batteries

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Potential of bamboo organosolv pulp as a reinforcing element in fiber-cement materials

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)