Biocompatibility in vitro tests of mineral trioxide aggregate and regular and white Portland cements

Mineral trioxide aggregate (MTA) and Portland cement are being used in dentistry as root end-filling materials. However, biocompatibility data concerning genotoxicity and cytotoxicity are needed for complete risk assessment of these compounds. In the present study, genotoxic and cytotoxic effects of MTA and Portland cements were evaluated in vitro using the alkaline single cell gel (comet) assay and trypan blue exclusion test, respectively, on mouse lymphoma cells. The results demonstrated that the single cell gel (comet) assay failed to detect DNA damage after a treatment of cells by MTA and Portland cements for concentrations up to 1000 mu g/ml. Similarly, results showed that none of the compounds tested were cytotoxic. Taken together, these results seem to indicate that MTA and Portland cements are not genotoxins and do not induce cellular death.

Evaluation of genetic damage in human peripheral lymphocytes exposed to mineral trioxide aggregate and Portland cements

Mineral trioxide aggregate (MTA) and Portland cement are being used in dentistry as root-end-filling material for periapical surgery and for the sealing of communications between the root canal system and the surrounding tissues. However, genotoxicity tests for complete risk assessment of these compounds have not been conducted up to now. In the present study, the genotoxic effects of MTA and Portland cements were evaluated in peripheral lymphocytes from 10 volunteers by the alkaline single cell gel (comet) assay. The results pointed out that the single cell gel (comet) assay failed to detect the presence of DNA damage after a treatment of peripheral lymphocytes by MTA and Portland cements for concentrations up to 1000 mu g mL(-1). In summary, our results indicate that exposure to MTA or Portland cements may not be a factor that increases the level of DNA lesions in human peripheral lymphocytes as detected by single cell gel (comet) assay.

Cytotoxicity of Portland Cement with Different Radiopacifying Agents: A Cell Death Study

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Radiopacity of Portland Cement Associated With Different Radiopacifying Agents

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The Influence of Calcium Chloride on the Setting Time, Solubility, Disintegration, and pH of Mineral Trioxide Aggregate and White Portland Cement with a Radiopacifier

This study evaluated the influence of addition of 10% calcium chloride (CaCl(2)) on the setting time, solubility, disintegration, and pH of white MTA (WMTA) and white Portland cement (WPC). A test of the setting time was performed following the #57 ADA specifications and a test of the final setting time according to the ASTM. For the solubility tests disintegration and pH, Teflon rings were filled with the cements and weighed after setting. After 24 h in a desiccator, they were once again weighed. Thereafter, they were immersed in MiliQ water for 24 and 72 h and 7, 14, and 28 days, with maintenance in the desiccator and weighing between periods. The pH of water in which the rings were immersed was measured immediately after contact with them and in the other periods. The addition of CaCl(2) provided a significant reduction (50%) in the initial setting time of cements. The final setting time of WMTA was reduced in 35.5% and the final setting time of WPC in 68.5%. The WMTA with CaCl(2) absorbed water and gained weight with time, except for in the 24-h period. The addition of CaCl(2) to the WPC reduced its solubility. The addition of CaCl(2) increased the pH of WMTA in the immediate period and at 24 and 72 h and for WPC in the immediate period and at 24 h. The addition of CaCl(2) to WMTA and WPC reduced the setting times and solubility of both and increased the pH of cements in the initial periods. (J Endod 2009;35:550-554)

Ileum of the Cephalotes ants: A specialized structure to harbor symbionts microorganisms

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Genotoxicity and cytotoxicity of mineral trioxide aggregate and regular and white Portland cements on Chinese hamster ovary (CHO) cells in vitro

Objective. Recently, mineral trioxide aggregate (MTA) and Portland cement have been used in dentistry as root-end-filling materials. However, the reported results concerning the biocompatibility of these materials are inconsistent. The goal of this study was to examine the genotoxicity and cytotoxicity of MTA and Portland cements in vitro by the single-cell gel (comet) assay and trypan blue exclusion test.Study design. Chinese hamster ovary (CHO) cells were exposed to MTA and regular and white Portland cements at final concentration ranging from 1 to 1000 mu g/mL for 1 h at 37 degrees C.Results. All compounds tested did not show genotoxic effects in all concentrations evaluated. No significant differences (P > .05) in cytotoxicity were observed for all compounds tested.Conclusions. Taken together, our results suggest that MTA and Portland cements are not genotoxins and are not able to induce cellular death.

Microbial leakage of MTA, Portland cement, Sealapex and zinc oxide-eugenol as root-end filling materials

Objective: The aim of this study was to compare the microbial leakage of mineral trioxide aggregate (MTA), Portland cement (PC), Sealapex and zinc oxide-eugenol (ZOE) as root-end filling materials.Study design: An in vitro microbial leakage test (MLT) with a split chamber was used in this study. A mixture of facultative bacteria and one yeast (S. aureus + E. faecalis + P. aeruginosa + B. subtilis + C. albicans) was placed in the upper chamber and it could only reach the lower chamber containing Brain Heart Infusion broth by way of leakage through the root-end filling. Microbial leakage was observed daily for 60 days. Sixty maxillary anterior human teeth were randomly assigned to different groups - MTA and PC (gray and white), Sealapex + zinc oxide and ZOE, control groups and subgroups to evaluate the influence of EDTA for smear layer removal. These materials were further evaluated by an agar diffusion test (ADT) to verify their antimicrobial efficacy. Data were analyzed statistically by Kruskal-Wallis and Mann-Whitney test.Results: In the MLT, Sealapex + zinc oxide and ZOE did not show evidence of microbial leakage over the 60-day experimental period. The other materials showed leakage from the 15th day. The presence of smear layer influenced microbial leakage. Microbial inhibition zones were not observed in all samples tested by ADT.Conclusion: Sealapex + zinc oxide and ZOE did not show microbial leakage over the experimental period, whereas it was verified within 15 to 45 days in MTA and Portland cement.

Reaction of rat connective tissue to implanted dentin tube filled with mineral trioxide aggregate, Portland cement or calcium hydroxide.

The subject of this study was to observe the rat subcutaneous connective tissue reaction to implanted dentin tubes filled with mineral trioxide aggregate, Portland cement or calcium hydroxide. The animals were sacrificed after 7 or 30 days and the undecalcified specimens were prepared for histological analysis with polarized light and Von Kossa technique for mineralized tissues. The results were similar for the studied materials. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was an irregular tissue like a bridge that was Von Kossa-positive. The dentin walls of the tubes exhibited in the tubules a structure highly birefringent to polarized light, usually like a layer and at different depths. The mechanism of action of the studied materials has some similarity.

Healing process of dog dental pulp after pulpotomy and pulp covering with mineral trioxide aggregate or Portland cement.

Considering several reports about the similarity between the chemical compositions of the mineral trioxide aggregate (MTA) and Portland cement (PC), the subject of this investigation was to analyze the behavior of dog dental pulp after pulpotomy and direct pulp protection with these materials. After pulpotomy, the pulp stumps of 26 roots of dog teeth were protected with MTA or PC. Sixty days after treatment, the animal was sacrificed and the specimens removed and prepared for histomorphological analysis. There was a complete tubular hard tissue bridge in almost all specimens. In conclusion, MTA and PC show similar comparative results when used in direct pulp protection after pulpotomy.

In vitro antimicrobial activity of endodontic sealers, MTA-based cements and Portland cement.

The aim of this study was to evaluate the antimicrobial activity of different root-end filling materials - Sealer 26, Sealapex with zinc oxide, zinc oxide and eugenol, white and gray Portland cement, white and gray MTA-Angelus, and gray Pro Root MTA - against six different microorganism strains. The agar diffusion method was used. A base layer was made using Müller-Hinton agar (MH) and wells were formed by removing the agar. The materials were placed in the wells immediately after manipulation. The microorganisms used were: Micrococcus luteus (ATCC9341), Staphylococcus aureus (ATCC6538), Escherichia coli (ATCC10538), Pseudomonas aeruginosa (ATCC27853), Candida albicans (ATCC 10231), and Enterococcus faecalis (ATCC 10541). The plates were kept at room temperature for 2 h for prediffusion and then incubated at 37 degrees C for 24 h. Triphenyltetrazolium chloride 0.05% gel was added for optimization, and the zones of inhibition were measured. Data were subjected to the Kruskal-Wallis and Dunn tests at a 5% significance level. The results showed that all materials had antimicrobial activity against all the tested strains. Analysis of the efficacy of the materials against the microbial strains showed that Sealapex with zinc oxide, zinc oxide and eugenol and Sealer 26 created larger inhibition halos than the MTA-based and Portland cements (P < 0.05). On the basis of the methodology used, it may be concluded that all endodontic sealers, MTA-based and Portland cements evaluated in this study possess antimicrobial activity, particularly the endodontic sealers.

Effect of different radiopacifying agents on the physicochemical properties of white portland cement and white mineral trioxide aggregate

Introduction: The aim of this study was to evaluate the pH, calcium ion release, setting time, and solubility of white mineral trioxide aggregate (WMTA) and white Portland cement (WPC) combined with the following radiopacifying agents: bismuth oxide (BO), calcium tungstate (CT), and zirconium oxide (ZO). Methods: Fifty acrylic teeth with root-end filling material were immersed in ultrapure water for measurement of pH and calcium release (atomic absorption spectrophotometry) at 3, 24, 72, and 168 hours. For evaluation of setting time, each material was analyzed according to the American Society for Testing and Materials guidelines 266/08. The solubility test was performed according to American National Standards Institute/American Dental Association specification no. 57/2000. Solubility, setting time, and pH values were compared by using analysis of variance and Tukey test, and the values of calcium release were compared by the Kruskal-Wallis and Miller tests. The significance level was set at 5%. Results: The pH and calcium release were higher at 3 and 24 hours. WPC was the material with the higher values for both properties. WMTA had the greatest solubility among all materials (P <.05). All radiopacifiers increased the setting time of WPC, and WMTA had the shortest setting time among all materials (P < .05). Conclusions: All materials released calcium ions. Except for WPC/CT at 168 hours, all materials promoted an alkaline pH. On the basis of the obtained results, ZO and CT can be considered as potential radiopacifying agents to be used in combination with Portland cement. Copyright © 2012 American Association of Endodontists.

Influence of radiopacifying agents on the solubility, pH and antimicrobial activity of Portland cement

The aim of this study was to evaluate the interference of the radiopacifiers bismuth oxide (BO), bismuth carbonate (BC), bismuth subnitrate (BS), and zirconiun oxide (ZO) on the solubility, alkalinity and antimicrobial properties of white Portland cement (WPC). The substances were incorporated to PC, at a ratio of 1:4 (v/v) and subjected to a solubility test. To evaluate the pH, the cements were inserted into retrograde cavities prepared in simulated acrylic teeth and immediately immersed in deionized water. The pH of the solution was measured at 3, 24, 72 and 168 h. The antimicrobial activity was evaluated by a radial diffusion method against the microorganisms S. aureus (ATCC 25923), P. aeruginosa (ATCC 27853), E. faecalis (ATCC 29212) and C. albicans (ATCC 10231). The zone of microbial growth inhibition was measured after 24 h. The addition of BS and BC increased the solubility of the cement. The pH values demonstrated that all materials produced alkaline levels. At 3 h, BS showed lower pH than WPC (p<0.05). At 168 h, all materials showed similar pHs (p>0.05). The materials did not present antimicrobial activity for S. aureus, P. aeruginosas and E. faecalis (p>0.05). With regards to C. albicans, all materials formed an inhibition zone, mainly the mixture of WPC with ZO (p<0.05). The type of radiopacifier incorporated into WPC interfered with its physical and antimicrobial properties. ZO was found to be a viable radiopacifier that can be used with WPC.

Physicochemical and mechanical properties of zirconium oxide and niobium oxide modified Portland cement-based experimental endodontic sealers

Aim: To evaluate the physicochemical and mechanical properties of Portland cement-based experimental sealers (ES) with different radiopacifying agents (zirconium oxide and niobium oxide micro- and nanoparticles) in comparison with the following conventional sealers: AH Plus, MTA Fillapex and Sealapex. Methodology: The materials were tested for setting time, compressive strength, flow, film thickness, radiopacity, solubility, dimensional stability and formaldehyde release. Data were subjected to anova and Tukey tests (P < 0.05). Results: MTA Fillapex had the shortest setting time and lowest compressive strength values (P < 0.05) compared with the other materials. The ES had flow values similar to the conventional materials, but higher film thickness (P < 0.05) and lower radiopacity (P < 0.05). Similarly to AH Plus, the ES were associated with dimensional expansion (P > 0.05) and lower solubility when compared with MTA Fillapex and Sealapex (P < 0.05). None of the endodontic sealers evaluated released formaldehyde after mixing. Conclusion: With the exception of radiopacity, the Portland cement-based experimental endodontic sealers presented physicochemical properties according to the specifications no 57 ANSI/ADA (ADA Professional Product Review, 2008) and ISO 6876 (Dentistry - Root Canal Sealing Materials, 2012, British Standards Institution, London, UK). The sealers had setting times and flow ability that was adequate for clinical use, satisfactory compressive strength and low solubility. Additional studies should be carried out with the purpose of decreasing the film thickness and to determine the ideal ratio of radiopacifying agents in Portland cement-based root canal sealers. © 2013 International Endodontic Journal.

Citotoxicidade e ação antimicrobiana do cimento Portland associado a diferentes agentes radiopacificadores

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)