Pressure-induced electrical and structural anomalies in Pb1-xCaxTiO3 thin films grown at various oxygen pressures by chemical solution route

Lead calcium titanate (Pb1-xCaxTiO3 or PCT) thin films have been thermally treated under different oxygen pressures, 10, 40 and 80 bar, by using the so-called chemical solution deposition method. The structural, morphological, dielectric and ferroelectric properties were characterized by x-ray diffraction, FT-infrared and Raman spectroscopy, atomic force microscopy and polarization-electric-field hysteresis loop measurements. By annealing at a controlled pressure of around 10 and 40 bar, well-crystallized PCT thin films were successfully prepared. For the sample submitted to 80 bar, the x-ray diffraction, Fourier transformed-infrared and Raman data indicated deviation from the tetragonal symmetry. The most interesting feature in the Raman spectra is the occurrence of intense vibrational modes at frequencies of around 747 and 820 cm(-1), whose presence depends strongly on the amount of the pyrochlore phase. In addition, the Raman spectrum indicates the presence of symmetry-breaking disorder, which would be expected for an amorphous (disorder) and mixed pyrochlore-perovskite phase. During the high-pressure annealing process, the crystallinity and the grain size of the annealed film decreased. This process effectively suppressed both the dielectric and ferroelectric behaviour. Ferroelectric hysteresis loop measurements performed on these PCT films exhibited a clear decrease in the remanent polarization with increasing oxygen pressure.

Preparation and properties of ferroelectric Pb1-xCaxTiO3 thin films produced by the polymeric precursor method

Pb1- xCaxTiO3 thin films with x = 0.24 composition were prepared by the polymeric precursor method on Pt/Ti/SiO2/Si substrates. The surface morphology and crystal structure, and the ferroelectric and dielectric properties of the films were investigated. X-ray diffraction patterns of the films revealed their polycrystalline nature. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) analyses showed the surface of these thin films to be smooth, dense and crack-free with low surface roughness. The multilayer Pb1-xCaxTO3 thin films were granular in structure with a grain size of approximately 60-70 nm. The dielectric constant and dissipation factor were, respectively, 174 and 0.04 at a 1 kHz frequency. The 600-nm thick film showed a current density leakage in the order of 10(-7) A/cm(2) in an electric field of about 51 kV/cm. The C-V characteristics of perovskite thin films showed normal ferroelectric behavior. The remanent polarization and coercive field for the deposited films were 15 muC/cm(2) and 150 kV/cm, respectively. (C) 2001 Kluwer Academic Publishers.

Pb1-xCaxTiO3 solid solution (x=0.0, 0.25, 0.50, and 0.75): A theoretical and experimental approach

In this paper we report an experimental and theoretical study based on a periodic density functional investigation into selected compositions of Pb1-xCaxTiO3 (x=0.0, 0.25, 0.50, and 0.75). Based on our findings, we propose that the pseudocubic structure of these perovskites presents a long-range tendency for cubic symmetry, while the short-range displacements bring the solid solution to a tetragonal symmetry. The results are discussed in terms of x-ray diffraction, structural optimized parameters, Raman spectroscopy, band structure, density of states, Mulliken charge, and overlap population.

Reply to Comment on 'Pb1-xCaxTiO3 solid solution (x=0.0, 0.25, 0.50, and 0.75): A theoretical and experimental approach'

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Titanium K-edge XAS study on local structure of Pb1-xCaxTiO3 ferroelectric ceramics

In order to characterize the local structure of Pb1-xCaxTiO3 (PCT) samples, Ti K-edge XANES measurements were performed and showed that Ca incorporation to PbTiO3 structure leads to a decreasing of local distortion of Ti atoms in relation to oxygen atoms at the TiO6 octahedra. Moreover, according to EXAFS measurements, the local structure around Ti atoms exhibits tetragonal symmetry with P4mm space group for samples with x <= 0.475, whereas orthorhombic symmetry with Pbnm space group was observed for x equals to 0.50 and 0.55.

A Raman and dielectric study of a diffuse phase transition in (Pb1-xCax)TiO3 thin films

Dielectric and Raman scattering experiments were performed on polycrystalline Pb1-xCaxTiO3 thin films (x=0.10, 0.20, 0.30, and 0.40) as a function of temperature. The results showed no shift in the dielectric constant (K) maxima, a broadening with frequency, and a linear dependence of the transition temperature on increasing Ca2+ content. on the other hand, a diffuse-type phase transition was observed upon transforming from the cubic paraelectric to the tetragonal ferroelectric phase in all thin films. The temperature dependence of Raman scattering spectra was investigated through the ferroelectric phase transition. The temperature dependence of the phonon frequencies was used to characterize the phase transitions. Raman modes persisted above the tetragonal to cubic phase transition temperature, although all optical modes should be Raman inactive. The origin of these modes was interpreted in terms of a breakdown of the local cubic symmetry due to chemical disorder. The lack of a well-defined transition temperature and the presence of broad bands in some temperature interval above the FE-PE phase transition temperature suggested a diffuse-type phase transition. This result corroborates the dielectric constant versus temperature data, which showed a broad ferroelectric phase transition in these thin films.

Microstructural, dielectric and ferroelectric properties of calcium-modified lead titanate thin films derived by chemical processes

Ferroelectric Pb1-xCaxTiO3 (x = 0.24) thin films were formed on a Pt/Ti/SiO2/Si substrate by the polymeric precursor method using the dip-coating technique for their deposition. Characterization of the films bq X-ray diffraction showed a perovskite single phase with a tetragonal structure after annealing at 700 degreesC. Atomic force microscopy (AFM) analyses showed that the film had a smooth and crack-free surface with low surface roughness. In addition, the PCT thin film had a granular structure with an 80 nm grain size. The thickness of the films observed by the scanning electron microscopy (SEM) is 550 nm and there is a good adhesion between the film and substrate. For the electrical measurements metal-ferroelectric-metal of the type capacitors were obtained, where the thin films showed good dielectric and ferroelectric properties. The dielectric constant and dissipation factor at 1 kHz and measured at room temperature were found to be 457 and 0.03. respectively. The remanent polarization and coercive field for the: deposited films were P-r = 17 muC/cm(2) and E-c = 75 kV/cm, respectively. Moreover. The 550-nm-thick film showed a current density in the order of 10(-8) A/cm(2) at the applied voltage of 2 V. The high values of the thin film's dielectric properties are attributed to its excellent microstructural quality and the chemical homogeneity obtained by the polymeric precursor method. (C) 2001 Elsevier science Ltd. All rights reserved.

Influence of Ca concentration on the electric, morphological, and structural properties of (Pb,Ca)TiO3 thin films

Pb1-xCaxTiO3 (0.10less than or equal toxless than or equal to0.40) thin films on Pt/Ti/SiO2/Si(100) substrates were prepared by the soft solution process and their characteristics were investigated as a function of the calcium content (x). The structural modifications in the films were studied using x-ray diffraction and micro-Raman scattering techniques. Lattice parameters calculated from x-ray data indicate a decrease in lattice tetragonality with the increasing content of calcium in these films. Raman spectra exhibited characteristic features of pure PbTiO3 thin films. Variations in the phonon mode wave numbers, especially those of lower wave numbers, of Pb1-xCaxTiO3 thin films as a function of the composition corroborate the decrease in tetragonality caused by the calcium doping. As the Ca content (x) increases from 0.10 to 0.40, the dielectric constant at room temperature abnormally increased at 1 kHz from 148 to 430. Also calcium substitution decreased the remanent polarization and coercive field from 28.0 to 5.3 muC/cm(2) and 124 to 58 kV/cm, respectively. These properties can be explained in terms of variations of phase transition (ferroelectric-paraelectric), resulting from the substitution the lead site of PbTiO(3)for the nonvolatile calcium. (C) 2002 American Institute of Physics.

Síntese de perovskitas nanométricas com estrutura 'PB IND.1-x''M IND.X''TI''O IND.3'(M='BA', 'CA' e 'SR')

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effects of strontium and calcium simultaneous substitution on electrical and structural properties of Pb1-x-y Ca (x) Sr (y) TiO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and morphological characteristics of (Pb1-x Sr (x) )TiO3 powders obtained by polymeric precursor method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural transition on Pb1-xSrxTiO3 produced by chemical method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Quantitative variation in the tropical maize population, ESALQ-PB1

A boa produtividade e os valores intermediários para altura da planta e altura da espiga caracterizam a população de milho ESALQ-PB1 como agronomicamente promissora. São relatadas estimativas de parâmetros para 13 caracteres: altura da planta (PH), altura da espiga (EH), posição relativa da espiga (EP), comprimento do pendão (TL), peso do pendão (TW), número de ramificações do pendão (TB), peso de espigas (EW), peso de grãos (GW), comprimento da espiga (EL), diâmetro da espiga (ED), número de fileiras de grãos (RN), número de grãos por fileira (KR) e prolificidade (PR). Os resultados se referem a um único ambiente (um local e um ano). Foi detectada variação genética para todos os caracteres, e são apresentadas estimativas da variância genética aditiva. Os coeficientes de herdabilidade (indivíduos) variaram de 0,14 a 0,72 e foram considerados altos para PH, EH e TB; intermediários para EP, TL, TW, EL e ED, e baixos para EW, GW, KR e PR. O coeficiente de herdabilidade para médias de progênies mostrou aproximadamente a mesma tendência, variando de 0,40 a 0,75. O maior ganho esperado por seleção foi para TB (27% por ciclo) sob seleção massal e para TW (16,4%) por seleção entre progênies; o menor ganho esperado foi para ED, tanto por seleção massal (1,9%) como por seleção entre progênies (2,9%). Coeficientes de correlação aditiva (rA) 0.5

Study on the orientation degree of Pb1-xLaxTiO3 thin films by the rocking curve technique and its morphological aspects

Thin films of perovskite-type materials such as PbTiO3, BaTiO3, (Pb,La)TiO3, (Pb, La)(ZrTi)O-3, KNbO3, and Pb(Mg,Nb)03 have been attracting great interest for applications like non-volatile memories, ultrasonic sensors and optical devices. Thin film should be epitaxially grown or at least highly textured since the properties of this anisotropic material depend on the crystallographic orientation. For optical devices, in particular, an epitaxial thin film without defects are essential to reduce optical propagation losses. Pb1-xLaxTiO3 (PLT) where x=0, 13 and 27% thin films were prepared by a chemical method (polymeric precursors method), and deposited by the spin coating technique onto substrates of SrTiO3 (STO) and LaAlO3 (LAO). The films were then beat treated at 500 degrees C in a controlled atmosphere of 0,. The orientation degree of the thin films was obtained from rocking curve technique, by means of X-ray difftaction analysis. A microstructural study revealed that the films were crack-free, homogeneous and have low roughness. (c) 2006 Elsevier B.V. All rights reserved.

Electronic structure of Pb1-xLaxTiO3 ferroelectric materials from Ti 2p and O 1s soft x-ray absorption spectroscopy

The electronic structure of Pb1-xLaxTiO3 (PLT) compounds for x ranging from 0 to 30 at. % of La is investigated by means of soft x-ray absorption near edge structure (XANES) at the Ti L-3,L-2 and O K edges. The greatest modification in the structure of the Ti 2p XANES spectra of the PLT compounds is observed in the region of the high energy peak of the L-3 edge (e(g) states), which exhibits a splitting in the undoped sample. As the amount of lanthanum increases, this splitting becomes less pronounced. This modification is interpreted as a decrease in the degree of disorder of titanium atoms, which is correlated to the substitution of Pb by La atoms. The structural changes observed at the low energy peaks of the O K-edge XANES spectra of the PLT compounds may be interpreted in terms of hybridization between O 2p, Ti 3d, and Pb 6p orbitals. A decrease in the degree of hybridization observed as Pb atoms are replaced by La atoms may be related to the differences in the ferroelectric properties observed between x=0.0 and x=0.30 compounds. (c) 2006 American Institute of Physics.