Characterization and application of PZT/PU and graphite doped PZT/PU composite

Composites, made of lead zirconate titanate (PZT) ceramic powder and castor oil-based polyurethane (PU), were prepared in the film form. The films were obtained in the thickness range 100-300 mum using up to 50/50 vol.% of ceramic. Another composite (PZT/C/PU) was obtained by adding a small amount (1.0 vol.%) of graphite (C) to the PZT/PU composite. By increasing the conductivity of PU-containing graphite, polarization of PZT could be carried out with better efficiency. A comparison of piezo- and pyroelectric activities and spatial distribution of polarization between graphite doped and undoped composites reveal the advantages of using semiconductor filler. These composites were used as sensors to detect acoustic emission (AE). The detection was made using two simulated sources of AE, i.e., ball bearing drop and pencil lead break. PZT/C/PU composite was able to detect both flexural and extensional components of wave vibration. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Lead zirconate titanate/polyurethane (PZT/PU) composite for acoustic emission sensors

Piezoelectric composite, made from ferroelectric ceramic lead zirconate titanate (PZT) and vegetable based polyurethane (PU) polymer, was doped with a semiconductor filler, graphite. The resulting composite (PZT/C/PU) with 49/1/50- vol. % composition could be poled at lower field and shorter time due to the increased conductivity of the polymer phase following the introduction of graphite. The PZT/C/PU composite showed higher pyroelectric coefficient in comparison with the undoped PZT/PU composite with 50/50-vol. % composition. Also, the PZT/C/PU composite has shown the ability to detect both extensional and flexural modes of simulated acoustic emission (AE) at a distance up to 8.0 m from the source, thus indicating that it may be used for detection of structural damages.