The influence of thermal treatment on the preparation of PNM and PMN-PT thin films

Ferroelectric thin films belong to a class of materials with great technological importance in optic fibers, micro-electromechanical systems, and microprocessors and computers memories.The (1-x)PbMg1/3Nb2/3O3(x)PbTiO3 (PMN-PT) thin films, with x=0, 0.1, 0.35 and 0.5, were prepared by Pechini's process and deposited by spin-coating on Si(100), Pt/Ti/SiO2/Si(100) and quartz substrates. The goal of the present paper is to verify the thermal treatment influence on the perovskite phase formation, which is desirable for these applications. The phase formation was analyzed by X-ray diffraction. The film's surface was characterized by atomic force microscopy to analyze the roughness and the homogeneity. The results of this study indicate that the optimum conditions for obtaining the perovskite phase using a Pt/Ti/SiO2/Si(100) substrate, were drying each deposited layer at 140 degreesC (heating plate), and a final thermal treatment at 600 degreesC for 3 h in a closed system with a lead-rich atmosphere. (C) 2003 Elsevier B.V. All rights reserved.

Effect of precursor solution on the formation of perovskite phase of Pb(Mg-1/Nb-3(2/3))O-3 thin films

Precursor solutions for Pb(Mg1/3Nb2/3)O-3 (PMN) synthesis were obtained by Pechini's method. The influence of the concentration of organic materials on the phase formation has been studied. For this purpose, PMN solutions were prepared with different precursors and were characterized by thermogravimetric and differential thermal analysis. The obtained solutions were deposited onto a Si (100) substrate by dip coating and pre-treated in a hot plate at 300 degreesC for 1 h. The films were annealed at 600, 700, 800 and 900 degreesC for 1 h and characterized by X-ray diffraction. The perovskite phase was formed after annealing at 600 and 700 degreesC when the solution of PMN was prepared with a lower amount of organic material and starting with mobium oxide. By increasing the temperature to 800 or 900 degreesC, only the formation of pyrochlore phase was observed. With the solution prepared from mobium ethoxide, only the presence of pyrochlore phase was observed independently of the annealing temperature. (C) 2002 Elsevier B.V. B.V. All rights reserved.