Langmuir and Langmuir-Blodgett (LB) films of poly [(2-methoxy,5-n-octadecyl)-p-phenylenevinylene] (OC1OC18-PPV)

A PPV derivative, poly(2-methoxy,5-(n-octadecyl)-p-phenylenevinylene) (OC1OC18-PPV), has been synthesized via the Gilch route and used to fabricate Langmuir and Langmuir-Blodgett (LB) films. True monomolecular films were formed at the air/water interface, which were successfully transferred onto different types of substrate. Using UV-visible absorption, FTIR, fluorescence and Raman scattering spectroscopies we observed that the polymer molecules were randomly distributed in the LB film, with no detectable anisotropy. This is in contrast to the anisotropic LB films of a previously reported PPV derivative, poly(2-methoxy-5-n-hexyloxy)-p-phenylenevinylene (OC1OC6-PPV), which is surprising because the longer chain of OC1OC18-PPV investigated here was expected to lead to more ordered films. As a consequence of the lack of order, LB films of OC1OC18-PPV exhibit lower photoconductivity and require higher operating voltage in a polymer light-emitting diode (PLED) in comparison with LB films of OC1OC6-PPV. This result confirms the importance of molecular organization in the LB film to obtain efficient PLEDs. (c) 2005 Elsevier Ltd. All rights reserved.

Langmuir and langmuir-blodgett films of polyfluorenes and their use in polymer light-emitting diodes

The Langmuir and Langmuir-Blodgett (LB) film properties of two polyfluorene derivatives, namely poly(2,7-9,9'-dihexylfluorene-dyil) (PDHF) and poly(9,9 dihexylfluorene-dyil-vynilene-alt-1,4-phenylene-vyninele) (PDHF-PV), are reported. Surface pressure (Pi-A) and surface potential (Delta V-A) isotherms indicated that PDHF-PV forms true monolayers at the air/water interface, but PDHF does not. LB films could be transferred onto various types of substrate for both PDHF and PDHF-PV. Only the LB films from PDHF-PV could withstand deposition of a layer of evaporated metal to form a light-emitting diode (PLED), which had typical rectifying characteristics and emitted blue light. It is inferred that the ability of the polymer to form true monomolecular layers at the air/water interface seems to be associated with the viability of the LB films in PLEDs.

Polymer light emitting devices with Langmuir Blodgett (LB) films of a polyfluorene derivative

Polyfluorenes are promising materials for the emitting layer of polymer light emitting devices (PLEDs) with blue emission. In this work, we report on PLEDs fabricated with Langmuir-Blodgett (LB) films of a polyfluorene derivative, namely poly(9,9-di-hexylfluorenediyl vinylene-alt-1,4-phenylenevinylene) (PDHF-PV). Y-type LB films were transferred onto ITO substrates at a surface pressure of 35 mN m-1 and with dipping speed of 3 mm min -1. A thin aluminum layer was evaporated on top of the LB film, thus yielding a sandwich structure (ITO/PDHF-PV(LB)/Al). Current-voltage (I vs V) measurements indicate that the device displays a classical behavior of a rectifying diode. The threshold value is approximately 5 V, and the onset for visible light emission occurs at ca. 10 V. From the a.c. electrical responses we infer that the active layer has a typical behavior of PLEDs where the real component of ac conductivity obeys a power-law with the frequency. Cole-Cole plots (Im(Z) vs. Re(Z)) for the device exhibit a series of semicircles, the diameter of which decreases with increasing forward bias. This PLED structure is modeled by a parallel resistance and capacitance combination, representing the dominant mechanisms of charge transport and polarization in the organic layer, in series with a resistance representing the ITO contact. Overall, the results presented here demonstrate the feasibility of LEDs made with LB films of PDHF-PV.

Desenvolvimento e caracterização de dispositivos luminescentes híbridos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Hopping-tunneling model to describe electric charge injection at metal/organic semiconductor heterojunctions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)