In vitro study of staining agents effects on optical properties of esthetic restorative materials

The authors have studied the effect of four staining agents on the optical properties of esthetic restorative materials through translucency tests. Two commercial brands of composite resins were used: Point 4 (Kerr) and Charisma (Heraeus-Kulzer). The liquids tested were: wine, cola, chlorhexidine solution and nicotine solution. The translucency was measured at different periods of time: P0 – before immersion (baseline), P1 - 1 h after immersion, P2 - 2 h after immersion and successively, P3 – 24 h after immersion up to a period of 7 weeks. ANOVA statistical analysis was applied to the data (p < 0.05). The results lead to the following conclusions: (1) Composite resins submitted to the tested immersion mediums were stained, (2) the lower percentage of translucency was observed for nicotine containing solution, (3) The percentage of translucency decreased with the period of immersion.

The brightening of Saturn's F ring

Image photometry reveals that the F ring is approximately twice as bright during the Cassini tour as it was during the Voyager flybys of 1980 and 1981. It is also three times as wide and has a higher integrated optical depth. We have performed photometric measurements of more than 4800 images of Saturn's F ring taken over a 5-year period with Cassini's Narrow Angle Camera. We show that the ring is not optically thin in many observing geometries and apply a photometric model based on single-scattering in the presence of shadowing and obscuration, deriving a mean effective optical depth tau approximate to 0.033. Stellar occultation data from Voyager PPS and Cassini VIMS validate both the optical depth and the width measurements. In contrast to this decades-scale change, the baseline properties of the F ring have not changed significantly from 2004 to 2009. However, we have investigated one major, bright feature that appeared in the ring in late 2006. This transient feature increased the ring's overall mean brightness by 84% and decayed with a half-life of 91 days. (c) 2012 Elsevier B.V. All rights reserved.

In vitro penetration of bleaching agents into the pulp chamber

Aim: To investigate pulp chamber penetration of bleaching agents in teeth following restorative procedures. Methodology: Bovine lateral incisors were sectioned 3 mm apical to the cemento-enamel junction and the coronal pulpal tissue was removed. Teeth were divided into six groups (n = 10): G1, G2 and G3 were not submitted to any restorative procedure, while G4, G5 and G6 were submitted to Class V preparations and restored with composite resin. Acetate buffer was placed in the pulp chamber and treatment agents were applied for 60 min at 37°C as follows: G1 and G4, immersion into distilled water; G2 and G5, 10% carbamide peroxide (CP) exposure; G3 and G6, 35% CP bleaching. The buffer solution was removed and transferred to a glass tube where leuco crystal violet and horseradish peroxidase were added, producing a blue solution. The optical density of the blue solution was determined spectrophotometrically at 596 nm. A standard curve made with known amounts of hydrogen peroxide was used to convert the optical density values of the coloured samples into microgram equivalents of hydrogen peroxide. Data were submitted to ANOVA and Tukey's test (5%). Results: Amounts of hydrogen peroxide found in the pulp chamber of G2 and G5 specimens (0.1833 ± 0.2003 μg) were significantly lower (P = 0.001) when compared to G3 and G6 specimens (0.4604 ± 0.3981 μg). Restored teeth held significantly higher (P = 0.001) hydrogen peroxide concentrations in the pulp chamber than intact teeth. Conclusion: Higher concentrations of the bleaching agent produced higher levels of hydrogen peroxide in the pulp chamber, especially in restored teeth.

The effect of endodontic materials on the optical density of dyes used in marginal leakage studies

The aim of this study was to determine the effect of the exposure of different endodontic materials to different dye solutions by evaluating the optical density of the dye solutions. Seventy-five plastic tubes were filled with one of the following materials: AH Plus, Sealapex, Portland cement, MTA (Angelus and Pro Root) and fifteen control plastic tubes were not. Each specimen of material and control was immersed in a container with 1 ml of each dye solution. A 0.1 ml-dye solution aliquote was removed before immersion and after 12, 24, 48 and 72 hours of each specimen immersion to record its optical density (OD) in a spectrophotometer. Statistical analysis was performed with ANOVA and Tukey tests (5%). No significant difference was found among any of the solution OD values for AH Plus cement. Portland cement promoted different OD values after 12 hours of immersion. MTA-Angelus cement presented different OD values only for 2% rhodamine B and the MTA-Pro Root cement presented different OD values in all 2% rhodamine B samples. Sealapex cement promoted a reduction in the India Ink OD values. Dye evaluation through OD seems to be an interesting method to select the best dye solution to use in a given marginal leakage study.