Solution heat treatment of plasma nitrided 15-5PH stainless steel - Part I: Improvement of the corrosion resistance

The results of the investigation on Solution Heat Treatment of Plasma Nitrided (SHTPN) precipitation-hardened steel 15-5PH are presented. The layers have been obtained by the plasma nitriding process followed by solution heat treatment at different temperatures. The influence of the solution heat treatment after nitriding on the dissolution process of the nitrided layer has been considered. The nitrided layers were studied by scanning electron microscopy, X-ray microanalysis (EDX), and X-Ray diffraction. Micro-hardness tests of the nitrided layers and solubilized nitrided layers have been carried out and interpreted by considering the processing conditions. It was found that high nitrogen austenitic cases could be obtained after SHTPN of martensitic precipitation-hardened steel (15-5PH). When Solution Heat Treatment (SHT) was performed at 1100 °C, some precipitates were observed. The amount of precipitates significantly reduced when the temperature increased. The EDX microanalysis indicated that the precipitate may be chromium niobium nitride. When the precipitation on the austenite phase occurred in small amount, the corrosion resistance increased in SHTPN specimens and the pit nucleation potential also increased. The best corrosion result occurred for SHT at 1200 °C.

Fatigue Strength of X45CrSi93 stainless steel applied as internal combustion engine valves

Stainless steels are used to intake and exhaust valves production applied as internal combustion engines. In general valves are requested to support cyclic stresses applied due to opening and closing processes during the operation. The objective of this research is to study the influence on the axial fatigue strength of the resulting microstructure after heat treatment at the martensitic X45CrSi93 steel, combined with different surface treatments as hard chrome-plating, nitride and grinding. It was verified a significant increase on the fatigue strength of the martensitic steel after nitriding, compared with results from the chrome-plating specimens. A slight increase in the tensile strength was also noticed on nitrided parts as a consequence of a resistance increase due to nitrogen and carbon solid solution. (C) 2011 Published by Elsevier Ltd. Selection and peer-review under responsibility of ICM11

Avaliação da resistência ao desgaste de aços inoxidáveis endurecíveis por precipitação nitretados

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Plasma nitriding of sintered AISI 316L at several temperatures

Samples of sintered AISI 316L stainless steel were plasma nitrided in a mixture of H-2-20% N-2, for 3 or 4 h. The treatment temperature was selected in 400-550 degreesC interval, in steps of 50 degreesC. X-ray diffraction (glancing angle geometry-GAXRD), conversion electron Mossbauer spectroscopy (CEMS), optical microscopy and Vickers microhardness were used as analytical techniques. For T greater than or equal to 500 degreesC and t = 4 h, a 40-mum layer is formed. The GAXRD results showed a transformation of the austenite gamma phase to the martensite in the sinterization process and showed as well, that the gamma' (Fe4N) phase is the predominant nitride besides small amounts of epsilon-Fe2N, gamma(N) CrN, Cr2O3 and the fcc nitrogen supersatured solid phase gamma(N). The CrN phase seems to decrease with temperature while the gamma(N) phase fraction is almost less than or equal to10%, independently on the temperature. The CEMS results indicated that while the gamma(N) fraction decreases with temperature of plasma nitriding, the gamma' fraction increases proportionally. (C) 2003 Elsevier B.V. All rights reserved.

Microstructural characterization of layers produced by plasma nitriding on austenitic and superaustenitic stainless steel grades

High chromium content is responsible for the formation of a protective passive surface layer on austenitic stainless steels (ASS). Due to their larger amounts of chromium, superaustenitic stainless steels (SASS) can be chosen for applications with higher corrosion resistance requirements. However, both of them present low hardness and wear resistance that has limited their use for mechanical parts fabrication. Plasma nitriding is a very effective surface treatment for producing harder and wear resistant surface layers on these steel grades, without harming their corrosion resistance if low processing temperatures are employed. In this work UNS S31600 and UNS S31254 SASS samples were plasma nitrided in temperatures from 400 °C to 500 °C for 5 h with 80% H 2-20% N2 atmosphere at 600Pa. Nitrided layers were analyzed by optical (OM) and transmission electron microscopy (TEM), x-ray diffraction (XRD), and Vickers microhardness testing. Observations made by optical microscopy showed that N-rich layers were uniform but their thicknesses increased with higher nitriding temperatures. XRD analyses showed that lower temperature layers are mainly composed by expanded austenite, a metastable nitrogen supersaturated phase with excellent corrosion and tribological properties. Samples nitrided at 400 °C produced a 5 μm thick expanded austenite layer. The nitrided layer reached 25 lm in specimens treated at 500 °C. There are indications that other phases are formed during higher temperature nitriding but XRD analysis was not able to determine that phases are iron and/or chromium nitrides, which are responsible for increasing hardness from 850 up to 1100 HV. In fact, observations made by TEM have indicated that formation of fine nitrides, virtually not identified by XRD technique, can begin at lower temperatures and their growth is affected by both thermodynamical and kinetics reasons. Copyright © 2012 by ASTM International.

Plasma nitriding and nitrocarburising of a supermartensitic stainless steel

Supermartensitic stainless steels (SMSSs) are a new generation of the classic 13%Cr martensitic steels, lower in carbon and with additional alloying of nickel and molybdenum offering better weldabilty and low temperature toughness. Several works have shown that plasma nitriding and nitrocarburising of stainless steels at low temperatures produces a hard surface layer which results in increased wear resistance. In this work, SMSS samples were plasma nitrided and nitrocarburised at 400, 450 and 500 °C. The plasma treated SMSS samples were characterised by means of optical microscopy, microhardness, X-ray diffraction and dry wear tests. The thickness of the layers produced increases as temperature is raised, for both plasma nitriding and nitrocarburising. X-ray diffraction demonstrates that the chromium nitride content grows with temperature for nitriding and nitrocarburising, which also showed increasing content of iron and chromium carbides with temperature. After plasma treating, it was found that the wear volume decreases for all temperatures and the wear resistance increased as the treatment temperature was raised. The main wear mechanism observed for both treated and untreated samples was grooving abrasion. © 2012 IHTSE Partnership Published by Maney on behalf of the Partnership.

A influência da microestrutura e dos tratamentos superficiais na vida em fadiga de aços inoxidáveis martensítico e austenítico usados na fabricação de válvulas para motores a combustão interna

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização mecânica e microestrutural de um aço 4340 com estrutura multifásicas e tratamento de nitrocarbonetação a plasma

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Morphological study of nitrides of NbTi (50:50, by weight) alloy

Plates of NbTi (50:50, by weight) were nitrided in a nitrogen atmosphere in the temperature range 800-1000 °C for 15, 30, 60, 120 and 180 min. X-Ray diffraction and optical and electronic microscopy were used to characterize the samples. Two nitride layers were identified on the substrate: an external and continuous phase of TiN, named δ, and a deeper and discontinuous phase of Ti 2N, named ε{lunate}. The electron micrographs reveal the presence of paths rich in Nb which may be responsible for the diffusion of nitrogen into the matrix. © 1993.

Caracterização mecânica e microestrutural de juntas soldadas a laser em aços maraging com posterior tratamento térmico e termoquímico de superfície a plasma