Corrosion behaviour of thermal sprayed nitinol coatings

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Preparation of Ni-Ti-Mo and Ni-Ti-Mo-Zr Alloys by High-Energy Ball Milling and Subsequent Hot Pressing

This work discusses on the preparation of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr (at-%) alloys by high-energy ball milling and hot pressing, which are potentially attractive for dental and medical applications. The milling process was performed in stainless steel balls (19mm diameter) and vials (225 mL) using a rotary speed of 300rpm and a ball-to-powder weight ratio of 10:1. Hot pressing under vacuum was performed in a BN-coated graphite crucible at 900 degrees C for 1 h using a load of 20 MPa. The milled and hot-pressed materials were characterized by X-ray diffraction, electron scanning microscopy, and electron dispersive spectrometry. Peaks of B2-NiTi and Ni4Ti3 were identified in XRD patterns of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr powders milled for 1h. The NiTi compound dissolved small Mo amounts lower than 4 at%, which were measured by EDS analysis. Moreover, it was identified the existence of an unknown Mo-rich phase in microstructures of the hot-pressed Ni-Ti-Mo alloys.

Wear resistance of nickel-titanium endodontic files after surface treatment

Objectives The purpose of this work was to submit the Nitinol files to plasma immersion ion implantation (PIII) and evaluate the effects of the surface treatment. Materials and Methods Wear resistance was determined in vitro by using an equipment for the application of horizontal movements on previously prepared notched plates made of resin. Vickers microhardness was measured in plates and files, before and after surface treatment and the surface chemical composition of the instruments was determined by X-rays photoelectron spectroscopy. Results The hardness values found for the treated Nitinol files were significantly lower than the hardness values measured before the implantation process. The comparison of commercially available instruments shows that the wear resistance of the stainless steel file is higher than the resistance of the Nitinol. Conclusions The results found led to the conclusion that the surface treatment significantly increased the Nitinol files wear resistance.

Comparação dos efeitos de compressão isostática e compressão uniaxial na obtenção da liga NiTi por metalurgia do pó

Several alloys present the shape memory effect and among them, the equiatomic NiTi alloy, nitinol, is the most important one. It is usually used in several engineering applications and also in biomedical devices, in the fabrication of orthodontic wire, stents and Judet staples. Although a considerable amount of these biomedical devices is utilized in Brazil and a fraction of it is already made here, all nitinol used is bought abroad. Thus, it is important to develop the necessary know-how to fabricate NiTi wire and sheet. It would mean less importation with job creation and wealth generation for the country. In this work nitinol was obtained powder metallurgy from elemental powders of Ti and Ni using uniaxial compression and uniaxial compression followed by isostatic compression. The final densities achieved were determined by the Archimedes method. The precipitation of intermetallic secondary phases was studied and the samples were characterized by metallographic analysis, optical microscopy and X-ray diffraction. Results indicated that 50 hours sintering route showed a low amount of intermetallics, and no trace of unreacted powder. XRD and metallography at room temperature indicated B19’ as the predominant phase, which corresponds to martensite. Although density results showed little dispersion, the most dense sample was compacted under uniaxial compression and presented 4.8 g/cm3, corresponding to 20.84% porosity. Density variation was considered normal to the measurement process and independent of the compaction mode

Estudo de tempos e temperaturas de sinterização na obtenção da liga NiTi por metalurgia do pó

The nickel-titanium alloys are very attractive and so it is widely used in industry, engineering applications in general and also in biomedical and dental applications. Besides showing the shape of memory effect, biocompatibility and superelastic, the alloy commercially known as Nitinol, has excellent mechanical properties. Most devices used in Brazil have been produced nationally, but using imported material is also necessary, which shows the need of produce the alloy nationally. In this study we have investigated the influence of sintering temperatures and times to obtain nickel-titanium alloys by powder metallurgy alloys and the characterization of the precipitated intermetallic phases by using the post-mix of elemental nickel and titanium in proportion of 49.5% Ti - 50.5% Ni. The samples were sintered at 930ºC for periods of 30, 40 and 50 hours and were characterized by optical microscopy using metallography and x-ray diffraction. The results of the study show that the 50 hours sintering time was the most suitable time for obtaining the alloy, observing a low volume of precipitated intermetallic phases and absence of Ni and Ti residuals

Stress distribution in delayed replanted teeth splinted with different orthodontic wires: a three-dimensional finite element analysis