Surface study of vitreous carbon obtained from glassy carbon powder

This work presents a surface study of monolithic vitreous (or glassy) carbon - MVC - obtained from vitreous carbon powder. Defective MVC pieces are crushed in a ball mill and size classified by sifting. The MVC powder is mixed with furfuryl-alcohol resin and compacted in a mould using a hydraulic press. Samples with different powder granulometries are produced in this way and carbonized in a furnace under nitrogen atmosphere. Complete carbonization of the powder is achieved in only one day and losses due to breakage of the pieces is less than 5%. These results compare very favorably with respect to traditional MVC production methods where full carbonization may require up to seven days and losses due to breakage can be as high as 70%. After carbonization, samples are sanded and polished. Surface roughness and microstructure are characterized by light microscopy. Porosity is quantified from micrographs using ImageJ software and nanometric height variations are measured by atomic force microscopy. © 2012 Materials Research Society.

Comparison of the nanoparticles performance in the photocatalytic degradation of a styrene-butadiene rubber nanocomposite

Much has been talking about the advantages of polymeric nanocomposites, but little is known about the influence of nanoparticles on the stability of these materials. In this sense, we studied the influence of both oxides of zirconium and titanium, known to have photocatalytic properties, as well as the influence of synthetic clay Laponite on the photodegradation of styrene-butadiene rubber (SBR). SBR nanocomposites were prepared by the colloidal route by mixing commercial polymer lattices and nanometric anatase TiO2, monoclinic ZrO2 or exfoliated Laponite clays colloidal suspensions. To better understand the degradation mechanisms that occur in these nanocomposites, the efficiency of different photocatalysts under ultraviolet radiation was monitored by FT-IR and UV-vis spectroscopies and by differential scanning calorimetric. It was observed that TiO2 and ZrO2 nanoparticles undoubtedly acted as catalysts during the photodegradation process with different efficiencies and rates. However, when compared to pure SBR samples, the polymer degradation mechanism was unaffected. Unlike studies with nanocomposites montmorillonite, exfoliated laponite clay effectively acts as a photostabilizer of polymer UV photodegradation. Copyright © 2012 Wiley Periodicals, Inc.

Sintering of porous alumina obtained by biotemplate fibers for low thermal conductivity applications

In this research report, a sintering process of porous ceramic materials based on Al2O3 was employed using a method where a cation precursor solution is embedded in an organic fibrous cotton matrix. For porous green bodies, the precursor solution and cotton were annealed at temperatures in the range of 100-1600°C using scanning electron microscopy (SEM) and thermogravimetric (TG) analysis to obtain a porous body formation and disposal process containing organic fibers and precursor solution. In a structure consisting of open pores and interconnected nanometric grains, despite the low porosity of around 40% (calculated geometrically), nitrogen physisorption determined a specific surface area of 14m2/g, which shows much sintering of porous bodies. Energy dispersive X-ray (EDX) and X-ray diffraction (XRD) analytical methods revealed a predominant amount of α-Al2O3 in the sintered samples. Thermal properties of the sintered Al2O3 fibers were obtained by using the Laser Flash which resulted in the lower thermal conductivity obtained by α-Al2O3 and therefore improved its potential use as an insulating material. © 2012 Elsevier Ltd.

Aplicação do Método de Rietveld em caracterização estrutural e nanoestrutural do espinélio 'Ni IND. 1'- 'delta' Co'delta''Fe IND.2''O IND.4' preparado por reação de combustão

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo do efeito de CdO e Bi2O3 no processo de nucleação e crescimento de cristais em matrizes vítreas [TeO2WO3] (CdO;Bi2O3)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)