The role of Bi2O3 on the thermal, structural, and optical properties of tungsten-phosphate glasses

Glasses in the ternary system (70 - x)NaPO3-30WO 3-xBi2O3, with x = 0-30 mol %, were prepared by the conventional melt-quenching technique. X-ray diffraction (XRD) measurements were performed to confirm the noncrystalline nature of the samples. The influence of the Bi2O3 on the thermal, structural, and optical properties was investigated. Differential scanning calorimetry analysis showed that the glass transition temperature, Tg, increases from 405 to 440 C for 0 ≤ x ≤ 15 mol % and decreases to 417 C for x = 30 mol %. The thermal stability against devitrification decreases from 156 to 67 C with the increase of the Bi2O3 content. The structural modifications were studied by Raman scattering, showing a bismuth insertion into the phosphate chains by Bi-O-P linkage. Furthermore, up to 15 mol % of Bi 2O3 formation of BiO6 clusters is observed, associated with Bi-O-Bi linkage, resulting in a progressive break of the linear phosphate chains that leads to orthophosphate Q0 units. The linear refractive index, n0, was measured using the prism-coupler technique at 532, 633, and 1550 nm, whereas the nonlinear (NL) refractive index, n 2 was measured at 1064 nm using the Z-scan technique. Values of 1.58 ≤ n0 ≤ 1.88, n2 ≥ 10-15 cm 2/W and NL absorption coefficient, α2 ≤ 0.01 cm/GW, were determined. The linear and NL refractive indices increase with the increase of the Bi2O3 concentration. The large values of n0 and n2, as well as the very small α2, indicate that these materials have large potential for all-optical switching applications in the near-infrared. © 2012 American Chemical Society.

Infrared to visible up-conversion emission in Er3+/Yb 3+ codoped fluoro-phosphate glass-ceramics

Erbium Er3+ and ytterbium Yb3+ codoped fluoro-phosphate glasses belonging to the system NaPO3-YF 3-BaF2-CaF2 have been prepared by the classical melt-quenching technique. Glasses containing up to 10 wt% of erbium and ytterbium fluorides have been obtained and characterized using differential scanning calorimetry (DSC) and UV-visible and near-infrared spectroscopy. Transparent and homogeneous glass-ceramics have been then reproducibly synthetized by appropriate heat treatment above glass transition temperature of a selected parent glass. Structural investigations of the crystallization performed through X-ray diffractometry (XRD) and scanning electron microscopy (SEM) have evidenced the formation of fluorite-type cubic crystals based during the devitrification process. Finally, infrared to visible up-conversion emission upon excitation at 975 nm has been studied on the Er3+ and Yb 3+ codoped glass-ceramics as a function of thermal treatment time. A large enhancement of intensity of the up-conversion emissions-about 150 times- has been observed in the glass-ceramics if compared to the parent glass one, suggesting an incorporation of the rare-earth ions (REI) into the crystalline phase. © 2012 The American Ceramic Society.

Photoinduced structural changes in antimony polyphosphate based glasses

A photocontraction effect in amorphous films of the binary glass system 0.20 [Sb(PO3)(3)](n)-0.80 Sb2O3 has been observed after UV irradiation using the 350.7 nm Kr+ ion laser line with 5.0 W/cm(2). Good optical quality films up to 4.0 mum were deposited on silica substrates at room temperature in vacuum by electron beam physical vapor deposition (EB-PVD) and characterized using WDX, XRD, optical absorption, infrared reflectance, profilometry and atomic force microscopy (AFM) techniques. Very stable glasses were prepared by the melt quenching technique and used as evaporation source for the production of films. The photoinduced structural change (PSC) was observed as a variation of about 6% in the film thickness and this effect is accompanied by a photobleaching of the irradiated area with a blue shift of the optical absorption edge. Otherwise this photoinduced change in the film thickness is very sensitive to the variations in the shape and intensity of the laser beam; therefore several possibilities in optical recording arise from these results. (C) 2003 Published by Elsevier B.V.

Síntese e caracterização do sistema vítreo (1-x) NaPO 3 – (x)WO 3

Pós-graduação em Ciência dos Materiais - FEIS

Structural studies of AgPO3-MoO3 glasses using solid state NMR and vibrational spectroscopies

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

1.5 mu m and visible up-conversion emissions in Er3+/Yb3+ co-doped tellurite glasses and optical fibers for photonic applications

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Test of the adiabatic nucleation model in SeTe and GeSnSe glasses

Se1-yTey and Ge1-ySnySe2.5 glasses, with compositions Y less than or equal to 0.5 and Y less than or equal to 0.6 respectively, are investigated. These glasses show a glass transition temperature (T-g) above the stability limit, indicated by the Adiabatic Nucleation Model (ANM). This effect has to be so because, other-wise, when cooled, these undercooled liquids would crystallize by generalized nucleation near the stability limit and no T-g could be observed. This shows that Se1-yTey glasses for Y < 0.5 are structurally stable. Limiting cases are pure Te and Se50Te50, which have T'(g)'s on the stability limit. Pure amorphous Te has to be obtained by fast quenching techniques, where the effective (fast quenching) T-g(*) is higher and Se50Te50 tends to crystallize easily. (C) 2004 Elsevier B.V. All rights reserved.

Luminescence quantum efficiency at 1.5 μm of Er3+-doped tellurite glass determined by thermal lens spectroscopy

Erbium doped tellurite glasses (TeO2 + Li2O + TiO2) were prepared by conventional melt-quenching method to study the influence of the Er3+ concentration on the luminescence quantum efficiency (η) at 1.5 μm. Absorption and luminescence data were used to characterize the samples, and the η parameter was measured using the well-known thermal lens spectroscopy. For low Er3+ concentration, the measured values are around 76%, and the concentration behavior of η shows Er-Er and Er-OH- interactions, which agreed with the measured lifetime values. © 2013 Elsevier B.V. All rights reserved.

Cinética de cristalização em vidros teluritos do sistema TLWN

Pós-graduação em Ciência dos Materiais - FEIS

Estudo da cinética de cristalização de vidros teluretos 20Li2O-80TeO2

Pós-graduação em Ciência dos Materiais - FEIS

Geração de segundo harmônico em vidros teluritos TeO2 – LiNbO3

Pós-graduação em Ciência dos Materiais - FEIS

Thermal and structural study of glasses in the binary system TeO2-Pb(PO3)(2)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

On observation of the downconversion mechanism in Er3+/Yb3+ co-doped tellurite glass using thermal and optical parameters

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Laser stimulated piezoelectricity in Er3+ doped GeO2-Bi2O3 glasses containing silicon nanocrystals