Avaliação das características de superfície e formação de biofilmes em materiais odontológicos tratados em plasmas de HMDSO

Pós-graduação em Reabilitação Oral - FOAR

Avaliação da biocompatibilidade de materiais para remoção química da lesão da cárie: análise histológica em tecido conjuntivo de camundongos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação do selamento de ápices radiculares retrobturados ou recobertos com diferentes materiais mediante infiltração marginal por corante e análise da interface em microscopia eletrônica de varredura

The purpose of this study was to evaluate the apical sealing ability and the marginal adaptation of five dental materials used in retrofillings or applied to the bevelled root surface. One hundred and forty extracted single rooted human teeth were used, divided into seven groups of twenty each. ln the first, second, third and fourth groups, the teeth were apicoectomized, submitted to cavity preparations and retrofilled with one of the following materiais: zinc free silver amalgam, a dentin bonding system plus composite resin, a glass ionomer cement ora compomer. In the fifth, sixth and seventh groups, the teeth were apicoectomized and capped on the bevelled root surface with one of the following materiais: a dentin bonding system plus composite resin, a glass ionomer cement or a compomer. Two specimens of each experimental group were evaluated for the marginal adaptation using scanning electron microscopy. The remaining 126 specimens were immersed in 2% methylene blue dye, stored for one week at 37ºC and the infiltration was evaluated with a stereomicroscope. The results showed that the glass ionomer cement presented the lowest values of marginal infiltration when used as retrofilling material, with a significant statistical difference when compared with the others tested materials. When used as apical capping, the glass ionomer cement and the compomer were equivalent and significantly better than the dentin bonding system plus composite resin. Using scanning electron microscopy, all the materials showed some slight adjustment problem. ln the retrofilling, the smallest marginal gaps were observed with the compomer and the dentin bonding system plus composite resin, while the largest were observed with the glass ionomer cement and zinc free silver amalgam. ln the apical capping, the smallest marginal gaps were observed with the compomer and the dentin bonding system plus composite resin and ...

Avaliação das propriedades térmicas, químicas e mecânica relacionando dente bovino e dente humano

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação in vitro da translucidez de dois sistemas cerâmicos metal-free: In-Ceram x Empress 2

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação qualitativa e quantitativa da resposta tecidual frente aos cimentos: MTA Ângelus cinza e MTA fotopolimerizável experimental: análise microscópica de implantes realizados em subcutâneos de ratos

Pós-graduação em Ciência Odontólogica - FOA

Atividade antibacteriana de sistemas adesivos dentinários autocondicionantes sobre bactérias cariogênicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resposta tecidual a cimentos cirúrgicos: estudo histológico realizado em alvéolo dental de ratos

Pós-graduação em Odontologia - FOA

Estudo da dureza e do grau de conversão de resinas compostas: efeito de fonte de luz e material

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Propriedades físicas e mecânicas de um cimento de ionômero de vidro após a incorporação de nanopartículas de dióxido de titânio

Pós-graduação em Ciências Odontológicas - FOAR

Air abrasion before and/or after zirconia sintering: surface characterization, flexural strength, and resin cement bond strength

The purpose of this in vitro study was to evaluate the effect of air-abrasion/zirconia sintering order on the yttria partially stabilized tetragonal zirconia polycrystal (Y-TZP) surface characterization (roughness, morphology, and phase transformation), flexural strength (FS), and shear bond strength (SBS) to a resin cement. Y-TZP specimens were air abraded with 50-μm Al2O3 particles after (AS), before (BS), or before and after zirconia sintering (BAS). For roughness (Ra), 30 block specimens (12×12×3.0 mm; n=10) had their surfaces analyzed by a profilometer. Next, on the air-abraded surfaces of these specimens, composite resin discs (n=30) were bonded with RelyX ARC. The bonded specimens were stored for 24 hours in distilled water at 37°C before shear testing. Failure mode was determined with a stereomicroscope (20×). The surface morphology (n=2) was evaluated by SEM (500×). For the four-point flexural strength test (EMIC DL2000), 39 bar-shaped specimens (20×4.0×1.2 mm; n=13) were air abraded according to the three conditions proposed, and an additional group (nonabraded) was evaluated (n=13). The quantitative analysis of phase transformation (n=1) was completed with Rietveld refinement with X-ray diffraction data. Ra (μm) and SBS (MPa) data were analyzed by one-way analysis of variance (ANOVA) and the Tukey test (α=0.05). Pearson correlation analysis was used to determine if there was a correlation between roughness and SBS. For FS (MPa) data, one-way ANOVA and the Dunnett C-test (α=0.05) were used. The air-abrasion/zirconia sintering order influenced significantly (p<0.001) Ra, SBS, and FS. The BS and AS groups presented the highest (1.3 μm) and the lowest (0.7 μm) Ra. The highest SBS (7.0 MPa) was exhibited by the BAS group, followed by the AS group (5.4 MPa) and finally by the BS group (2.6 MPa). All groups presented 100% adhesive failure. A weak correlation (r=−0.45, p<0.05) was found between roughness and SBS. The air-abrasion/zirconia sintering order provided differences in the surface morphology. The nonabraded (926.8 MPa) and BS (816.3 MPa) groups exhibited statistically similar FS values but lower values than the AS (1249.1 MPa) and BAS (1181.4 MPa) groups, with no significant difference between them. The nonabraded, AS, BS, and BAS groups exhibited, respectively, percentages of monoclinic phase of 0.0 wt%, 12.2 wt%, 0.0 wt%, and 8.6 wt%. The rougher surface provided by the air-abrasion before zirconia sintering may have impaired the bonding with the resin cement. The morphological patterns were consistent with the surface roughness. Considering the short-term SBS and FS, the BAS group exhibited the best performance. Air abrasion, regardless of its performance order, provides tetragonal to monoclinic transformation, while sintering tends to zero the monoclinic phase content.

Effect of surface treatments on the shear bond strength of luting cements to Y-TZP ceramic

Statement of problem Because zirconia is a glass-free material, alternative surface treatments such as airborne-particle abrasion or silica coating should be used for long-term bonding. However, these surface treatments in combination with different bonding agents and luting cements have not yet been studied. Purpose The purpose of the study was to evaluate the effect of surface treatments on the shear bond strength (SBS) of luting cements to Y-TZP ceramic. Material and methods Zirconia disks (N=240) were airborne-particle abraded with the following particles (n=48): 50 μm Al2O3; 120 μm Al2O3; 30 μm silica-coated Al2O3 (Rocatec Soft); 120 μm Al2O3+110 μm silica-coated Al2O3 (Rocatec Plus); and Rocatec Plus. After silanization of the zirconia surface, composite resin disks were bonded with (n=12) RelyX Luting 2; RelyX ARC; RelyX U100; and Panavia F. The bonded specimens were thermocycled (10 000 cycles) and tested for SBS. Failure mode was determined with a stereomicroscope (×20). The morphology and elemental composition of airborne-particle abraded surfaces were evaluated with scanning electron microscopy (×500) and energy-dispersive x-ray spectroscopy (×50). Results Surface treatments, cements, and their interaction were significant (P<.001). For RelyX ARC, Rocatec Soft and Rocatec Plus provided the highest SBS. In general, surface treatments did not influence the SBS of RelyX U100 and Panavia F. Regardless of the cement, no significant difference was found between 50 μm and 120 μm Al2O3 particles, between Rocatec Soft and Rocatec Plus, or between Rocatec Plus and 120 μm Al2O3 particles+Rocatec Plus. All groups showed adhesive failures. Different particle sizes provided differences in morphological patterns. The elemental composition comprised Al and Al/Si for alumina and silica-abraded zirconia. Conclusions Particle size did not influence the SBS of the groups abraded exclusively with alumina or silica-coated particles. RelyX ARC was more surface-treatment dependent than RelyX U100 or Panavia F.

Interação entre odontologia restauradora e periodontia - parte 2: reanatomização dentária

The development of new dental materials has expanded dental therapeutic modalities ensuring excellence in aesthetic restorative treatments. Thus, the direct restorative procedures have been used in cases of dental reconstruction allowing an effective treatment with a low cost, while preserving healthy tooth structure. However, the clinician must be used to the techniques and the material in order to ensure longevity and success in the direct restorative procedure. The aim of this paper is to descrive, after completion of periodontal surgical procedures, the direct restorative step performed for dental reconstruction and diastema closure. The integration between Restorative Dentistry and periodontics enableb the restoration of a harmonious smile in a conservative manner, ensuring aesthetics and patient stisfaction.

Lichenoid reaction: case report

Lichenoid lesions are mucocutaneous disease of chronic inflammatory origin. Can produce side effects to drugs, dental materials, affecting 0.5 to 1% of the world population mainly in women in the fourth decade of life. The history and meticulous clinical servation may clarify the reactive nature, but the clinical diagnosis will only be conclusive when associated with tests such as histopathology. Therefore the objective of the study is to report a case of a woman of 55 years old, complaining of "white spots sore". Reported being allergic to metals, chocolate, acidic foods and certain types of clothes. From accurate intraoral clinical examination, white plaques were found in the dorsum of the tongue, hard palate and buccal mucosa, inaccurate and rough limits, and ulcerations throughout the labial edge and upper palate. Histopathology revealed a lichenoid reaction. Was instituted as pharmacological treatment, the use of systemic corticosteroids. Clinical follow-up of one year showed reduction of clinical symptoms, allowing to conclude that the clinical follow-up of this disease is necessary since its dubious malignant potential and diagnostic difficulty. Thus, early recognition of this disease allows instituting appropriate treatment with relief of anxiety of the patient and their family.