Detection of catechol using mixed Langmuir-Blodgett films of a phospholipid and phthalocyanines as voltammetric sensors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Release and diffusion of hydroxyl ion from calcium hydroxide-based medicaments

The release and diffusion of hydroxyl ions (OH-) of calcium hydroxide (Ca(OH)2)-based intracanal medications may be affected by the association with other substances. The aim of this study was to evaluate the diffusion of OH- ions through root dentin by the medications: G1, Ca(OH)2/saline; G2, Calen; G3, Calen/camphorated p-monochlorophenol (CMCP); and G4, Calen/0.4% chlorhexidine (CHX). Root canals from bovine teeth were prepared in a standardized manner. A cavity until dentin was prepared in the middle third of the root surface of each specimen. The external surface of the root was made impermeable using a layer of adhesive, except the prepared cavity. The root canals were filled with different medications, and teeth were individually stored in flasks containing 10 ml distilled water at 37 degrees C. The water pH was measured at 1, 3, 7, 14, 21, 30, and 60 days. Data obtained were subjected to anova and Tukeys tests. Increase in pH was observed at 3 days for Calen/CHX and from 7 to 14 days for the other mixtures. Calen paste promoted pH increase up to 21 days. Calen/CMCP had the highest pH up to 21 days, and all groups had similar results at 30 days. At 60 days, the greatest pH values were observed for Calen/CMCP and Calen alone. All different formulations of Ca(OH)2-based medications tested release hydroxyl ion that can diffuse through the dentin.

Diffusion coefficient of K+ in ion exchanged glasses calculated from the refractive index and the Vickers hardness profiles

The top faces of float glass samples were exposed to vapors resulting from the decomposition of KNO3 at 565 degrees C for up to 32 h. X-ray dispersive spectra (EDS) show that K+ ions migrate into the glass. The K+ concentration profile was obtained and its diffusion coefficient was calculated by the Boltzmann-Matano technique. The mean diffusion coefficient was approximately 10 X 10(-11) cm(2) s(-1). It was observed that the refractive index and the Vickers hardness decrease with the depth (after the removal of successive layers), and their profiles were thus obtained. These profiles enabled the calculation of the diffusion coefficient of K+ through the Boltzmann-Matano technique, with mean results ranging between 6 x 10(-11) and 30 x 10(-11) cm(2) s(-1). (c) 2006 Elsevier B.V. All rights reserved.

In situ application of a cellulose bag and an ion exchanger for differentiation of labile and inert metal species in aquatic systems

This work involved the development and application of a new analytical procedure for in-situ characterization of the lability of metal species in aquatic systems by using a system equipped with a diffusion membrane and cellulose organomodified with p-aminobenzoic acid groups (DM-Cell-PAB). To this end, the DM-Cell-PAB system was prepared by adding cellulose organomodified with p-aminobenzoic acid groups (Cell-PAB) to pre-purified cellulose bags. After the DM-Cell-PAB system was sealed, it was examined in the laboratory. The in-situ application involved immersing the DM-Cell-PAB system in two different rivers, enabling us to study the relative lability of metal species (Cu, Cd, Fe, Mn, and Ni) as a function of time and quantity of exchanger. The procedure is simple and opens up a new perspective for understanding environmental phenomena relating to the complexation, transport, stability, and lability of metal species in aquatic systems rich in organic matter.

Plasma immersion ion implantation of nitrogen into H13 steel under moderate temperatures

Ion implantation of nitrogen into samples of tempered and quenched H13 steel was carried out by plasma immersion technique. A glow discharge plasma of nitrogen species was the ion source and the negative high voltage pulser provided 10-12 kV, 60 mu s duration and 1.0-2.0 kHz frequency, flat voltage pulses. The temperatures of the samples remained between 300 and 450 degrees C, sustained solely by the ion bombardment. In some of the discharges, we used a N-2 + H-2 gas mixture with 1:1 ratio. PIII treatments as long as 3, 6, 9 and up to 12 h were carried out to achieve as thickest treated layer as possible, and we were able to reach over 20 mu m treated layers, as a result of ion implantation and thermal (and possibly radiation enhanced) diffusion. The nitrogen depth profiles were obtained by GDOS (Glow Discharge Optical Spectroscopy) and the exact composition profiles by AES (Auger Electron Spectroscopy). The hardness of the treated surface was increased by more than 250%, reaching 18.8 GPa. No white layer was seen in this case. A hardness profile was obtained which corroborated a deep hardened layer, confirming the high efficacy of the moderate temperature PIII treatment of steels. (c) 2005 Elsevier B.V. All rights reserved.

Vehicle influence on calcium hydroxide pastes diffusion in human and bovine teeth

The purpose of this study was to compare the pH and calcium ion liberation after use of calcium hydroxide pastes with different paste vehicles in human or bovine teeth. Ninety-two single-rooted human and bovine roots were used. The roots were instrumented and an external cavity preparation was performed. The roots were divided in to human and bovine groups. Each group was subdivided into four subgroups (SB) according to the vehicle:SB1, detergent; SB2, saline; SB3, polyethylenoglycol + camphorated paramonochlorophenol (Calen PMCC) and SB4, polyethylenoglycol + furacyn paramonochlorophenol (FPMC). Specimens were immersed into saline solution at 37 degrees C and after 7 and 14 days pH and calcium ion measurements were made. The results were analyzed by ANOVA and Tukey tests (P < 0.05). There was no statistical difference between bovine and human teeth in the pH analysis (P < 0.05), but bovine teeth provided larger calcium ion liberation than human teeth. Calen PMCC was statistically more effective for pH increase and calcium ion liberation in all analyses, followed by FPMC and saline. Detergent showed the lowest pH alterations and calcium ion liberation. The period of 14 days showed more calcium ionic liberation than the 7-day period.

Er3+-doped germanate glasses for active waveguides prepared by Ag+/K+ <-> Na+ ion-exchange

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of the diffusion capacity of calcium hydroxide pastes through the dentinal tubules

This study aimed to evaluate the diffusion capacity of calcium hydroxide pastes with different vehicles through dentinal tubules. The study was conducted on 60 extracted single-rooted human teeth whose crowns had been removed. The root canals were instrumented and divided into 4 groups according to the vehicle of the calcium hydroxide paste: Group I - distilled water; Group II - propylene glycol; Group III - 0.2% chlorhexidine; Group IV - 2% chlorhexidine. After placement of the root canal dressings, the teeth were sealed and placed in flasks containing deionized water. After 1, 2, 7, 15, 30, 45 and 60 days, the pH of the water was measured to determine the diffusion of calcium hydroxide through the dentinal tubules. The data were recorded and statistically compared by the Tukey test. The results showed that all pastes presented a similar diffusion capacity through dentin. Group IV did not present difference compared to group I. Group II presented difference compared to the other groups, as did Group III. In conclusion, groups I and IV presented a better diffusion capacity through dentin than groups II and III; 2% chlorhexidine can be used as a vehicle in calcium hydroxide pastes. © 2009 Sociedade Brasileira de Pesquisa Odontológica.

Bleaching effectiveness, hydrogen peroxide diffusion, and cytotoxicity of a chemically activated bleaching gel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Diffusion of Lambda(c) in hot hadronic medium and its impact on Lambda(c)/D ratio

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)