Influence of thermal and mechanical stresses on the strength of intact and relined denture bases

Statement of problem. Denture bases may become increasingly weaker as a result of thermal stress and flexural cyclic loading. Information regarding this potential problem and its relationship to the denture base reline is limited.Purpose. This study evaluated the influence of thermal and mechanical stresses on the strength of intact and relined denture bases.Material and methods. Twenty-eight microwave-polymerized (Acron MC) intact denture bases were prepared in the shape of a 3-mm-thick maxillary denture. Additionally, fifty-six 2-mm-thick denture bases were relined with 1 mm of autopolymerizing resin (Tokuyama Rebase Fast II or New Truliner) (n = 28). Intact and relined specimens were divided into 4 groups (n = 7) as follows: without stress (control); a mechanical stress at 0.8 Hz for 10,000 cycles; 5000 thermal cycles between 5 degrees C and 55 degrees C; or a combination thermo-mechanical stress. The specimens were vertically loaded in compression with a rounded rod at 5 mm/min until failure, using a universal testing machine. Data on maximum fracture load (N), deflection at fracture (%), and fracture energy (N-mm) were analyzed by 2-way analysis of variance and Student-Newman-Keuls tests (alpha = .05).Results. The strength of the denture bases relined with New Truliner was not significantly affected by any of the experimental conditions, but comparing the control groups, New Truliner exhibited the lowest maximum fracture load values. The maximum fracture load of intact denture bases (P = .002) and those relined with Tokuyama Rebase Fast II (P = .01) showed a significant decrease after thermal stress. Additionally, cyclic loading significantly decreased the maximum fracture load (P < .001), deflection at fracture (P = .025), and fracture energy (P < .001) of intact denture bases and those relined with Tokuyama Rebase (P values of .002, .039, and .001, respectively).Conclusion. Thermal and mechanical stresses exert deleterious effects on the strength of intact and/or relined denture bases, which vary according to the relining material used.

Shear Bond Strength of Different Repair Systems to Titanium After Water Aging

This study evaluated the shear bond strength (SBS) and stability of commercially pure titanium (CP Ti)/repair material interfaces promoted by different repair systems. One hundred CP Ti cast discs were divided into five repair system groups: 1) Epricord (EP); 2) Bistite 11 DC (BT); 3) Cojet (CJ); 4) Scotchbond Multi-Purpose Plus (SB) (control group); and 5) Cojet Sand plus Scotchbond Multi-Purpose Plus (CJSB). The specimens were stored in distilled water for 24 hours at 37 degrees C, thermal cycled (5000 cycles, 5 degrees-55 degrees C) and stored under the same conditions for either 24 hours or six months (n=10). SBS was tested and the data were analyzed by two-way analysis of variance (ANOVA) and Tukey test (alpha=.05). Failure mode was determined with a stereomicroscope (20x). The repair system, storage time, and their interaction significantly affected the SBS (p<0.001). At 24 hours, CJSB exhibited the highest SBS value, followed by CJ. At six months, these two groups had similar mean SBS (p>0.05) and higher means in comparison to the other groups. For both storage times, BT presented the lowest SBS, while the EP and SB groups did not differ significantly from one another (p>0.05). There were no significant differences in SBS between the storage times for the groups EP and CJ (p>0.05). The groups BT, SB, and CJSB showed 100% adhesive failure, irrespective of storage time. The CJSB group showed the highest SBS at both storage times. At six months, the CJ group exhibited a similar SBS mean value when compared to the CJSB group. Water storage adversely affected the groups BT, SB (control group), and CJSB. Considering SBS values, stability, and the failure mode simultaneously, the CJ group showed the best CP Ti repair performance.

Effect of Conventional and Resin-modified Glass-Ionomer Liner on Dentin Adhesive Interface of Class I Cavity Walls After Thermocycling

Objective: The aim of this in vitro study was to analyze the effect of glass-ionomer cement as a liner on the dentin/resin adhesive interface of lateral walls of occlusal restorations after thermocycling.Materials and Methods: Occlusal cavities were prepared in 60 human molars, divided into six groups: no liner (1 and 4); glass-ionomer cement (GIC, Ketac Molar Easymix, 3M ESPE) (2 and 5); and resin-modified glass-ionomer cement (RMGIC, Vitrebond, 3M ESPE) (3 and 6). Resin composite (Filtek Z250, 3M ESPE) was placed after application of an adhesive system (Adper Single Bond 2, 3M ESPE) that was mixed with a fluorescent reagent (Rhodamine B) to allow confocal microscopy analysis. Specimens of groups 4, 5 and 6 were thermocycled (5 degrees C-55 degrees C) with a dwell time of 30 seconds for 5000 cycles. After this period, teeth were sectioned in approximately 0.8-mm slices. One slice of each tooth was randomly selected for confocal microscopy analysis. The other slices were sectioned into 0.8 nun x 0.8 mm beams, which were submitted to microtensile testing (MPa). Data were analyzed using two-way ANOVA and Tukey test (p < 0.05).Results: There was no detectedstatistical difference on bond strength among groups (alpha < 0.05). Confocal microscopy analysis showed a higher mean gap size in group 4(12.5 mu m) and a higher percentage of marginal gaps in the thermocycled groups. The RNIGIC liner groups showed the lowest percentage of marginal gaps.Conclusions: Lining with RMGIC resulted in less gap formation at the dentin/resin adhesive interface after artificial aging. RMGIC or GIC liners did not alter the microtensile bond strength of adhesive system/resin composite to dentin on the lateral walls of Class I restorations.

CONCERTED ACTION OF THE HIGH-AFFINITY CALCIUM-BINDING SITES IN SKELETAL-MUSCLE TROPONIN-C

Mutants of each of the four divalent cation binding sites of chicken skeletal muscle troponin C (TnC) were constructed using site directed mutagenesis to convert Asp to Ala at the first coordinating position in each site. With a view to evaluating the importance of site-site interactions both within and between the N- and C-terminal domains, in this study the mutants are examined for their ability to associate with other components of the troponin-tropomyosin regulatory complex and to regulate thin filaments. The functional effects of each mutation in reconstitution assays are largely confined to the domain in which it occurs, where the unmutated site is unable to compensate for the defect, Thus the mutants of sites I and II bind to the regulatory complex but are impaired in ability to regulate tension and actomyosin ATPase activity, whereas the mutants of sites III and IV regulate activity but are unable to remain bound to thin filaments unless Ca2+ is present. When all four sites are intact, free Mg2+ causes a 50-60-fold increase in TnC's affinity for the other components of the regulatory complex, allowing it to attach firmly to thin filaments. Calcium can replace Mg2+ at a concentration ratio of 1:5000, and at this ratio the Ca2 . TnC complex is more tightly bound to the filaments than the Mg2 . TnC form, In the C-terminal mutants, higher concentrations of Ca2+ (above tension threshold) are required to effect this transformation than in the recombinant wild-type protein, suggesting that the mutants reveal an attachment mediated by Ca2+ in the N-domain sites.

AN EXTREMELY LARGE, CAULIFLOWER-TYPE, CUTANEOUS METASTASIS OF OVARIAN-CANCER ASSOCIATED WITH GOOD PROGNOSIS

We report an unusual case of a 37-year-old woman who presented in 1980 with a serous papillary cystadenocarcinoma of the ovary. The patient refused any treatment and the patient was lost to follow-up for 6 years. After this period of time she returned with an extremely large, cutaneous, cauliflower-type of metastasis located in the lower abdominal wall and measuring 20 x 20 cm. She received two courses of chemotherapy treatment consisting of intraperitoneal cisplatin (100 mg/m2) and intravenous epirubicin (50 mg/m2) every 3 weeks. After the second course of chemotherapy she received cobalt radiotherapy (5000 cGy). Subsequently, she received four more courses of chemotherapy with dramatic remission of the cutaneous metastasis. Shortly after chemotherapy, the patient underwent a laparotomy consisting of the resection of the abdominal wall including the cutaneous metastasis completed by total abdominal hysterectomy, bilateral salpingo-oophorectomy, and omentectomy. The patient is well after the surgery and without any evidence of residual disease after 6 years of follow up. This description illustrates a rare example of ovarian cancer with skin metastases and favorable outcome. (C) 1994 Academic Press, Inc.

Effect of cleansing methods on saliva-contaminated zirconia: an evaluation of resin bond durability

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

In vitro effect of calcium-containing prescription-strength fluoride toothpastes on bovine enamel erosion under hyposalivation-simulating conditions

Purpose: To evaluate the ability of calcium-containing prescription-strength fluoride (F) toothpastes in preventing enamel erosion under low salivary flow simulating conditions. Methods: Enamel and dentin bovine specimens were assigned to the following groups: A - placebo; B - 1,100 ppm F/NaF (Aquafresh Advanced); C - 5,000 ppm F/NaF (Prevident 5000 Booster); D - 5000 ppm F/NaF+calcium sodium phosphosilicate (Topex Renew); and E - 5,000 ppm F/NaF+tri-calcium phosphate (Clinpro 5000). Specimens were positioned in custom-made devices, creating a sealed chamber on the surface, connected to peristaltic pumps. Citric acid was injected into the chamber for 2 minutes, followed by artificial saliva (0.05 ml/minute), for 60 minutes, 4x/day, for 3 days. Aquafresh was also tested under normal salivary flow (0.5 ml/minute), as reference (Group F). Specimens were exposed to the toothpastes for 2 minutes, 2x/day. After cycling, surface loss (SL) and concentration of loosely- and firmly-bound F were determined. Data were analyzed by ANOVA. Results: Group A (placebo) presented highest surface loss (SL), while Group F had the lowest, for both substrates. For enamel, none of the dentifrices differed from Group B or among each other. For dentin, none of the dentifrices differed from Group B, but Group E showed greater protection than Group C. Group E presented the highest F concentrations for both substrates, only matched by Group D for firmly-bound fluoride on enamel. All fluoridated dentifrices tested reduced SL, with no additional benefit from higher F concentrations. Some formulations, especially Clinpro 5000, increased F availability on the dental substrates, but no further erosion protection was observed.

Poluentes orgânicos persistentes em ar interior: desenvolvimento de método de extração em adsorvente para amostragem ativa

Persistent Organic Pollutants (POPs) are chemical substances extraordinarily toxic and persistent in the environment. Due to these properties, POPs are targets of the Stockholm Convention which aims to provide means to eliminate production and use by encouraging the reduction and, where possible, eliminating the release of these contaminants to the environment. One of the articles of this _Convention aims to assess the basal levels of such substances in the environment to monitor both the reduction of release to the environment, and to assess human exposure, using analyzes of milk and air for example. Although efforts to control POPs production and release to the environment have been made, data about their levels in Brazil are still scarce, mainly in the atmosphere or indoor environment. Considering the permanence of people inside its house, this study presents a method for POP extraction from XAD-2 sorbent employed in indoor air sampling, with identification and quantification by GC-ECD. GC-ECD linear range of the studied analytes, congeners of polychlorinated biphenyls (PCB) (28, 52, 101, 118, 138, 153 and 180), DDTs and their metabolites (DDDs, DDEs) and endosullan (isomers c - and 13 - and metabolite endosulfan sulfate) ranged between 0.5 and 16.0 ng mL-I with r2 > 0.967. The method developing consist of selecting the extraction solvent system by agitation (90 rpm, 1 hour) with n-hexan,e (2 mL) or n-hexane:acetone (1:1, v/v) (2 mL), concentration the extract with a gentle N2 stream, and evaluation of breakthrough with passage or air through the fortified XAD-2 cartridge before extraction, employing a low volume air suction pump (Pump Model 224 universal-PCXR8; 5-5000 mL min-1, SKC Inc., Eighty Four, PA, USA), Calibrator Dry-Cal DC-Lite (BIOS, Butler, NJ, USA)). Two fortification levels were employed, 15 and 30 ng. After selecting n-hexane as extraction solvent, with accuracy and precision ranging...

Orcs Inc. - jogo de tabuleiro empresarial: capacitação profissional através do lúdico

A proposta deste trabalho é criar um Jogo de Tabuleiro Empresarial voltado para a capacitação de profissionais de micro e pequenas empresas em comunicação, juntamente com a aluna de Design da Unesp - Bauru, Tatiana Kurokawa Hasimoto. Observando o poder dessa ferramenta em outras áreas do conhecimento (como administração e empreendedorismo) exploramos o potencial da área de comunicação para a criação de um Jogo de Tabuleiro Empresarial, voltado para a capacitação e seleção. O trabalho tem como base um mapeamento de microempresas da cidade de Bauru, realizado pelo Núcleo de Opinião da UNESP, coordenado pela Profª Drª Célia Maria Retz Godoy dos Santos, onde foi possível perceber a falta de conhecimento sobre a área de comunicação por essas empresas. O objetivo é mostrar a importância da comunicação e principalmente como o profissional de Relações Públicas pode atuar nessas empresas