Electrocatalysis of hydrogen evolution reaction on Pt electrode surface-modified by S-2 chemisorption

Kinetic studies of hydrogen evolution reaction (HER) at the surface of Pt in alkaline conditions, reported in this paper, show that electrocatalytic activity is enhanced after adsorption of S-2 ions. EIS and steady-state polarization curve data pointed to an undoubted improvement in performance with the Pt-S cathode that was attributed to higher adsorbed hydrogen coverage. Experimental findings suggested an increase in the electronic density of the modified surface sites that may strengthen the interaction between H2O and the adsorption site and, consequently, accelerates the Volmer step. (c) 2006 International Association for Hydrogen Energy. Published by Elsevier Ltd. All rights reserved.

The hydrogen evolution reaction on codeposited Ni-hydrogen storage intermetallic particles in alkaline medium

The hydrogen evolution reaction (HER) was studied on Ni-LaNi5 and Ni-MmNi(3.4)Co(0.8)Al(0.8) electrode materials in 1 mol dm(-3) NaOH solution. The steady-state polarization curves and electrochemical impedance spectroscopy experimental data showed a pronounced improvement in HER kinetics when these electrode materials were used. The electrochemical results are in accordance with the Volmer-Heyrovsky mechanism. The kinetic results indicate a more effective improvement in the Heyrovsky step, suggesting an electrocatalytic synergistic effect of the hyper-electronic character of the Ni and the hypo-electronic character of the rare-earth element on the electrode surface. (C) 2000 International Association for Hydrogen Energy. Published by Elsevier B.V. Ltd. All rights reserved.

SURFACE EFFECTS IN THE HYDROGEN EVOLUTION REACTION ON NI-ZN ALLOY ELECTRODES IN ALKALINE-SOLUTIONS

Hydrogen evolution reaction was studied on Ni-Zn (25% of Ni before leaching) in 1 M NaOH at 25 degrees C. These electrodes were characterized by very low Tafel slopes of 67 mV dec(-1). Other techniques used included potential and current pulse, potential relaxation in an open circuit, and ac impedance spectroscopy. Analysis of the experimental results led to the conclusion that hydrogen adsorption in the surface layers was responsible for the observed behavior. Influence of the oxidation of the electrode surface and the addition of poisons, thiourea and cyanides, were also studied. These processes inhibit the hydrogen absorption and restore ''normal'' Tafel slopes. Kinetic parameters of the hydrogen evolution reaction were determined.

Electrode surface modifications improve cathode hydrogen production and anode capacity in Ni-MH batteries

This paper reports results from electrochemical evaluations of electrodes used as cathodes for a hydrogen evolution reaction and anodes in Ni-MH batteries that had been surface-modified by micro-encapsulation, co-deposition and sol-gel methods. The surface modifications produced actual improvements in the corresponding electrochemical reactions by enhancing the performance and/or the mechanical stability of the electrode material. (c) 2005 International Association for Hydrogen Energy. Published by Elsevier Ltd. All rights reserved.

A spectroelectrochemical study of the inhibition of the electrode process on copper by 2-mercaptobenzothiazole in ethanolic solutions

The effect of 2-mercaptobenzothiazole (MBT) on the corrosion of copper in ethanol-water mixture with 0.01 mol dm(-3) HClO4 was investigated by linear sweep voltammetry and surface enhanced Raman scattering spectroscopy. The linear sweep voltammetry for the copper electrode in the presence of MBT shows one anodic process associated with the oxidation of MBT, which leads to the formation of a film on the electrode. This film inhibits the anodic copper dissolution and cathodic hydrogen evolution reaction. SERS studies indicated that MBT oxidizes and forms polymeric complexes involving copper ions and the ionized form of thiol. (C) 1997 Elsevier B.V. Ltd.

Platinum surface modification with cerium species and the effect against the methanol anodic reaction

Spontaneous deposition and electrochemical deposition by potential perturbation programs were used to place cerium-containing species on platinum surfaces in acid solution. Cyclic voltammetric profiles of cerium-modified platinum surfaces obtained after potentiostatic or potentiodynamic procedures (applied in the true hydrogen evolution region) differ from those recorded after spontaneous methods. However, the catalytic effects are nearly the same on these cerium-modified platinum surfaces for methanol electrooxidation, i.e. lower onset potential values for the anodic reaction. Besides, a different electrocatalytic effect was observed at large positive potentials on methanol oxidation due to the cerium oxide capability of oxygen storage. This effect is observed on platinum modified by a drastic potentiostatic procedure (by applying -2.0 V) in cerium(IV) acid solution. (C) 2008 Elsevier B.V. All rights reserved.

Electrocatalysis of oxidation of hydrogen on platinum ordered intermetallic phases: Kinetic and mechanistic studies

An experimentally based kinetic and mechanistic study of the hydrogen oxidation reaction (HOR) on platinum and platinum ordered intermetallic materials in acid medium is presented. RDE kinetic data were re-evaluated and complemented by Tafel plots obtained from chronoamperometric measurements. Among the materials evaluated, PtSb and PtSn exhibited markedly improved kinetic current densities and exchange current densities, compared to Pt in the same experimental conditions. It is proposed that the intermetallic phase enhanced the adsorptive characteristic of the surface sites and, as a consequence, improved the kinetics of the adsorption steps (Tafel or Heyrovsky) of the mechanism involved. (c) 2006 Published by Elsevier B.V.

Hydrogen oxidation on ordered intermetallic electrodes covered with CO

This describes an experimental evaluation of the electrocatalytic activity of the hydrogen oxidation reaction on electrodes of platinum and the ordered intermetallic phases PtSb and PtSn, on which CO has previously been deposited. The experiments were carried out in perchloric acid solution and the analysis based on steady-state polarization curves and Tafel plots derived from chronoamperometric data. Both intermetallics, PtSb and PtSn, performed better than Pt towards the HOR, when their surface was deliberately covered with CO. It is suggested that the intermetallic surfaces have a lower affinity for CO molecules, causing a lower CO coverage on these surfaces, and/or a weaker surface-CO interaction, compared to Pt under the same conditions. (C) 2007 Elsevier B.V. All rights reserved.

Changes on iron electrode surface during hydrogen permeation in borate buffer solution

Hydrogen interaction with oxide films grown on iron electrodes at open circuit potential (E-oc) and in the passive region (+0.30 V-ECS) was studied by chronopotentiometry, chronoamperometry and electrochemical impedance spectroscopy techniques. The results were obtained in deaerated 0.3 mol L-1 H3BO3 + 0.075 mol L-1 Na2B4O7 (BB, pH 8.4) solution before, during and after hydrogen permeation. The iron oxide film modification was also investigated by means of in situ X-ray absorption near-edge spectroscopy (XANES) and scanning electrochemical microscopy (SECM) before and during hydrogen permeation. The main conclusion was that the passive film is reduced during the hydrogen diffusion. The hydrogen permeation stabilizes the iron surface at a potential close to the thermodynamic water stability line where hydrogen evolution can occur. The stationary condition required for the determination of the permeation parameters cannot be easily attained on iron surface during hydrogen permeation. Moreover, additional attention must be paid when obtaining the transport parameters using the classical permeation cell. (c) 2007 Elsevier Ltd. All rights reserved.

Preparation of Fe-Cr-P-Co amorphous alloys by electrodeposition

The effects of bath composition and electroplating conditions on structure, morphology, and composition of amorphous Fe-Cr-P-Co deposits on AISI 1020 steel substrate, priorly plated with a thin Cu deposit, were investigated. The increase of charge density activates the inclusion of Cr in the deposit. However, above specific values of the charge density, which depend on the deposition current density, the Cr content in the deposit decreases. This Cr content decreasing is probably due to the significant hydrogen evolution with the increasing of deposition cur-rent and charge density. The effect of charge density on the content of Fe and Co is not clear. However, there is a tendency of increasing of Fe content and decreasing of Co content with the raising of current density. The Co is more easily deposited than the P, and its presence results in a more intense inhibition effect on the Cr deposition than the inhibition effect caused by P presence. Scanning electron microscope (SEM) analysis showed that Co increasing in the Fe-Cr-P-Co alloys analyzed does not promote the susceptibility to microcracks, which led to a good quality deposit. The passive film of the Fe-Cr-P-Co alloy shows a high ability formation and high protective capacity, and the results obtained by current density of corrosion, j(cor), show that the deposit with addition of Co, Fe31Cr11P28Co30, presents a higher corrosion resistance than the deposit with addition of Ni, Fe54Cr21P20Ni5. (C) 2004 Published by Elsevier B.V.

A disposable chitosan-modified carbon fiber electrode for dengue virus envelope protein detection

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

CATHODIC BEHAVIOUR of ANODIZED TITANIUM IN SIMULATED PHYSIOLOGICAL CONDITIONS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microstructural characteristics and electrochemical behavior of Co3O4 sintered electrodes

Co3O4 can be used as electrocatalyst for oxygen evolution reaction. The macro and microstructure of the oxide, obtained by compacting and sintering lithium-doped Co3O4 powder in atmosphere of dry air and in conditions of controlled temperature and time was analyzed by metallographic techniques. The porous material was characterized by XRD, SEM and EDS combined techniques. For working temperatures up to 1200°C, the pellet was consituted of particles with varying sizes over a wide range of particle size and, at higher temperatures CoO is formed and polymorphic transformation was observed. The materials were also characterized electrochemically in alkaline media by open circuit potential and potentiodynamic I/E measurements. The results were compared to those previously prepared by others by thermal deposition.

Comportamento eletroquímico do crômio em soluções contendo íons cloreto

Pós-graduação em Química - IQ

Filmes de 'CO' obtidos por deslocamento galvânico e suas propriedades magnéticas

Pós-graduação em Química - IQ