Hardness and compressive strength of indirect composite resins: effects of immersion in distilled water

The aim of this study was to evaluate the effect of ageing in distilled water on the hardness and compressive strength of a direct composite resin Z100, a feldspatic porcelain (Noritake) and three indirect composites (Artglass, Solidex and Targis). For the Vickers hardness tests, five disk-shaped specimens (2 x 4 mm) of each material were prepared according to the manufacturers' instructions. The hardness tests were conducted using a Vickers diamond indentor. Compressive strength measurements were recorded on cylindrical specimens with a diameter of 6 mm and a length of 12 mm. The compression tests were carried out with a constant cross-head speed of 0.5 mm min(-1) on a mechanical test machine. For each material, 10 specimens were tested after 7 days of dry storage at 37 +/- 1 degreesC and 10 specimens were tested after water storage at 37 +/- 1 degreesC for 180 days. Noritake porcelain specimens showed higher hardness values than the composites. Among the composite materials, Z100 promoted the highest VHN values, regardless of the ageing periods. The results showed that Solidex and Z100 had the highest compressive strength values. Ageing in water reduced the hardness for all composites, but had no long-term effect on the compressive strength.

Effect of chlorhexidine gluconate on porosity and compressive strength of a glass ionomer cement

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Compressive strength and setting time of MTA and portland cement associated with different radiopacifying agents

The aim of this study was to evaluate the compressive strength and setting time of MTA and Portland cement (PC) associated with bismuth oxide (BO), zirconium oxide (ZO), calcium tungstate (CT), and strontium carbonate (SC). Methods. For the compressive strength test, specimens were evaluated in an EMIC DL 2000 apparatus at 0.5 mm/min speed. For evaluation of setting time, each material was analyzed using Gilmore-type needles. The statistical analysis was performed with ANOVA and the Tukey tests, at 5% significance. Results. After 24 hours, the highest values were found for PC and PC + ZO. At 21 days, PC + BO showed the lowest compressive strength among all the groups. The initial setting time was greater for PC. The final setting time was greater for PC and PC + CT, and MTA had the lowest among the evaluated materials (< 0.05). Conclusion. The results showed that all radiopacifying agents tested may potentially be used in association with PC to replace BO.

Compressive strength of dental composites photo-activated with different light tips

The aim of this study was to evaluate the compressive strength of microhybrid (Filtek™ Z250) and nanofilled (Filtek™ Supreme XT) composite resins photo-activated with two different light guide tips, fiber optic and polymer, coupled with one LED. The power density was 653 mW cm -2 when using the fiber optic light tip and 596 mW cm-2 with the polymer. After storage in distilled water at 37 ± 2 °C for seven days, the samples were subjected to mechanical testing of compressive strength in an EMIC universal mechanical testing machine with a load cell of 5 kN and speed of 0.5 mm min-1. The statistical analysis was performed using ANOVA with a confidence interval of 95% and Tamhane's test. The results showed that the mean values of compressive strength were not influenced by the different light tips (p > 0.05). However, a statistical difference was observed (p < 0.001) between the microhybrid composite resin photo-activated with the fiber optic light tip and the nanofilled composite resin. Based on these results, it can be concluded that microhybrid composite resin photo-activated with the fiber optic light tip showed better results than nanofilled, regardless of the tip used, and the type of the light tip did not influence the compressive strength of either composite. Thus, the presented results suggest that both the fiber optic and polymer light guide tips provide adequate compressive strength to be used to make restorations. However, the fiber optic light tip associated with microhybrid composite resin may be an interesting option for restorations mainly in posterior teeth. © 2013 Astro Ltd.

Comparison of compressive strength between three different plates for mandibular angle fractures fixation

The present study aims to compare three types of internal fixation for fractures of the mandibular angle. Mechanical testing was performed on replicas of polyurethane hemimandibles sectioned at the angle region to simulate a fracture and fixed with three different hardwares. Fixation devices enrolled on this survey included the grid plates with and without an intermediate bar and the method described by Champy and colleagues in 1978 and the sample consisted of 10 hemimandibles for each group. Vertical loadings were applied on each hemimandible and recorded after a vertical displacement of 3 and 5 mm. Statistical analysis was made by means of the variance analysis (ANOVA) and the Duncan test with a significance level of 5%. The Champy technique showed a statistically significant increased resistance when compared to the grid plates after vertical displacements of 3 and 5 mm. The results of this survey suggest that the Champy technique, when compared to the grid plate positioned at the middle of the mandibular bone (placement site selected for this study), is more resistant than the grid plate and that the inclusion or not of an intermediate bar to the grid plates does not improve its resistance after linear vertical loadings.

Influence of Nd:YAG laser on intrapulpal temperature and bond strength of human dentin under simulated pulpal pressure

The aim of this study was to evaluate the effects of simulated pulpal pressure (SPP) on the variation of intrapulpal temperature (ΔT) and microtensile bond strength (μTBS) to dentin submitted to an adhesive technique using laser irradiation. One hundred sound human molars were randomly divided into two groups (n = 50), according to the presence or absence of SPP (15 cm H2O). Each group was divided into five subgroups (n = 10) according to Nd:YAG laser energy (60, 80, 100, 120, 140 mJ/pulse). The samples were sequentially treated with the following: 37 % phosphoric acid, adhesive (Scotchbond Universal), irradiation with Nd:YAG laser (60 s), and light curing (10 s). ΔT was evaluated during laser irradiation using a type K thermocouple. Next, a composite resin block was build up onto the irradiated area. After 48 h, samples were submitted to microtensile test (10 kgf load cell, 0.5 mm/min). Data were analyzed by two-way ANOVA and Tukey tests (p = 0.05). ANOVA revealed significant differences for ΔT and TBS in the presence of SPP. For ΔT, the highest mean (14.3 ± 3.23 °C)(A) was observed in 140 mJ and without SPP. For μTBS, the highest mean (33.4 ± 4.15 MPa)(A) was observed in 140 mJ and without SPP. SPP significantly reduced both ΔT and μTBS during adhesive procedures, lower laser energy parameters resulted in smaller ΔT, and the laser parameters did not influence the μTBS values.

Evaluation of WC-17Co and WC-10Co-4Cr thermal spray coatings by HVOF on the fatigue and corrosion strength of AISI 4340 steel

It is known that chromium electroplating is related to the reduction in the fatigue strength of base metal. However, chromium results in protection against wear and corrosion combined with chemical resistance and good lubricity. Environmental requirements are an important point to be considered in the search for possible alternatives to hard chrome plating. Aircraft landing gear manufactures are considering WC thermal spray coating applied by the high-velocity oxygen-fuel (HVOF) process an alternative candidate, which shows performance at least comparable to results, obtained for hard chrome plating. The aim of this study is to compare the influence of WC-17Co and WC-10Co-4Cr coatings applied by HVOF process and hard chromium electroplating on the fatigue strength of AISI 4340 steel, with and without shot peening. S-N curves were obtained in axial fatigue test for base material, chromium plated and tungsten carbide coated specimens. Tungsten carbide thermal spray coating results in higher fatigue strength when compared to hard chromium electroplated. Shot peening prior to thermal spraying showed to be an excellent alternative to increase fatigue strength of AISI 4340 steel. Experimental data showed higher axial fatigue and corrosion resistance in salt fog exposure for samples WC-10Co-4Cr HVOF coated when compared with WC-17Co. Fracture surface analysis by scanning electron microscopy (SEM) indicated the existence of a uniform coverage of nearly all substrates. (C) 2004 Elsevier B.V. All rights reserved.

Fractography analysis and fatigue strength of carbon fiber/RTM6 laminates

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

End-to-end arterial anastomosis with fibrin glue in larger arteries: histology, hydroxyproline concentration and tensile strength study in carotids of rabbits

A anastomose arterial término-terminal é demorada, requer tempo prolongado de oclusão vascular e esta associada a necrose focal, infiltração leucocitária e, conseqüentemente, à fibrose e calcificação da parede arterial. A cola de fibrina é uma alternativa para a anastomose microvascular e pode evitar estas alterações com menor aderência aos tecidos vizinhos e melhor coaptação das bordas arteriais. OBJETIVO: Comparar o processo cicatricial de anastomoses convencionais com anastomoses feitas com cola de fibrina em artérias maiores. MÉTODOS: em 22 coelhos, ambas carótidas foram seccionadas transversalmente e reconstruídas por meio de anastomose término-terminal com 4 pontos simples de reparo e cola de fibrina de um lado (G1), e com 8 pontos separados do outro lado (G2). Após 3 e 15 dias, os animais foram destinados aleatoriamente para estudo de força tênsil concentração de hidroxiprolina (8 animais) e avaliação histológica das anastomoses (3 animais). As lâminas histológicas foram coradas pelo HE Masson e Picrossirius polarização (PSP). RESULTADOS: Após 3 e 15 dias a força tênsil aumenta em ambos os grupos, de 280,0± 32,6g para 432,2± 131,2g no Grupo 1 e de 221,4± 72,4g para 452,2± 132,0g no Grupo 2; sem diferença estatística entre os grupos em cada período. A concentração de hidroxiprolina expressa como razão hidroxiprolina/proteína, variou de 0,0816± 0,0651 para 0,0622± 0,0184 no Grupo 1 e de 0,0734± 0,0577 para 0,0460± 0,0271 no Grupo 2; sem diferença estatística entre os períodos e grupos. Os estudos histológicos mostraram discreto aumento das reações de inflamação e reparação no Grupo 2. A técnica PSP mostrou predomínio do colágeno tipo I em relação do colágeno tipo II nas anastomoses de ambos os grupos, sem diferença expressiva entre esses grupos. CONCLUSÃO: A anastomose com a cola de fibrina foi menos lesiva para a parede arterial do que a anastomose convencional. Mesmo usando menos pontos, as características de força tênsil e de cicatrização da anastomose com cola de fibrina foram similares em ambos os grupos. Os tempos de realização das anastomoses foram significativamente maiores do que na anastomose convencional.

Resting energy expenditure and carbohydrate oxidation are higher in elderly patients with COPD: a case control study

Background: Elderly patients with chronic obstructive pulmonary disease (COPD) usually have a compromised nutritional status which is an independent predictor of morbidity and mortality. To know the Resting Energy Expenditure (REE) and the substrate oxidation measurement is essential to prevent these complications. This study aimed to compare the REE, respiratory quotient (RQ) and body composition between patients with and without COPD.Methods: This case-control study assessed 20 patients with chronic obstructive pulmonary disease attending a pulmonary rehabilitation program. The group of subjects without COPD (control group) consisted of 20 elderly patients attending a university gym, patients of a private service and a public healthy care. Consumption of oxygen (O-2) and carbon dioxide (CO2) was determined by indirect calorimetry and used for calculating the resting energy expenditure and respiratory quotient. Body mass index (BMI) and waist circumference (WC) were also measured. Percentage of body fat (%BF), lean mass (kg) and muscle mass (kg) were determined by bioimpedance. The fat free mass index (FFMI) and muscle mass index (MMI) were then calculated.Results: The COPD group had lower BMI than control (p = 0.02). However, WC, % BF, FFMI and MM-I did not differ between the groups. The COPD group had greater RQ (p = 0.01), REE (p = 0.009) and carbohydrate oxidation (p = 0.002).Conclusions: Elderly patients with COPD had higher REE, RQ and carbohydrate oxidation than controls.

Evaluation of strain, dietary energy level and stocking density on broiler feathering

This study evaluated the effects of strain, stocking density and dietary energy level on the feathering of broiler chickens. Four trials were carried out between September 2000 and April 2002. There were 10,685 broiler chicks from the strains Ross 308, Cobb 500, Hybro PG, Hubbard, MPK, and Isa Vedette. The bids were reared at stocking densities varying between 10 and 16 birds/m² and were given diets containing different metabolizable energy levels. Broiler feathering was evaluated either by atrributing scores from 1 to 10 to feather covering along the thigh and back (visual inspection), or by determining the percentage weight of the feathers at 28 and 42 days of age. Increasing rearing densities resulted in poorer feathering, mainly if 12 or 13 birds/m² were compared with 16 birds/m². The strains showed different feathering; it was better in Cobb 500 and MPK birds, whereas Hubbard birds showed poorer feathering, mostly along the back. The energy level in the diet has also affected feathering scores. Medium energy level resulted in better feathering along the back at 28 days, and the low level, in better feathering along the thigh at 35 days of age. Finally, feather scores were better in females than in males.

Effect of thermocycling on the flexural and impact strength of urethane-based and high-impact denture base resins

Objective: Mechanical properties of the acrylic resins used for denture fabrication may be influenced by water and temperature. Thus, the aim of this study was to evaluate the effect of thermocycling on the flexural and impact strength of a high-impact (Lucitone 199) and a urethane-based denture material (Eclipse).Materials and methods: Flexural strength (64 x 10 x 3.3 mm) and impact strength (60 x 6 x 4 mm) specimens were made following the manufacturers' instructions and assigned to two groups (n = 10): control (C) - not thermocycled - and T - thermocycled (5000 cycles between 5 and 55 degrees C). Specimens were submitted to three-point bending and Charpy impact tests.Results: Flexural strength (MPa) and impact strength (kJ/m(2)) data were analysed with two-way ANOVA (p = 0.05). The flexural strength of material Eclipse (C, 136.5; T, 130.7) was significantly higher than that of resin Lucitone 550 (C, 99.4; T, 90.1). Material Eclipse exhibited significantly higher impact strength (C, 6.9; T, 5.3) than the resin Lucitone 550 (C, 3.5; T, 3.0). For both materials, a significant decrease in flexural and impact strengths was observed when the specimens were thermocycled.Conclusion: Flexural and impact strengths were higher for Eclipse than for Lucitone 550, in both groups. Thermocycling decreased the flexural and impact strengths of Eclipse and Lucitone 550.