Caracterização de uma cerâmica 3Y-TZP e avaliação do efeito de tratamentos de superfície na adesão da cerâmica ao glaze ou cimento resinoso

Pós-graduação em Odontologia Restauradora - ICT

Hard machining, glaze firing and hydrofluoric acid etching: Do these procedures affect the flexural strength of a leucite glass-ceramic?

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Confocal Laser Microscopic Analysis of Biofilm on Newer Feldspar Ceramic

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Strain Gauge Analysis of the Effect of Porcelain Firing Simulation on the Prosthetic Misfit of Implant-Supported Frameworks

Objectives: This study investigated the effect of porcelain firing on the misfit of implant-supported frameworks and analyzed the influence of preheat treatment on the dimensional alterations.Materials and Methods: Four external-hex cylindrical implants were placed in polyurethane block. Ten frameworks of screw-retained implant-supported prostheses were cast in Pd-Ag using 2 procedures: (1) control group (CG, n = 5): cast in segments and laser welded; and test group (TG, n = 5): cast in segments, preheated, and laser welded. All samples were subjected to firing to simulate porcelain veneering firing. Strain gauges were bonded around the implants, and microstrain values (mu epsilon = 10(-6)epsilon) were recorded after welding (M1), oxidation cycle (M2), and glaze firing (M3). Data were statistically analyzed (2-way analysis of variance, Bonferroni, alpha = 0.05).Results: The microstrain value in the CG at M3 (475.2 mu epsilon) was significantly different from the values observed at M1 (355.6 mu epsilon) and M2 (413.9 mu epsilon). The values at M2 and M3 in the CG were not statistically different. Microstrain values recorded at different moments (M1: 361.6 mu epsilon/M2: 335.3 mu epsilon/M3: 307.2 mu epsilon) did not show significant difference.Conclusions: The framework misfit deteriorates during firing cycles of porcelain veneering. Metal distortion after porcelain veneering could be controlled by preheat treatment. (Implant Dent 2012;21:225-229)

Effectiveness of surface protection for resin-modified glass-ionomer materials

Objective: the purpose of this study was to evaluate the effectiveness of various surface treatments for resin-modified glass-ionomer restorative materials by determining dye uptake spectrophotometrically. Method and materials: Two hundred twenty-four specimens, 4.1 mm in diameter and 2.0 mm thick, were made of 3 materials: Vitremer, Fuji II LC, and Photac-Fil Aplicap. Specimens were divided into 15 groups. The positive and negative control specimens remained unprotected, while the experimental specimens were protected with Heliobond light-activated bonding resin, Colorama nail varnish, or surface coatings indicated by the manufacturers of the glass-ionomer materials. Finishing Gloss for Vitremer, Fuji Varnish for Fuji II LC, and Ketac Glaze for Photac-Fil. The disks were immersed in 0.05% methylene blue for 24 hours except for the negative control group, which was immersed in deionized water. After 24 hours, the disks were removed, washed, and individually placed in 1 mL of 65% nitric acid for 24 hours. The solutions were centrifuged and the spectrophotometric absorbance was determined at 606 nm. The dye uptake was expressed in micrograms of dye per milliliter, and the results were analyzed with the Kruskal-Wallis test. Results: There were no differences in dye uptake among the 3 resin-modified glass-ionomer restorative materials, however, all of them required surface protection. Conclusion: the best surface protection for the 3 evaluated materials was obtained with Heliobond light-activated bonding resin.

SEM analysis of the in situ early bacterial colonization on two novel feldspathic ceramics submitted to different types of glazing

Aim: The aim of this study was to evaluate in situ, the early bacterial colonization on feldspar-ceramics submitted to different glazing. Methods and Materials: Fourteen standardized disc specimens (diameter: 5 mm, thickness: 1.5 mm) of each of two micro-particulate feldspathic ceramics (VM7 and VM13, Vita) were produced according to manufacturers' specifications for a total of 28 specimens (24 for the analysis of biofilm and 4 for topographic analysis analyzing the ceramic surfaces). Specimens from each type of ceramic were submitted to two different glazing methods composing four groups: VM7 glazed using glazing liquid Vita Akzent® 25 (G1) and glaze firing (G2), VM13 glazed using glazing liquid (G3) and glaze firing (G4). Six individuals (n=6) wore oral appliances with four ceramic specimens, fixed on the buccal face of the appliances. After 8 hours, each sample was evaluated for the presence (1) or absence (0) of bacterial colonization under a scanning electron microscope (SEM) on five randomly selected fields. The value for each sample was cumulative of the results observed in the fields. One sample from each group was evaluated under a SEM to verify the topographic pattern. Results: There was no difference with regard to bacterial colonization between the feldspar-ceramics and between the glazing types (Kruskal-Wallis non-parametric test). Conclusion: Feldspar-ceramics submitted to firing or glaze firing with Vita Akzent® 25 present a similar condition for in situ bacterial colonization. The similar topographic pattern of the ceramic surfaces seems to have influenced the bacterial colonization.

Análise rugosimétrica de duas cerâmicas odontológicas submetidas a diferentes tratamentos de superfície

Pós-graduação em Reabilitação Oral - FOAR

Efeito do sistema de acabamento e polimento na rugosidade superficial e formação in situ de biofilme dentário inicial em cerâmica feldspática micro-particulada

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito da escovação na formação in situ de biofilme dentário inicial e na rugosidade superficial em cerâmica de y-tzp após vitrificação e polimento

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência de união e discrepância marginal absoluta de infraestruturas feitas em cerâmica Y-TZP: influência de novos métodos de tratamento de superfície

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização mecânica de uma porcelana de aplicação convencional e uma prensada para recobrimento de infraestruturas de zircônia e o efeito do método de resfriamento na resistência à flexão biaxial do conjunto zircônia/porcelana

Pós-graduação em Reabilitação Oral - FOAR

Evaluation of Resin Bond Strength to Yttria-stabilized Tetragonal Zirconia and Framework Marginal Fit: Comparison of Different Surface Conditionings

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of tensile tetention of Y-TZP crowns after long-term aging: Effect of the core substrate and crown surface conditioning

This study evaluated the effect of the core substrate type (dentin and composite resin) on the retention of crowns made of yttrium oxide stabilized tetragonal zirconia polycrystal (Y-TZP), submitted to three inner surface conditionings. For this purpose, 72 freshly extracted molars were embedded in acrylic resin, perpendicular to the long axis, and prepared for full crowns: 36 specimens had crown preparations in dentin; the remaining 36 teeth had the crowns removed, and crown preparations were reconstructed with composite resin plus fiber posts with dimensions identical to the prepared dentin. The preparations were impressed using addition silicone, and 72 Y-TZP copings for the tensile test were produced. Cementation was performed with a dual-cured cement containing phosphate monomers. For cementation, the crown preparation (dentin or resin) was conditioned with the adhesive system, and the ceramic was subjected to one of three surface treatments: isopropyl alcohol, tribochemical silica coating, or thin low-fusing glassy porcelain layer application plus silanization. After 24 hours, all specimens were submitted to thermocycling (6000 cycles) and placed in a special tensile testing device in a universal testing machine to determine failure loads. The failure modes of all samples were analyzed under a stereomicroscope. Two-way analysis of variance showed that the surface treatment and substrate type (alpha=0.05) affected the tensile retention results. The dentin substrate presented the highest tensile retention values, regardless of the surface treatment. When the substrate was resin, the tribochemical silica coating and low-fusing glaze application plus silanization groups showed the higher retention values.

Resistência de união de cimentos resinosos em superfície de cerâmica de Y-TZP após aplicação de filme vitrocerâmico

Pós-graduação em Odontologia Restauradora - ICT

Influência de três tratamentos de superfície para cerâmicas a base de zircônia na resistência adesiva e no comportamento à fadiga do material

Pós-graduação em Odontologia Restauradora - ICT