Glass foam of macroporosity using glass waste and sodium hydroxide as the foaming agent

Glass foams using float glass waste and sodium hydroxide were produced. The influence of the sodium hydroxide amount in the foam formulation was studied. Titanium dioxide was used as a strengthening agent. The variations of temperature, heating rate and sintering time were investigated during the synthesis process. Open porosity was estimated using mercury porosimetry. The morphology of the glass foams was evaluated using scanning electron microscopy, phase formation was studied using X-ray diffraction, and chemical composition was estimated using X-ray fluorescence. As a result, glass foams with macroporosity were obtained. Since the glass foams used glass waste as reactant, the results suggest the development of an alternative route for glass recycling. © 2012 Elsevier Ltd and Techna Group S.r.l.

Recycling of glass cullet as aggregate for clays used to produce roof tiles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Crystallization of SiO2-CaO-Na2O Glass Using Sugarcane Bagasse Ash as Silica Source

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Construction and demolition waste as a source of PVC for recycling

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nutrient recycling and physical indicators of an alley cropping system in a sandy loam soil in the pre-Amazon region of Brazil

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Use of glass transition temperature for stabilization of board's cracks of Eucalyptus grandis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Understanding the Crystallization Mechanism of a Wollastonite Base Glass Using Isoconversional, IKP Methods and Master Plots

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Continuous ethanol production in a nonconventional five-stage system operating with yeast cell recycling at elevated temperatures

Three ranges of increasing temperatures (35-43, 37-45, 39-47degreesC) were sequentially applied to a five-stage system continuously operated with cell recycling so that differences of 2degreesC (between one reactor to the next) and 8degreesC (between the first reactor at the highest temperature and the fifth at the lowest temperature) were kept among the reactors for each temperature range. The entire system was fed through the first reactor. The lowest values of biomass and viability were obtained for reactor R-3 located in the middle of the system. The highest yield of biomass was obtained in the effluent when the system was operated at 35-43degreesC. This nonconventional system was set up to simulate the local fluctuations in temperature and nutrient concentrations that occur in different regions of the medium in an industrial bioreactor for fuel ethanol production mainly in tropical climates. Minimized cell death and continuous sugar utilization were observed at temperatures normally considered too high for Saccharomyces cerevisiae fermentations.

Crystallization study of the (1-x)Sb2O3-(x)SbPO4 glass system

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Tunable visible photoluminescence of powdered silica glass

intense photoluminescence in the visible region was observed at room temperature in standard soda-lime-silica glass powder, mechanically milled in a high-energy attrition mill. The emission band maximum shows an interesting dependence on the exciting wavelength, suggesting the possibility to tune the PL emission. These findings indicate that the photoluminescence may be directly related to unsatisfied chemical bonds correlated with the high surface area. The Raman scattering and ultraviolet-visible optical reflectance measurements corroborate this assertion. Transmission electron microscopy measurements indicate that samples milled more than 10 h present the formation of nanocrystallites with about 10-20 nm. (C) 2007 Elsevier B.V. All rights reserved.

PET containers in Brazil: Opportunities and challenges of a logistics model for post-consumer waste recycling

The use of post-consumer materials is directly related to reducing the cost of production and extraction of natural resources. Non-recyclable materials are randomly disposed in the environment. Brazil is one of the largest consumers of PET (polyethylene terephthalate) bottles. The purpose of this paper is to describe the opportunities and challenges of the logistics model for post-consumer PET bottle recycling in Brazil, while providing knowledge of its practices along the recycling chain. The results describe the need to educate those directly and indirectly involved in the process: to reduce consumption in order to reduce the amount of waste generated: to structure the post-consumer reverse chain and engage industrial sectors and government, through public policies, to support cleaner technologies along the PET bottle production chain. (C) 2010 Elsevier B.V. All rights reserved.

Processing and hygrothermal effects on viscoelastic behavior of glass fiber/epoxy composites

Fiber reinforced epoxy composites are used in a wide variety of applications in the aerospace field. These materials have high specific moduli, high specific strength and their properties can be tailored to application requirements. In order to screening optimum materials behavior, the effects of external environments on the mechanical properties during usage must be clearly understood. The environmental action, such as high moisture concentration, high temperatures, corrosive fluids or ultraviolet radiation (UV), can affect the performance of advanced composites during service. These factors can limit the applications of composites by deteriorating the mechanical properties over a period of time. Properties determination is attributed to the chemical and/or physical damages caused in the polymer matrix, loss of adhesion of fiber/resin interface, and/or reduction of fiber strength and stiffness. The dynamic elastic properties are important characteristics of glass fiber reinforced composites (GRFC). They control the damping behavior of composite structures and are also an ideal tool for monitoring the development of GFRC's mechanical properties during their processing or service. One of the most used tests is the vibration damping. In this work, the measurement consisted of recording the vibration decay of a rectangular plate excited by a controlled mechanism to identify the elastic and damping properties of the material under test. The frequency amplitude were measured by accelerometers and calculated by using a digital method. The present studies have been performed to explore relations between the dynamic mechanical properties, damping test and the influence of high moisture concentration of glass fiber reinforced composites (plain weave). The results show that the E' decreased with the increase in the exposed time for glass fiber/epoxy composites specimens exposed at 80 degrees C and 90% RH. The E' values found were: 26.7, 26.7, 25.4, 24.7 and 24.7 GPa for 0, 15, 30, 45 and 60 days of exposure, respectively. (c) 2005 Springer Science + Business Media, Inc.

Hygrothermal effects on damping behavior of metal/glass fiber/epoxy hybrid composites

Continuous fiber/metal laminates (FML) offer significant improvements over current available materials for aircraft structures due to their excellent fatigue endurance and low density. Glass fibers/epoxy laminae and aluminum foil (Glare) are commonly used to obtain these hybrid composites. The environmental factors can limit the applications of composites by deteriorating the mechanical properties during service. Usually, epoxy resins absorb moisture when exposed to humid environments and metals are prone to surface corrosion. Therefore, the combination of the two materials in Glare (polymeric composite and metal). can lead to differences that often turn out to be beneficial in terms of mechanical properties and resistance to environmental influences. In this work. The viscoelastic properties. such as storage modulus (E') and loss modulus (E'), were obtained for glass fiber/epoxy composite, aluminum 2024-T3 alloy and for a glass fiber/epoxy/aluminum laminate (Glare). It was found that the glass fiber/epoxy (G/E) composites decrease the E' modulus during hygrothermal conditioning up to saturation point (6 weeks). However, for Glare laminates the E' modulus remains unchanged (49GPa) during the cycle of hygrothermal conditioning. The outer aluminum sheets in the Glare laminate shield the G/E composite laminae from moisture absorption. which in turn prevent, in a certain extent, the material from hygrothermal degradation effects. (c) 2005 Elsevier B.V. All rights reserved.

Influência da temperatura no desempenho mecânico de compósitos PEI/fibras de vidro

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Determination of Population Size of Glass-like Carbon Sampling Used in Weibull Analysis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)