Structural characterization of undoped and Sb-doped SnO2 thin films fired at different temperatures

SnO2 thin films were obtained by the sol-gel method starting from inorganic precursor solutions. In this work, we compare the structure of undoped and Sb-doped SnO2 films prepared by dip-coating. The films were deposited on quartz substrates and then fired at different temperatures ranging from 383 up to 1173 K. The density and the thickness of the films were determined by X-ray reflectivity (XRR) and their porous nanostructure was characterized by grazing-incidence small angle X-ray scattering (GISAXS). XRR results corresponding to undoped and Sb-doped samples indicate a monotonous decrease in film thickness when they are fired at increasing temperatures. At same time, the apparent density of undoped samples exhibits a progressive increase while for Sb-doped films it remains invariant up to 973 K and then increases for T = 1173 K. Anisotropic GISAXS patterns of both films, Sb-doped and undoped, fired above 573 K indicate the presence of elongated pores with their major axis perpendicular to the film surface. For all firing temperatures the nanopores in doped samples are larger than in undoped ones. This suggests that Sb-doping favours the pore growth hindering the film densification. At the highest firing temperature (1173 K) this effect is reversed.

Study on the initial stages of water corrosion of fluorozirconate glasses

The surface corrosion process associated with the hydrolysis of fluorozirconate glass, ZBLAN (53ZrF(4), 20BaF(2), 20NaF, 4LaF(2), 3AlF(3)) was investigated using X-ray photoelectron spectroscopy (XPS), grazing-incidence small angle X-ray scattering (GISAXS), X-ray reflectivity (XRR) and scanning electron microscopy (SEM). After a short exposure period (25 min) of the glass surface to deionized water the XPS data indicate an increase of the oxygen content accompanied by a decrease of fluorine concentration. The analysis of the chemical bonding structure identified the predominant surface reaction products as zirconium hydroxyfluoride and oxyfluoride species. The second most abundant glass component, bariumfluoride, remains almost unaffected by oxygen, while sodium fluoride is completely removed from the attacked surface region. The detected structural and compositional changes are related to the selective dissolution of the glass components leading to the formation of a new surface phase. This process is accompanied by a visible surface roughening caused by reprecipitated species, observed by SEM. The modification of the glass surface is responsible for an increase of the GISAXS intensity. The scattering was attributed to nanovoids formed at the surface region of the glass with an average size of 2.4 +/- 0.05 nm. (C) 2004 Elsevier B.V. All rights reserved.

Nanostructure and properties of ZnO films produced by the pyrosol process

Indium doped ZnO films were deposited by the pyrosol process on glass substrates at different temperatures from solutions containing In/Zn molar ratios up to 10%. The nanostructure of the films was investigated using grazing-incidence small angle X-ray scattering (GISAXS). The mass density was determined by X-ray reflectivity and the composition by X-ray photoelectron spectroscopy. The GISAXS measurements revealed an anisotropic pattern for films deposited at 573 and 623 K and a isotropic one for those deposited at higher temperatures. The anisotropic patterns indicate the presence of elongated nanopores with their long axes perpendicular to the film surface. In contrast, the isotropic nature of GISAXS patterns of films grown at high temperatures (673 and 723 K) suggests the presence of spherical voids. The pore size distribution function determined from the isotropic patterns indicates a multimodal size distribution. on the other hand, the measured mass density of the doped films with isotropic nanotexture is higher than that of the anisotropic films while the electric resistivity is significantly lower. This is in agreement with the detected strong reduction of the void density and specific surface area at approximately constant pore size.