Ferroelectric and dielectric properties of Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 thin films grown by the soft chemical method

Polycrystalline Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 (BST:Sn) thin films with a perovskite structure were prepared by the soft chemical method on a platinum-coated silicon substrate from spin-coating technique. The resulting thin films showed a dense structure with uniform grain size distribution. The dielectric constant of the films estimated from C-V curve is around 1134 and can be ascribed to a reduction in the oxygen vacancy concentration. The ferroelectric nature of the film indicated by butterfly-shaped C-V curves and confirmed by the hysteresis curve, showed remnant polarization of 14 mu C/cm(2) and coercive field of 74 kV/cm at frequency of 1 MHz. At the same frequency, the leakage current density at 1.0 V is equal to 1.5 x 10(-7) A/cm(2). This work clearly reveals the highly promising potential of BST:Sn for application in memory devices. (c) 2006 Elsevier B.V. All rights reserved.

Ferroelectric and dielectric behaviour of Bi0.92La0.08FeO3 multiferroic thin films prepared by soft chemistry route

Bi0.92La0.08FeO3 (BLFO) thin films were grown on platine substrates by the soft chemical route. Ferroelectric and dielectric behaviors of BLFO films deposited by spin-coating technique and annealed at 773 K for 2 h in air atmosphere were explained. BLFO thin films obtained presents a rhombohedral structure. The BLFO films present dielectric and ferroelectric behaviors with dielectric permittivity and dielectric loss of approximately 81 and 0.0144 at 1 kHz. The Au/BLFO/Pt capacitor shows a hysteresis loop with remnant polarization of 20.6 mu C/cm(2) and coercive field of 53.88 kV/cm. The polarization switching and the fatigue behavior of the BLFO films were significantly enhanced.

Ferroelectric and dielectric properties of vanadium-doped Ba(Ti0.90Zr0.10)O-3 ceramics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of strains and defects on ferroelectric and dielectric properties of thin-film barium-strontium titanates

Pristine, W and Mn 1% doped Ba(0.6)Sr(0.4)TiO(3) epitaxial thin films grown on the LaAlO(3) substrate were deposited by pulsed laser deposition (PLD). Dielectric and ferroelectric properties were determined by the capacitance measurements and X-ray diffraction was used to determine both residual elastic strains and defect-related inhomogeneous strains-by analyzing diffraction line shifts and line broadening, respectively. We found that both elastic and inhomogeneous strains are affected by doping. This strain correlates with the change in Curie-Weiss temperature and can qualitatively explain changes in dielectric loss. To explain the experimental findings, we model the dielectric and ferroelectric properties of interest in the framework of the Landau-Ginzburg-Devonshire thermodynamic theory. As expected, an, elastic-strain contribution due to the epilayer-substrate misfit has an important influence on the free-energy. However, additional terms that correspond to the defect-related inhomogeneous strain had to be introduced to fully explain the measurements.

Ferroelectric and dielectric properties of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration of 0.75 was grown on Pt/Ti/SiO2/Si substrates by using the polymeric precursor solution and spin-coating method. The scanning electron microscopy (SEM) showed rounded grains, which is not typical for these system. The BLT films showed well-saturated polarization-electric field curve which 2P(r) = 41.4 muC/cm(2) and V-c = 0.99 V. The capacitance dependence on the voltage is strongly nonlinear, confirming the ferroelectric properties of the film resulting from the domains switching. These properties make BLT a promising material for FERAM applications.

Ferroelectric and dielectric characteristics of Bi3.25La0.75Ti3O12 thin films prepared by the polymeric precursor method

The ferroelectric properties and leakage current mechanisms of preferred oriented Bi3.25La0.75 Ti3O12 (BLT) thin films deposited on La0.5Sr0.5CoO3 (LSCO) by the polymeric precursor method were investigated. Atomic force microscopy indicates that the deposited films exhibit a dense microstructure with a rather smooth surface morphology. The improved ferroelectric and leakage current characteristics can be ascribed to the plate-like grains of the BLT films. © 2006 Trans Tech Publications, Switzerland.

Ferroelectric switching and dielectric response of P(VDF-TrFE)/PMMA blends

The ferroelectric and the dielectric behaviors of binary blends formed by an equi-molar Poly(vinylidene fluoride trifluoroethylene) copolymer [P(VDF-TrFE)] and Poly(methyl methacrylate) [PMMA] were investigated, for several PMMA compositions. For 40 wt.% or more PMMA contents, the blends are completely amorphous. Below this value, they crystallize in the usual Cm2m polar structure of P(VDF-TrFE). The ferroelectric switching characteristics and the dielectric response of the blends demonstrate the formation of dynamically stable ferroelectric domains. Moreover, the blended films are highly transparent in the optical region. Therefore, thin films of these binary blends are good candidates as host materials for nonlinear optical applications.

Structural, dielectric, ferroelectric and optical properties of PBCT, PBST and PCST complex thin films on LaNiO3 metallic conductive oxide layer coated Si substrates by the CSD technique

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis, optical and ferroelectric properties of PZT thin films: experimental and theoretical investigation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Phase transition and dielectric properties of La-doped Pb(Zr, Ti)O-3 antiferroelectric ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and dielectric characterization of praseodymium-modified lead titanate ceramics synthesized by the OPM route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Ferroelectric and microstructural characteristics of SrBi2Ta2O9 thin films crystallized by the rapid thermal annealing process

Ferroelectric SrBi2Ta2O9 thin films on Pt/Ti/SiO2/Si were successfully synthesized by the modified polymeric precursor method. The films were deposited by spin coating and crystallized by rapid thermal annealing in a halogen lamp furnace, followed by postannealing at temperatures ranging from 700 degreesC to 800 degreesC in an oxygen atmosphere. Microstructural and phase evaluations were followed by x-ray diffraction and atomic force microscopy. The films displayed spherical grain structures with a superficial roughness of approximately 3-6 nm. The dielectric constant values were 121 and 248 for films treated at 700 degreesC and 800 degreesC, respectively. The P-E curve showed a voltage shift toward the positive side, which was attributed to crystallization under the halogen illumination. The remanent polarization (2P(r)) and coercive field (E-c) were 7.1 muC/cm(2) and 113 kV/cm, and 18.8 muC/cm(2) and 93 kV/cm for the films treated at 700 degreesC and 800 degreesC, respectively. (C) 2001 American Institute of Physics.

Preparation and properties of ferroelectric Pb1-xCaxTiO3 thin films produced by the polymeric precursor method

Pb1- xCaxTiO3 thin films with x = 0.24 composition were prepared by the polymeric precursor method on Pt/Ti/SiO2/Si substrates. The surface morphology and crystal structure, and the ferroelectric and dielectric properties of the films were investigated. X-ray diffraction patterns of the films revealed their polycrystalline nature. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) analyses showed the surface of these thin films to be smooth, dense and crack-free with low surface roughness. The multilayer Pb1-xCaxTO3 thin films were granular in structure with a grain size of approximately 60-70 nm. The dielectric constant and dissipation factor were, respectively, 174 and 0.04 at a 1 kHz frequency. The 600-nm thick film showed a current density leakage in the order of 10(-7) A/cm(2) in an electric field of about 51 kV/cm. The C-V characteristics of perovskite thin films showed normal ferroelectric behavior. The remanent polarization and coercive field for the deposited films were 15 muC/cm(2) and 150 kV/cm, respectively. (C) 2001 Kluwer Academic Publishers.

Ferroelectric and optical properties of Ba0.8Sr0.2TiO3 thin film

Barium strontium titanate (Ba0.8Sr0.2TiO3) thin films have been prepared on Pt/Ti/SiO2/Si substrates using a soft solution processing. X-ray diffraction and also micro-Raman spectroscopy showed that the Ba0.8Sr0.2TiO3 thin films exhibited a tetragonal structure at room temperature. The presence of Raman active modes was clearly shown at the 299 and 725 cm(-1) peaks. The tetragonal-to-cubic phase transition in the Ba0.8Sr0.2TiO3 thin films is broadened, and suppressed at about 35 degreesC, with a maximum dielectric constant of 948 (100 kHz). Electrical measurements for the prepared Ba0.8Sr0.2TiO3 thin films showed a remnant polarization (P-r) of 6.5 muC/cm(2), a coercive field (E-c) of 41 kV/cm, and good insulating properties. The dispersion of the refractive index is interpreted in terms of a single electronic oscillator at 6.97 eV. The direct band gap energy (E-g) and the refractive index (n) are estimated to be 3.3 eV and n = 2.27-2.10, respectively. (C) 2002 American Institute of Physics.

A Raman and dielectric study of a diffuse phase transition in (Pb1-xCax)TiO3 thin films

Dielectric and Raman scattering experiments were performed on polycrystalline Pb1-xCaxTiO3 thin films (x=0.10, 0.20, 0.30, and 0.40) as a function of temperature. The results showed no shift in the dielectric constant (K) maxima, a broadening with frequency, and a linear dependence of the transition temperature on increasing Ca2+ content. on the other hand, a diffuse-type phase transition was observed upon transforming from the cubic paraelectric to the tetragonal ferroelectric phase in all thin films. The temperature dependence of Raman scattering spectra was investigated through the ferroelectric phase transition. The temperature dependence of the phonon frequencies was used to characterize the phase transitions. Raman modes persisted above the tetragonal to cubic phase transition temperature, although all optical modes should be Raman inactive. The origin of these modes was interpreted in terms of a breakdown of the local cubic symmetry due to chemical disorder. The lack of a well-defined transition temperature and the presence of broad bands in some temperature interval above the FE-PE phase transition temperature suggested a diffuse-type phase transition. This result corroborates the dielectric constant versus temperature data, which showed a broad ferroelectric phase transition in these thin films.