THE EFFECT of IMMEDIATE DENTIN SEALING on THE MARGINAL ADAPTATION and BOND STRENGTHS of TOTAL-ETCH and SELF-ETCH ADHESIVES

Statement of problem. Sealing ability and bond strengths of total-etch and self-etch dentin adhesives used for immediate dentin sealing have not been assessed and established.Purpose. The purpose of this study was to determine the effectiveness of immediate dentin sealing (IDS) using total-etch or self-etch dentin adhesives on microleakage and microtensile bond strength.Material and methods. Twenty recently extracted molars were selected, and standard MOD inlay preparations were made with the gingival margins located below the cemento-enamel unction. The teeth were assigned to 4 experimental groups (n=5) according to the indirect composite restoration cementation technique used: (1) immediate dentin sealing with Adper Single Bond (TEBI); (2) conventional adhesive cementation technique using Adper Single Bond (TEAI); (3) immediate dentin sealing using Adper Prompt L-Pop (SEBI); or (4) conventional adhesive cementation technique using Adper Prompt L-Pop (SEAI). The restored teeth were thermal cycled 1,000 times between 5 degrees and 55 degrees C and then immersed in 50% ammoniacal silver nitrate. Three specimens per restoration were evaluated for microleakage, according to predefined scores, and submitted to Friedman's test (alpha-.05). The specimens were then sectioned to obtain 0.8 +/- 0.2-mm-thick sticks (with n ranging from 32 to 57 specimens) and submitted to microtensile bond strength (mu TBS) testing. The obtained data were submitted to 2-way ANOVA test (alpha=.05).Results. None of the experimental groups demonstrated complete elimination of marginal microleakage. There were significant differences in microleakage of the tested adhesives (P>.001). IDS microleakage scores were similar to those obtained using the conventional cementation technique (CCT) for both adhesives. The highest mean bond strengths were obtained with TEBI (51.1 MPa), whereas SEAI showed the lowest mean bond strengths (1.7 MPa). IDS resulted in significantly higher bond strengths than CCT (P<.001).Conclusions. Total-etch and self-etch adhesives have a significant effect on IDS. IDS resulted in high bond strengths for both adhesives; however, the microleakage was similar to that obtained with CCT (J Prosthet Dent 2009;102:1-9)

One-year clinical performance of self-etch adhesives in posterior restorations

Purpose: To evaluate the 1-year clinical performance of three self-etching adhesives (Adper Prompt L-Pop, Clearfil S-3 Bond, iBond) in posterior composite restorations using one etch&rinse adhesive (One-Step Plus) as control. Methods: Upon approval by the Institutional Review Board, 121 restorations were inserted in 38 subjects. The adhesives were applied as per manufacturers' instructions. Preparations were restored with a nanofilled resin composite (Filtek Supreme) and evaluated at baseline, 6 months, and 1 year. Statistical analyses included the Chi-square distribution with the McNemar non-parametric test (P< 0.05). Results: At 1 year, 111 restorations in 35 subjects were evaluated using the USPHS modified criteria. No significant changes were observed for the etch&rinse adhesive One-Step Plus. At 1 year the number of Alfa ratings decreased significantly for Clearfil S-3 Bond and for iBond in the categories color match, marginal staining, and marginal adaptation. For Adper Prompt L-Pop, marginal adaptation at 1 year was significantly worse than at baseline. Postoperative sensitivity to air improved significantly for Adper Prompt L-Pop, Clearfil S-3 Bond, and iBond. When the evaluation criteria were paired at 1 year, iBond resulted in a significantly lower number of Alfa ratings than any of the other adhesives for color match, marginal staining, and marginal adaptation. One-Step Plus resulted in a greater number of Alfa ratings for marginal adaptation than either Adper Prompt L-Pop or Clearfil S-3 Bond. Marginal adaptation was significantly better for Clearfil S-3 Bond than for Adper Prompt L-Pop. The post-operative sensitivity measured at 1 year for Adper Prompt L-Pop was statistically better than that for One-Step Plus.

Interaction between total-etch and self-etch adhesives and conventional and self-adhesive resin cements

The aim of this study was to compare the bond strength to enamel between resin cements combined with total-etch and self-etch adhesive systems and a self-adhesive cement. Eighty bovine incisors had their buccal surface ground flat exposing a plane area in the enamel. Eighty Artglass resin cylinders measuring 3 mm in diameter and 4 mm in height were fabricated. The teeth were divided into eight groups of 10 teeth each and the resin cylinders were cemented with different adhesive systems and resin cements; G1: RelyX Unicem (self-adhesive cement); G2: H 3PO 4 + Single Bond + RelyX ARC; G3: AdheSE + Variolink II; G4: H 3PO 4 + Excite + Variolink II; G5: Xeno III + Enforce; G6: H 3PO 4 + Prime&Bond NT + Enforce; G7: Biatite Primers 1 and 2 + Bistite II DC; G8: H 3PO 4 + Bistite Primers 1 and 2 + Bistite II DC. After application of the adhesives, the cylinders were cemented according to manufacturer instructions. The specimens were submitted to 2000 thermal cycles at a temperature ranging from 5±5°C to 55±5°C, and shear bond strength was then tested at a variety of 1 mm/min. The data were analyzed by ANOVA and the Tukey's test (á=5%), obtaining a p value of 0.00. The following mean (±standard deviation) bond strength values were observed for each group: G1: 5.14(±0.99)a; G3: 16.23(±4.69)b; G7: 17.82(±3.66)b; G5: 18.48(±2.88)bc; G8: 20.15(±4.12)bc; G4: 22.85(±3.08)cd; G2: 24.96(±2.89)d; G6: 26.07(±1.69)d. Groups followed by the same letters did not differ significantly. For most of the resin cements tested, the application of adhesive systems using acid etching resulted in a higher bond strength when compared to the self-etch adhesive systems and to the self-adhesive cement.

Using the self-etch adhesives in anterior restoration

With the arrival of self-etch adhesives systems, there has been a rise in interest among clinicians, making it imperative for health professionals to have knowledge of the properties, characteristics, the association as well as the dental structures of these materials, in order to select them and use them correctly. The self-etch adhesive systems show good values of bond strength, microleakage and performance, and have therefore become an option in direct adhesive restorations. In the regard, this case study aims to describe the technique involving the use of selfetch adhesives system for direct restoration of anterior teeth.

Etch and rinse versus self-etching adhesives systems: Tridimensional micromechanical analysis of dentin/adhesive interface

The purpose of this study was to evaluate stress distribution in the hybrid layer produced by two adhesive systems using three-dimensional finite element analysis (FEA). Four FEA models (M) were developed: Mc, a representation of a dentin specimen (41 x 41 x 82 mu m) restored with composite resin, exhibiting the adhesive layer, hybrid layer (HL), resin tags, peritubular dentin, and intertubular dentin to simulate the etch-and-rinse adhesive system; Mr, similar to Mc, with lateral branches of the adhesive; Ma, similar to Mc, however without resin tags and obliterated tubule orifice, to simulate the environment for the self-etching adhesive system; Mat, similar to Ma, with tags. A numerical simulation was performed to obtain the maximum principal stress (sigma(max)). The highest sigma(max) in the HL was observed for the etch-and-rinse adhesive system. The lateral branches increased the sigma(max) in the HL. The resin tags had a little influence on stress distribution with the self-etching system. (C) 2012 Elsevier Ltd. All rights reserved.

Response of human pulps capped with different self-etch adhesive systems

The aim of this study was to evaluate the response of human pulps capped with a calcium hydroxide hard-setting cement or with two-step self-etch adhesive systems. Pulp exposures were performed on the occlusal floor, and the bleeding control was performed with saline solution. The exposed pulp tissue was capped with Clearfil LB 2V (2V) or Clearfil SE Bond (SE) and restored with a composite resin. In control group, the pulpal wound was capped with Ca(OH)(2) cement and restored with Clearfil LB 2V or Clearfil SE Bond + composite resin. After 30 and 90 days, the teeth were extracted, processed for hematoxylin and eosin, and categorized in a histological score system. The pulpal response was worse for groups capped with the self-etch adhesive systems (2V and SE) in both periods of evaluation, when compared to their respective control groups at 90 days (p < 0.05). For both self-etch systems evaluated, the pulp tissue exhibited moderate to severe inflammatory cell infiltrate involving the coronal pulp with chronic abscesses. Dentin bridging was observed in a few specimens. For the calcium hydroxide groups, almost all specimens showed dentin bridge formation, with few scattered inflammatory cells and normal tissue below the pulp exposure site. Calcium hydroxide should be used as the material of choice for pulp capping, and the use of two-step self-etch adhesives for human pulp capping is contraindicated.

Avaliação da resistência de união entre dentina preparada por laser e um sistema adesivo a base de silorano, variando a técnica de aplicação e umidade do substrato

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Sistemas adesivos autocondicionantes: estudo micromecânico da interface de união através do método dos elementos finitos tridimensional

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estudo da resistência de união ao cisalhamento de sistemas adesivos: influência de diferentes substratos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of Nd:YAG Laser on the Bond Strength of Self-etching and Conventional Adhesive Systems to Dental Hard Tissues

Purpose: The aim of this study was to investigate the influence of Nd:YAG laser on the shear bond strength to enamel and dentin of total and self-etch adhesives when the laser was applied over the adhesives, before they were photopolymerized, in an attempt to create a new bonding layer by dentin-adhesive melting.Material and Methods: One-hundred twenty bovine incisors were ground to obtain flat surfaces. Specimens were divided into two substrate groups (n=60): substrate E (enamel) and substrate D (dentin). Each substrate group was subdivided into four groups (n=15), according to the surface treatment accomplished: X (Xeno III self-etching adhesive, control), XL (Xeno III + laser Nd:YAG irradiation at 140 mJ/10 Hz for 60 seconds + photopolymerization, experimental), S (acid etching + Single Bond conventional adhesive, Control), and SL (acid etching + Single Bond + laser Nd:YAG at 140 mJ/10 Hz for 60 seconds + photopolymerization, experimental). The bonding area was delimited with 3-mm-diameter adhesive tape for the bonding procedures. Cylinders of composite were fabricated on the bonding area using a Teflon matrix. The teeth were stored in water at 37 degrees C/48 h and submitted to shear testing at a crosshead speed of 0.5 mm/min in a universal testing machine. Results were analyzed with three-way analysis of variance (ANOVA; substrate, adhesive, and treatment) and Tukey tests (alpha=0.05). ANOVA revealed significant differences for the substrate, adhesive system, and type of treatment: lased or unlased (p<0.05). The mean shear bond strength values (MPa) for the enamel groups were X=20.2 +/- 5.61, XL=23.6 +/- 4.92, S=20.8 +/- 4.55, SL=22.1 +/- 5.14 and for the dentin groups were X=14.1 +/- 7.51, XL=22.2 +/- 6.45, S=11.2 +/- 5.77, SL=15.9 +/- 3.61. For dentin, Xeno III self-etch adhesive showed significantly higher shear bond strength compared with Single Bond total-etch adhesive; Nd:YAG laser irradiation showed significantly higher shear bond strength compared with control (unlased).Conclusion: Nd:YAG laser application prior to photopolymerization of adhesive systems significantly increased the bond strength to dentin.

Estudo comparativo in vitro da resistência ao cisalhamento de sistemas adesivos em dentina humana: uso de hipoclorito de sódio em sistemas convencionais ou primers acidificados

Pós-graduação em Odontologia Restauradora - ICT

Effect of time between adhesive application and photoactivation on adhesion and collagen exposure

Fundacao de Amparo a Pesquisa do Estado de sao Paulo (FAPESP)

The effect of dimethyl sulfoxide (DMSO) on dentin bonding and nanoleakage of etch-and-rinse adhesives

Objective The objective was to examine the effect of a solvent dimethyl sulfoxide (DMSO) on resin-dentin bond durability, as well as potential functional mechanisms behind the effect. Methods Microtensile bond strength (μTBS) was evaluated in extracted human teeth in two separate experiments. Dentin specimens were acid-etched and assigned to pre-treatment with 0.5 mM (0.004%) DMSO as additional primer for 30 s and to controls with water pre-treatment. Two-step etch-and-rinse adhesive (Scotchbond 1XT, 3M ESPE) was applied and resin composite build-ups were created. Specimens were immediately tested for μTBS or stored in artificial saliva for 6 and 12 months prior to testing. Additional immediate and 6-month specimens were examined for interfacial nanoleakage analysis under SEM. Matrix metalloproteinase (MMP) inhibition by DMSO was examined with gelatin zymography. Demineralized dentin disks were incubated in 100% DMSO to observe the optical clearing effect. Results The use of 0.5 mM DMSO had no effect on immediate bond strength or nanoleakage. In controls, μTBS decreased significantly after storage, but increased significantly in DMSO-treated group. The control group had significantly lower μTBS than DMSO-group after 6 and 12 months. DMSO also eliminated the increase in nanoleakage seen in controls. 5% and higher DMSO concentrations significantly inhibited the gelatinases. DMSO induced optical clearing effect demonstrating collagen dissociation. Significance DMSO as a solvent may be useful in improving the preservation of long-term dentin-adhesive bond strength. The effect may relate to dentinal enzyme inhibition or improved wetting of collagen by adhesives. The collagen dissociation required much higher DMSO concentrations than the 0.5 mM DMSO used for bonding. © 2013 Academy of Dental Materials.

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS).Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM).Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM.Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.