Orientation dependence of stored energy of cold work in semi-processed electrical steels after temper rolling

Microhardness measurements were carried out in a low carbon lamination steel after 6% of temper rolling, in order to evaluate local variations of work hardening as a function of crystallographic orientation. EBSD (electron back scattered diffraction) was used to determine grain orientations with respect to individual rolling planes and rolling directions. Hardness was shown to increase with the local Taylor factor. TEM observations and a well-known dislocation hardening model were used to confirm the equivalence between hardness values and the stored energy of cold work. A definite correlation between stored energy and Taylor factors could therefore be established, being more consistent than previous data reported in the literature. The improvement was thought to be related to the rather small plastic deformation, during which Taylor factors could be considered to remain constant. (c) 2006 Elsevier B.V. All rights reserved.

Microstructure evolution during warm deformation of low carbon steel with dispersed cementite

The microstructure evolution and mechanical behavior during large strain of a 0.16%C-Mn steel has been investigated by warm torsion tests. These experiments were carried out at 685°C at equivalent strain rate of 0.1 s . The initial microstructure composed of a martensite matrix with uniformly dispersed fine cementite particles was attained by quenching and tempering. The microstructure evolution during tempering and straining was performed through interrupted tests. As the material was reheated to testing temperature, well-defined cell structure was created and subgrains within lath martensite were observed by TEM; strong recovery took place, decreasing the dislocation density. After 1 hour at the test temperature and without straining, EBSD technique showed the formation of new grains. The flow stress curves measured had a peculiar shape: rapid work hardening to a hump, followed by an extensive flow-softening region. 65% of the boundaries observed in the sample strained to ε = 1.0 were high angle grain boundaries. After straining to ε = 5.0, average ferrite grain size close to 1.5 μm was found, suggesting that dynamic recrystallization took place. Also, two sets of cementite particles were observed: large particles aligned with straining direction and smaller particles more uniformly dispersed. The fragmentation or grain subdivision that occurred during reheating and tempering time was essential for the formation of ultrafine grained microstructure.

Interaction between recrystallization and strain-induced precipitation in a high Nb- and N-bearing austenitic stainless steel: influence of the interpass time

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)