Direct pulp capping with a self-etching adhesive system: Histopathologic evaluation in dogs' teeth

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Calcifications in a clear cell mucoepidermoid carcinoma: a case report with histological and immunohistochemical findings

The aim of this study was to report an unusual case of mucoepidermoid carcinoma (MEC) in a 39-year-old woman. The tumor showed a prominent population of clear and intermediate basal cells. Clear cells rarely predominate over other cell types. Such cases are called clear cell variant of MEC. The case also revealed a variable amount of calcified material in the tumor mass. Calcifications are rare in clear cell MEC. These structures were periodic acid- Schiff positive and diastase resistant, excluding glycogen origin. Immunohistochemistry was performed, and the epidermoid component was positive for cytokeratin (CK) 7, CK13, CK14, and CK19. The mucous and clear cells presented mild staining for CK7. Cytokeratins 7, 13, and 19 stained luminal cells, and intermediate cells exhibited positivity for CK7, CK14, and vimentin. The origin of the calcifications is speculated to be the result of dystrophic calcification of the amorphous eosinophilic material secreted by intermediate basal cells.

Análise do desempenho de um gerador elétrico de pequeno porte acionado a motor de combustão a quatro tempos

Pós-graduação em Engenharia Mecânica - FEG

Effect of ceramic etching protocols on resin bond strength to a feldspar ceramic

This study sought to evaluate the resin micro-tensile bond strength (MTBS) stability of a leucite-reinforced ceramic after different ceramic etching protocols. The microtensile test had 40 ceramic blocks (5x5x6 mm) assigned to five groups (n=8), in accordance with the following surface etching protocols: NE nonetched (control); 9HF: hydrofluoric (HF) acid etching (9% HF)+wash/dry; 4HF: 4%HF+wash/dry; 5HF: 5%HF+wash/dry; and 5HF+N: 5%HF+neutralizer+wash/dry+ultrasonic-cleaning. Etched ceramic surfaces were treated with a silane agent. Next, resin cement blocks were built on the prepared ceramic surface and stored for 24 hours in distilled water at 37 degrees C. The specimens were then sectioned to obtain microtensile beams (32/block), which were randomly assigned to the following conditions, nonaged (immediate test) and aged (water storage for 150 days plus 12,000 thermal cycles), before the microtensile test. Bond strength data were submitted to one-way analysis of variance and Tukey test (alpha=0.05). Additional ceramic samples were subjected to the different ceramic etching protocols and evaluated using a scanning electron microscope (n=2) and atomic force microscopy (n=2). Aging led to a statistically significant decrease in the MTBS for all groups, except the untreated one (NE). Among the groups submitted to the same aging conditions, the untreated (NE) revealed inferior MTBS values compared to the 9HF and 4HF groups. The 5HF and 5HF+N groups had intermediate mean values, being statistically similar to the higher values presented by the 9HF and 4HF groups and to the lower value associated with the NE group. The neutralization procedure did not enhance the ceramic/resin cement bond strength. HF acid etching is a crucial step in resin/ceramic bonding.