In vitro study of the Nd : YAG laser effect on human dental enamel: Optical and scanning electron microscope analysis

Objective: the Nd:YAG laser irradiation of dental enamel was evaluated in enamel demineralization experiments in a Streptococcus mutans culture media. Summary Background Data: Previous studies had shown that a continuous wave Nd:YAG laser at an energy of approximately 67 mJ may induce an increased acid resistance in human dental enamel when exposed to severe demineralization conditions. Methods: Enamel windows of 3 x 4 cm in the buccal surface were irradiated with a continuous wave Nd:YAG laser at a wavelength of 1,064 Ecm using energy densities of from 83.75 to 187.50 J/cm(2), Enamel windows of 3 x 4 cm on the lingual surface served as control (without the laser irradiation). The enamel windows were then exposed to a Streptococcus mutans culture media at a temperature of 37 degrees C for 15 and 21 days. The laser effects and demineralization were examined both by optical microscopy and scanning electron microscopy (SEM), Results: A comparison between the lased and the unlased windows of enamel showed fusion and recrystalization of the enamel and increased acid-resistance in all groups irradiated with the Nd:YAG laser, on the other hand, the 3 x 4 delimited enamel surfaces from the control group (not irradiated with the Nd:YAG laser) showed 100% deminerization, Conclusions: These findings are consistent with the finding that laser irradiation of dental results in significant reduction of the effective solubility of enamel mineral.

Surface dental enamel lead levels and antisocial behavior in Brazilian adolescents

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of fermented milk containing probiotic on dental enamel and biofilm: In situ study

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Bonding Efficacy of New Self-etching, Self-adhesive Dual-curing Resin Cements to Dental Enamel

Purpose: This study evaluated the efficacy of the union between two new self-etching self-adhesive resin cements and enamel using the microtensile bond strength test.Materials and Methods: Buccal enamel of 80 bovine teeth was submitted to finishing and polishing with metallographic paper to a refinement of #600, in order to obtain a 5-mm(2) flat area. Blocks (2 x 4 x 4 mm) of laboratory composite resin were cemented to enamel according to different protocols: (1) untreated enamel + RelyX Unicem cement (RX group); (2) untreated enamel + Bifix SE cement (BF group); (3) enamel acid etching and application of resin adhesive Single Bond + RelyX Unicem (RXA group); (4) enamel acid etching and application of resin adhesive Solobond M + Bifix SE (BFA group). After 7 days of storage in distillated water at 37 degrees C, the blocks were sectioned for obtaining microbar specimens with an adhesive area of 1 mm(2) (n = 120). Specimens were submitted to the microtensile bond strength test at a crosshead speed of 0.5 mm/min. The results (in MPa) were analyzed statistically by ANOVA and Tu key's test.Results: Enamel pre-treatment with phosphoric acid and resin adhesive (27.9 and 30.3 for RXA and BFA groups) significantly improved (p <= 0.05) the adhesion of both cements to enamel compared to the union achieved with as-polished enamel (9.9 and 6.0 for RX and BF).Conclusion: Enamel pre-treatment with acid etching and the application of resin adhesive significantly improved the bond efficacy of both luting agents compared to the union achieved with as-polished enamel.

Micro-Shear Bond Strength of Different Adhesives to Human Dental Enamel

The aim of this study was to evaluate the micro-shear bond strength of 5 adhesive systems to enamel, one single-bottle acid-etch adhesive (O), two self-etching primers (P) and two all-in-one self-etching adhesives (S). Method: Sixty premolar enamel surfaces (buccal or lingual) were ground flat with 400- and 600-grit SiC papers and randomly divided into 5 groups (n=12), according to the adhesive system.. SB2 - Single Bond 2 (O); CSE - Clearfil SE Bond (P); ADS - AdheSE (P); PLP - Adper Prompt L-Pop (S); XE3 - Xeno III (S). Tygon tubing (inner diameter of 0.8mm) restricted the bonding area to obtain the resin composite (Z250) cylinders. After storage in distilled water at 37 degrees C for 24h and thermocycling, micro-shear testing was performed (crosshead speed of 0.5mm/min). Data were submitted to one-way ANOVA and Tukey test (a=5%). Samples were also subjected to stereomicroscopic and SEM evaluations after micro-shear testing. Mean bond strength values (MPa +/- SD) and the results of Tukey test were: SB2: 36.36(+/- 3.34)a; ADS: 33.03(+/- 7.83)a; XE3: 32.76(+/- 5.61)a; CSE: 30.61(+/- 6.68)a; PLP: 22.17(+/- 6.05)b. Groups with the same letter were not statistically different. It can be concluded that no significant difference was there between SB2, ADS, XE3 and CSE, in spite of different etching patterns of these adhesives. Only PLP presented statistically lower bond strengths compared with others. J Clin Pediatr Dent 35(3): 301-304, 2011

Effect of iron on inhibition of acid demineralisation of bovine dental enamel in vitro

Objectives: Iron ions (Fe2+) have been shown to be cariostatic in many studies particularly by their ability to reduce bacterial metabolism. Nevertheless, the role of iron ions on dissolution of enamel is unexplored. The aim of the present study was therefore to investigate the protective effect of increasing concentrations (0-120 mmol/L) of Fe2+ on the dissolution of enamel.Design: Enamel powder was subjected to acetic acid made with increasing concentrations with respect to FeSO4 center dot 7H(2)O. In order to determine the amount of enamel dissolved, the phosphate released in the medium was analysed spectrophotometrically using the Fiske-Subarrow method. Data were tested using Kruskall-Wall and Dunn's tests (p < 0.05). The degree of protection was found to approach maximum at about 15 mmol/L Fe2+. Higher concentrations of Fe2+ did not have an extra effect on inhibition of dissolution of enamel powder. In the next step, the protective effect of 15 mmol/L Fe2+ against mineral dissolution of the bovine enamel was evaluated using a simple abiotic model system. Enamel blocks were exposed to a sequence of seven plastic vials, each containing 1 mL of 10 mmol/L acetic acid. The acid in vial 4 was made 15 mmol/L with respect to FeSO4 center dot 7H(2)O. The mineral dissolved during each challenge was thus determined by phosphate released as described above. Data were tested using two-way ANOVA (p < 0.05). Results: Lower demineralisation (around 45%) was found in vial 4 (with Fe) that continued stable until vial 7.Conclusions: Thus, our data suggest that Fe2+, can be effective on inhibition of dissolution of enamel and that this effect may be durable. (c) 2006 Elsevier Ltd. All rights reserved.

Estudo da penetração de agentes ácidos para o condicionamento do esmalte dental em cimentos à base de hidróxido de cálcio.

It was verified the penetration of phosphoric acid into 3 commercial calcium hydroxide-based cements (Life, Renew and Prisma VLC Dycal). The colorimetric method employed permitted the identidication of phosphorus amount in representative samples of 6 successive layers 0.1 mm thick of each material. The acid etching used were the commercial products Scotchbond Etching Gel--3M at 36.114% by weight and Solução Condicionadora--Johnson & Johnson at 36.054% by weight. The contact time was 60 seconds. The result showed that layers 0.1 mm tick for Life and Prisma VLC Dycal and 0.2 mm thick for Renew were able to block the penetration of phosphoric acid solution whereas layers 0.1 mm thick for the 3 cements were able to block the penetration of phosphoric acid gel.

Effects of Coffea arabica on Streptococcus mutans adherence to dental enamel and dentine

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of time in hardness test on artificially demineralized human dental enamel

A cross-sectional microhardness (CSMH) test was carried out in human dental enamel exposed to a demineralizing solution in order to evaluate two different times of indentation in sound tissue and artificially induced caries. Twenty caries-free extracted human molars had one of their smooth surfaces sectioned and the enamel surface was isolated with nail polish except for an area of 6 mm2. These specimens were submitted to artificially induced enamel caries on a lactate buffer containing 0.1 ppm fluoride (F) during 28 days. All specimens were bisected to create groups A and B in which CSMH test was performed employing a Knoop indenter with a 25g load for 5 or 10 s, respectively. Student's paired t-test (p<0.05) was used to determine statistically significant differences between group A and B in 7 depths. There were no significant differences between any of the analyzed depths. Since the present experiment showed no significant difference when comparing indentations made with a 25 g load during either 5 or 10 s in different depths, this method can be used with either one of the time intervals tested without compromising a CSMH test on artificially demineralized human enamel.

Scanning electron microscopic study of the in situ effect of salivary stimulation on erosion and abrasion in human and bovine enamel

This in situ study investigated, using scanning electron microscopy, the effect of stimulated saliva on the enamel surface of bovine and human substrates submitted to erosion followed by brushing abrasion immediately or after one hour. During 2 experimental 7-day crossover phases, 9 previously selected volunteers wore intraoral palatal devices, with 12 enamel specimens (6 human and 6 bovine). In the first phase, the volunteers immersed the device for 5 minutes in 150 ml of a cola drink, 4 times a day (8h00, 12h00, 16h00 and 20h00). Immediately after the immersions, no treatment was performed in 4 specimens (ERO), 4 other specimens were immediately brushed (0 min) using a fluoride dentifrice and the device was replaced into the mouth. After 60 min, the other 4 specimens were brushed. In the second phase, the procedures were repeated but, after the immersions, the volunteers stimulated the salivary flow rate by chewing a sugar-free gum for 30 min. Enamel superficial alterations of all specimens were then evaluated using a scanning electron microscope. Enamel prism core dissolution was seen on the surfaces submitted to erosion, while on those submitted to erosion and to abrasion (both at 0 and 60 min) a more homogeneous enamel surface was observed, probably due to the removal of the altered superficial prism layer. For all the other variables - enamel substrate and salivary stimulation the microscopic pattern of the enamel specimens was similar.

Evaluation of some properties of fermented milk beverages that affect the demineralization of dental enamel

The aim of this in vitro study was to evaluate the erosive capacity of fermented milk beverages, as well as some of their properties that affect the demineralization of dental enamel (pH, buffering capacity, fluoride, calcium and phosphorus contents). Three different batches of 6 commercial brands of fermented milk beverages were analyzed. pH evaluation was accomplished using a potentiometer. The buffering capacity was measured by adding 1 mol L -1 NaOH. Fluoride concentration was assessed by an ion specific electrode after hexamethyldisiloxane-facilitated diffusion, and calcium and phosphorus concentrations were assessed by a colorimetric test using a spectrophotometer. Sixty specimens of bovine enamel were randomly assigned to 6 groups (n = 10). They were exposed to 4 cycles of demineralization in the fermented milk and remineralization in artificial saliva. Enamel mineral loss was determined by surface microhardness (%SMHC) and profilometric tests. The samples' pH ranged from 3.51 to 3.87; the buffering capacity ranged from 470.8 to 804.2 μl of 1 mol L -1 NaOH; the fluoride concentration ranged from 0.027 to 0.958 μgF/g; the calcium concentration ranged from 0.4788 to 0.8175 mgCa/g; and the phosphorus concentration ranged from 0.2662 to 0.5043 mgP/g. The %SMHC ranged from-41.0 to -29.4. The enamel wear ranged from 0.15 μm to 0.18 μm. In this in vitro study, the fermented milk beverages did not promote erosion of the dental enamel, but rather only a superficial mineral loss.

Analysis of the effects of thermal cycling on the microtensile shear bond strength of a self-etching and a conventional pit and fissure sealants to dental enamel

Objective: To analyze the effects of thermal cycling on the microtensile shear bond strength of a self-etching and a conventional pit and fissure sealants to dental enamel. Material and Method: Twenty-four healthy human molars extracted for orthodontic reasons, were sectioned in the mesio-distal direction and divided into two groups (n=24) according to the sealant to be applied: GI - conventional sealant Climpro (3M/ESPE) and GII - self-etching sealant Enamel Loc (Premier Dental). The sealants were applied on flattened enamel in matrixes 1 mm in diameter, in accordance with the manufacturers' recommendations. The specimens were stored in distilled water at 37°C for 24 hours. After this, half the samples of both groups were submitted to 500 thermal cycles in 30s baths at temperatures between 5 and 55°C. Forty-eight hours after the samples were made, the microtensile shear test was performed in an Instron 4411 test machine, with a stainless steel wire with a cylindrical cross section of 0.2mm in diameter at a constant speed of 0.5mm/s. The bond strength values were submitted to ANOVA for 2 factors and the fracture patterns were examined under an optical microscope at 65X magnification. Results: Thermal cycling did not influence the bond strength of the two sealants. The conventional sealant Climpro presented a statistically higher microtensile shear bond strength (11.72MPa, 11.34MPa with and without cycling, respectively) than the self-etching sealant Enamel Loc (5.92MPa, 5.02MPa with and without cycling, respectively). Fracture pattern analysis showed the occurrence of 100% of adhesive failures for Enamel Loc, while the conventional sealant Climpro presented 95% of adhesive failures and 5% of mixed failures. Conclusion: The conventional sealant presented higher microtensile shear bond strength to dental enamel in comparison with the self-etching sealant. Thermal cycling did not affect the bond strength of the sealants used in this study. © 2011 Nova Science Publishers, Inc.

Efficacy and cytotoxicity of a bleaching gel after short application times on dental enamel

Objectives: This study aimed to evaluate and correlate the efficacy and cytotoxicity of a 35 % hydrogen peroxide (HP) bleaching gel after different application times on dental enamel. Materials and methods: Enamel/dentin disks in artificial pulp chambers were placed in wells containing culture medium. The following groups were formed: G1, control (no bleaching); G2 and G3, three or one 15-min bleaching applications, respectively; and G4 and G5, three or one 5-min bleaching applications, respectively. Extracts (culture medium with bleaching gel components) were applied for 60 min on cultured odontoblast-like MDPC-23 cells. Cell metabolism (methyl tetrazolium assay) (Kruskal-Wallis/Mann-Whitney; α = 5 %) and cell morphology (scanning electron microscopy) were analyzed immediately after the bleaching procedures and the trans-enamel and trans-dentinal HP diffusion quantified (one-way analysis of variance/Tukey's test; α = 5 %). The alkaline phosphatase (ALP) activity was evaluated 24 h after the contact time of the extracts with the cells (Kruskal-Wallis/Mann-Whitney; α = 5 %). Tooth color was analyzed before and 24 h after bleaching using a spectrophotometer according to the Commission Internationale de l'Eclairage L*a*b* system (Kruskal-Wallis/Mann-Whitney; α = 0.05). Results: Significant difference (p < 0.05) in cell metabolism occurred only between G1 (control, 100 %) and G2 (60.6 %). A significant decrease (p < 0.05) in ALP activity was observed between G2, G3, and G4 in comparison with G1. Alterations on cell morphology were observed in all bleached groups. The highest values of HP diffusion and color alterations were observed for G2, with significant difference among all experimental groups (p < 0.05). G3 and G4 presented intermediate color change and HP diffusion values with no statistically significant differences between them (p > 0.05). The lowest amount of HP diffusion was observed in G5 (p < 0.05), which also exhibited no significant color alteration compared to the control group (p > 0.05). Conclusions: HP diffusion through dental tissues and its cytotoxic effects were proportional to the contact time of the bleaching gel with enamel. However, shorter bleaching times reduced bleaching efficacy. Clinical relevance: Shortening the in-office tooth bleaching time could be an alternative to minimize the cytotoxic effects of this clinical procedure to pulp tissue. However, the reduced time of bleaching agent application on enamel may not provide adequate esthetic outcome. © 2012 Springer-Verlag Berlin Heidelberg.