alpha-SiAlON-SiC composites obtained by gas-pressure sintering and hot-pressing

The objective of this work was the obtaining in situ of alpha-SiAlON-SiC composite, using an alternative rare-earth oxide mixture, RE2O3, as sintering additive, by two different sintering processes. As sintering additive, 20 vol.% of AlN-RE2O3 in a molar ratio of 90: 10 was mixed to the alpha-Si3N4 powder. In the Si3N4-AlN-RE2O3 powder mixture, 0, 10, 15 and 20wt.% of SiC were added. The powder batches were milled, dried and compacted by cold isostatic pressing. Two different sintering processes were used: gas-pressure sintering at 1950 degrees C for 1 h under 1.5 MPa of N-2 atmosphere, or uniaxial hot-pressing at 1750 degrees C, for 30 min under pressure of 20 MPa. The sintered samples were characterized by X-ray diffraction, scanning electron microscopy and mechanical properties. XRD patterns indicate only alpha-SiAlON (alpha') and beta-SiC as crystalline phases. It was observed that the SiC addition did not influence the alpha-SiAlON formation, although the growth of elongated alpha'-grains is substantially decreased. The hot-pressed composites presented better mechanical properties, exhibiting fracture toughness of 5 MPa m(1/2) and hardness around 21.5 GPa. (c) 2007 Elsevier B.V. All rights reserved.

Production of a low young modulus titanium alloy by powder metallurgy

Titanium alloys have several advantages over ferrous and non-ferrous metallic materials, such as high strengthto-weight ratio and excellent corrosion resistance. A blended elemental titanium powder metallurgy process has been developed to offer low cost commercial products. The process employs hydride-dehydride (HDH) powders as raw material. In this work, results of the Ti-35Nb alloy sintering are presented. This alloy due to its lower modulus of elasticity and high biocompatibility is a promising candidate for aerospace and medical use. Samples were produced by mixing of initial metallic powders followed by uniaxial and cold isostatic pressing with subsequent densification by isochronal sintering between 900 up to 1600 °C, in vacuum. Sintering behavior was studied by means of microscopy and density. Sintered samples were characterized for phase composition, microstructure and microhardness by X-ray diffraction, scanning electron microscopy and Vickers indentation, respectively. Samples sintered at high temperatures display a fine plate-like alpha structure and intergranular beta. A few remaining pores are still found and density above 90% for specimens sintered in temperatures over 1500 °C is reached.

Obtenção in situ do compósito alfa-SiAlON-SiC

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Development of alpha-SiAlON-SiC ceramic composites by liquid phase sintering

In this work, in situ alpha-SiAlON-SiC ceramic composites were obtained,by, liquid phase sintering, using SiC as reinforcement. Different beta-SiC powder contents (0-20 wt.%), were added to Si3N4-AlN-RE2O3. powder mixtures, and compacted by cold isostatic pressing. The samples were sintered at 1950 degrees C for 1 h, in N-2 atmosphere. Sintered: samples were characterized by relative density, weight loss, X-ray diffraction and scanning electron microscopy. Furthermore, mechanical properties such as hardness and fracture toughness were determined by Vickers indentation method. Lattice parameters of the alpha' phase did not considerably change with increase of SiC content. However, morphology, average grain size and aspect ratio of the alpha' phase were considerably changed with increase of the SiC content. These behavior influences significantly the mechanical properties of this hard ceramic composite. (C) 2006 Elsevier Ltd. All rights reserved.

Isochronal sintering of the blended elemental Ti-35Nb alloy

Titanium alloy parts are ideally suited for advanced aerospace systems and surgical implants because of their unique combination of high specific strength at both room temperature and moderately elevated temperature, in addition to excellent corrosion resistance. In this work, results of the Ti-35Nb alloy sintering are presented. This alloy, due to its lower modulus of elasticity and high biocompatibility, is a promising candidate for surgical and aerospace applications. Samples were produced by mixing of initial metallic hydride powders followed by uniaxial and cold isostatic pressing with subsequent densification by isochronal sintering between 700 and 1500 degrees C, in vacuum. Sintering behavior was studied by means of microscopy and density. Sintered samples were characterized for phase composition, microstructure and microbardness by X-ray diffraction, scanning electron microscopy and Vickers indentation, respectively. Samples sintered at high temperatures display a fine plate-like a structure and intergranular P. A few remaining pores are still found, and density above 97% for specimens sintered at 1500 degrees C is reached. (c) 2007 Elsevier B.V. All rights reserved.

Production of Ti-35Nb alloy by powder metallurgy for aerospace application

Titanium and its alloys provide high strength-to-weight ratios, good fatigue strength and increased corrosion resistance compared with others materials. Its acceptance in aerospace has been limited by costs considerations such as high cost of raw material, high buy-to-fly ratios and expensive machining operations. Significant cost reductions can be obtained by vacuum sintering and powder metallurgy (P/M) techniques by producing near net shapes and consequently minimizing material waste and machining time. The Ti 35Nb alloy exhibit a low modulus of elasticity. Stemming from the unique combination of high strength, low modulus of elasticity and low density, this alloy is intrinsically more resistant to shock and explosion damages than most other engineering materials. Samples were produced by mixing of initial metallic powders followed by uniaxial and cold isostatic pressing with subsequent densification by sintering between 900 and 1600 °C, in vacuum. Sintering behavior was studied by means of dilatometry. Sintered samples were characterized for phase composition, microstructure and microhardness by X-ray diffraction, scanning electron microscopy and Vickers indentation, respectively. Density was measured by Archimedes method. Copyright © 2004 Society of Automotive Engineers, Inc.

Obtenção da liga Ti-35Nb por metalurgia do pó para utilização em próteses ortopédicas

Pós-graduação em Engenharia Mecânica - FEG

Silicon carbide surface modification by nitrogen plasma expander

Silicon carbide (SiC) has been employed in many different fields such as ballistic armor, thermal coating, high performance mirror substrate, semiconductors devices, among other things. Plasma application over the silicon carbide ceramics is relatively recent and it is able to promote relevant superficial modifications. Plasma expander was used in this work which was supplied by nitrogen and switched by a capacitor bank. Nitrogen plasma was applied over ceramic samples for 20 minutes, in a total medium of 1440 plasma pulses. SiC ceramics were produced by uniaxial pressing method (40 MPa) associated to isostatic pressing (300 MPa) and sintered at 1950 degrees C under argon gas atmosphere. Silicon carbide (beta-sic - BF-12) supplied by HC-Starck and sintering additive (7.6% YAG - Yttrium Aluminum Garnet) were used in order to obtain the ceramics. Before and after the plasma application, the samples were characterized by SEM, AFM, contact angle and surface energy measurement.

Sintering of tin oxide using zinc oxide as a densification aid

The physicochemical electronic characteristics of SnO2 render it useful in many technical applications, including ceramic varistors, stable electrodes used in electric glass-melting furnaces and electrometallurgy of aluminum, transparent windows and chemical sensors. The use of ZnO as a sintering aid was explored in this study to obtain SnO2 as a dense ceramic. Compacts were obtained by mechanical mixing of oxides, isostatic pressing at 210 MPa and sintering in situ inside a dilatometer at heating rates of 10degreesC/min. The grain size and microstructure were investigated by scanning and transmission electron microscopy (SEM/TEM). The phases and chemical composition were analyzed by energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results indicated that ZnO acts as a densification aid for SnO2, improving its grain growth with additions of up to 2 mol%. ZnO forms a solid solution with SnO2 UP to 1 mol%, above which SnZnO3 precipitates in the grain boundary, potentially inhibiting shrinkage and grain growth. (C) 2004 Kluwer Academic Publishers

Sintering of tin oxide processed by slip casting

Sintering of SnO 2 compacts, obtained through slip casting, was studied by means of dilatometry, Hg porosimetry, scanning electron microscopy, and density measurement (Archimedes method). Sintering is strongly influenced by the green microstructure. Moreover, the sintering mechanisms are not dependent on the slurries' solid content up to 50% of solids in volume. Above this value, agglomerates are formed, leading to differential sintering inside and among the agglomerates. Another important point is the reduction of the temperature of maximum shrinkage rate when compared to tin oxide processed by isostatic pressing. This reduction is more accentuated when ammonium hydroxide is added to the suspension. (C) 2000 Published by Elsevier Science Ltd. All rights reserved.

Use of high energy ball milling on the sintering optimization of alumina ceramics

In this work, the effect of the milling time on the densification of the alumina ceramics with or without 5wt.%Y 2O 3, is evaluated, using high-energy ball milling. The milling was performed with different times of 0, 2, 5 or 10 hours. All powders, milled at different times, were characterized by X-Ray Diffraction presenting a reduction of the crystalline degree and crystallite size as function of the milling time increasing. The powders were compacted by cold uniaxial pressing and sintered at 1550°C-60min. Green density of the compacts presented an increasing as function of the milling time and sintered samples presented evolution on the densification as function of the reduction of the crystallite size of the milled powders. © (2010) Trans Tech Publications.

Development of silicon carbide substrates for aerospace applications

Payload and high-tech are important characteristics when the goals are aerospace applications. The development of the technologies associated to these applications has interests that transcend national boundaries and are of strategic importance to the nations. Ultra lightweight mirrors, supports and structures for optical systems are important part of this subject. This paper reports the development of SiC substrates, obtained by pressing, to be applied on embedded precision reflective optics. Different SiC granulometries, having YAG as sintering additive, were processed by: ball milling, drying and deagglomeration, sift, uniaxial and isostatic pressing, and, finally, argon atmosphere sintering at 1900°C. Different porosities were obtained according to the amount of organic material added. Into one side of the samples pellets of organic material were introduced to generate voids to reduce the weight of samples as a whole. The substrates were grinding and polished, looking for a SiC surface having low porosity, as porosity is directly related to light scattering that should be avoided on optical surfaces. Laser surface treatments were applied (using or not SiC barbotine) as a method to improve the surface quality. The samples were characterized by optical and laser confocal microscopy, roughness measurements and mechanical tests. The results are very promissory for future applications. © 2012 Materials Research Society.

Physicochemical analysis of Ti-Si-B powder aalloys

Titanium alloys of Ti-Si-B system were manufactured by blended elemental powder method using Ti, Si and B powders as starting materials. It was found that uniaxial and isostatic pressing followed by hot pressing at around 1000°C, for 20 minutes, provided good densification of such alloys. The physicochemical studies were performed by means of scanning electron microscopy, X-ray diffraction, atomic force microscopy and microindentation/wear tests. The investigations revealed a multiphase microstructure formed mainly by α-titanium, Ti6Si2B, Ti5Si3, TiB and Ti3Si phases. The phase transformations after pressureless sintering at 1200°C was also studied by X-ray diffraction for the Ti-18Si-6B composition. As stated in some other researches, these intermetallics in the α-titanium matrix provide high wear resistance and hardness, with the best wear rate of 0.2 mm3/N.m and the highest hardness of around 1300 HV. © (2012) Trans Tech Publications, Switzerland.

Vitrocerâmicas de alta resistência mecânica obtidas a partir da cristalização do sistema SiO2-Al2O3-MgO-Li2O com adição de ZrO2 e B2O3

Pós-graduação em Engenharia Mecânica - FEG

Otimização e caracterização microestrutural de cerâmicas de carbeto de silício obtidas com material nacional para uso em blindagem balística

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)