Self-assembled FePt nanocrystals with large coercivity: Reduction of the fcc-to-L1(0) ordering temperature

Herein we report the synthesis and properties of Fe55Pt45 nanoparticles, both monodisperse and self-assembled into hexagonal close-packed and cubic arrays of 4.0 +/- 0.2 nm size in an L1(0) structure, obtained by a modified polyol process. The new synthetic route improved the control over the particle composition, thereby reducing the temperature required to convert from face-centered cubic (fcc) to face-centered tetragonal (fct) phase by some 30-50 degrees C without additives. Annealing at 550 degrees C for 30 min converts the self-assembled nanoparticles into ferromagnetic nanocrystals with large coercivity, H-C = 11.1 kOe. Reducing the fcc-to-fct (L1(0)) ordering temperature avoided particle coalescence and decreased the loss in particle positional order without compromising the magnetic properties, as is generally observed when additives are used.

Preparation and structural characterization of vulcanized natural rubber nanocomposites containing nickel-zinc ferrite nanopowders

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Temperature dependence and magnetocrystalline anisotropy studies of self-assembled L1(0)-Fe55Pt45 ferromagnetic nanocrystals

Temperature dependence and uniaxial magnetocrystalline anisotropy properties of the chemically synthesized 4 nm L1(0)-Fe55Pt45 nanoparticle assembly by a modified polyol route are reported. As-prepared nanoparticles are superparamagnetic presenting fcc structure, and annealing at 550 degrees C converts the assembly into ferromagnetic nanocrystals with large coercivity (H-C>1 T) in an L1(0) phase. Magnetic measurements showed an increasing in the ferromagnetically ordered fraction of the nanoparticles with the annealing temperature increases, and the remanence ratio, S=M-R/M-S congruent to 0.76, suggests an (111) textured film. A monotonic increase of the blocking temperature T-B, the uniaxial magnetocrystalline anisotropy constant K-U, and the coercivity H-C with increasing annealing temperature was observed. Magnetic parameters indicate an enhancement in the magnetic properties due to the improved Fe55Pt45 phase stabilizing, and the room-temperature stability parameter of 67, which indicates that the magnetization should be stable for more than ten years, makes this material suitable for ultrahigh-density magnetic recording application.(c) 2007 American Institute of Physics.

Iron Oxide Versus Fe55Pt45/Fe3O4: Improved Magnetic Properties of Core/Shell Nanoparticles for Biomedical Applications

In this paper, synthesis of the Fe55Pt45/Fe3O4 core/shell structured nanoparticles using the modified polyol process combined with the seed-mediated growth method is reported. Iron oxide shell thickness was tuned controlling the Fe(acac)(3)/FePt seeds in the reaction medium. Annealing of the core/shell structure leads to iron-rich layer formation around the hard FePt phase in the nanoparticle core. However, the 2 nm Fe3O4 shell thickness seems to be the limit to obtain the enhanced magnetization close to the alpha-Fe and preserving an iron oxide shell after annealing at 500 degrees C for 30 min in a reducing atmosphere. The presence of both the oxide layer on nanoparticle surface and an intermediate iron-rich FePt layer after annealing promote strong decreases in the coercive field of the 2-nm-oxide shell thickness. These annealed nanoparticles were functionalized with dextran, presenting the enhanced characteristics for biomedical applications such as higher magnetization, very low coercivity, and a slightly iron oxide passivated layer, which leads an easy functionalization and decreases the nanoparticle toxicity.

Magnetic properties of acicular ultrafine iron particles

Magnetic properties of acicular (similar to60 and similar to200 nm) iron particles, obtained by reduction of alumina-coated goethite particles, are reported. X-ray diffraction and Mossbauer spectroscopy showed that the particles consist of a alpha-Fe core and a thin surface layer of maghemite. Magnetization data indicated an improvement of similar to28% in the saturation magnetization, coercive field, and squareness for particles with similar to60 nm. This magnetic property enhancement of the present particles, whose size is 40% smaller than those commercially available, could result in a similar decrease of the bit-size for higher density of magnetic media.

Effect of the bath pH on the electrodeposition of nanocrystalline Pd-Co alloys and their magnetic properties

The effect of the bath pH on the electrodeposition of nanocrystalline Pd-Co alloys and on their magnetic properties was studied. The pH practically did not affect the alloy composition. Conversely, the pH showed a significant influence on the shape and size of crystallites. Two different crystallites morphology were observed depending on the bath pH. A crystallite size ranging from 18.2 to 30 nm was obtained from X-ray diffractometry (XRD) patterns using the Scherrer's method. Also from the XRD patterns the lattice strain percentage was calculated and correlated with the residual stress, which probably originated during the film electrodeposition on the substrate. Some alloy magnetic properties showed small variations. In contrast, high and unexpected coercivities were obtained reaching a maximum of 1.69 kOe at pH 5.5. The high coercivity values were attributed to the presence of residual stress at the film-substrate interface, which increased as the bath pH and crystallite size decrease, both of them contributing simultaneously to increase in coercivity. (C) 2006 Elsevier B.V. All rights reserved.

The influence of residual stress and crystallite size on the magnetic properties of electrodepo sited nanocrystalline Pd-Co alloys

Nanocrystalline Pd-Co alloys were obtained by electrodeposition from an ammoniacal chloride bath. The influence of the crystallite size and the residual stress on the magnetic properties of the alloys was investigated. The residual stress increased as the applied current density was increased. It was associated to the high nucleation rate during electrodeposition and correlated to the lattice strain, estimated from the XRD patterns. Also from the XRD patterns the average crystallite size and the lattice constant were determined by Scherrer's and Rietveld's methods, respectively. Both parameters were directly influenced by the applied current density. Magnetic properties such as coercivity, remanence, saturation magnetization and squareness showed strong dependence on the residual stress and crystallite size. Coercivity higher than 1 kOe was achieved when a high current density was applied. High coercivity was attributed to the presence of residual stress and to the small crystallite size of deposits. (C) 2007 Elsevier B.V. All rights reserved.

Superparamagnetic Ni:SiO2-C nanocomposites films synthesized by a polymeric precursor method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Ferrita de bário: preparação de fases dopadas com cobalto, titânio e estanho

Pós-graduação em Química - IQ

Structural, morphological and magnetic characterization of electrodeposited Co-Fe-W alloys

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)