Determination of potassium and sodium in an ash sample by gamma-ray spectroscopy

Neutron activation analysis and gamma-ray spectroscopy were used to determine the quantity of potassium and sodium in an ash sample of Tabebuia sp bombarded with thermal neutrons. These techniques, widely applied in nuclear physics, can be used in the context of wood science as an alternative for the usual physical chemistry methods applied in this area. The quantity of K and Na in an 8.60 +/- 0.10 mg of ash was determined as being 1.3 +/- 0.3 mg and 11.0 +/- 1.8 mu g, respectively. The ratio of Tabebuia sp converted into ash was also determined as 0.758 +/- 0.004%.

Sugarcane bagasse ash as a potential quartz replacement in red ceramic

Sugarcane bagasse ash (SCBA) is an industrial waste that contains silicon and aluminum oxides as the major components and iron, calcium, magnesium, and potassium oxides as the main minor components. In this paper, SCBA from one Brazilian factory was characterized and tested for its influence on the ceramic properties of clay/ash ceramic probes. Prismatic probes were pressed (18 MPa) using a ceramic mass mixed with 0%, 5%, 8%, and 10% ash. The probes were fired at temperatures between 800 degrees and 1200 degrees C. X-ray diffraction, X-ray fluorescence, thermal analysis (differential thermal analysis, thermo-gravimetric analysis/differential thermogravimetric analysis), and tests for texture (particle-size analysis), flexural strength, and linear shrinkage were carried out to characterize the samples. The results showed that the amount of ash to be incorporated will depend on mainly the composition of clay but also ash, and indicated that the clay used in this work can incorporate up to 10% weight of ash to produce solid bricks. The results also showed an improvement in ceramic/ash properties up to sintering temperatures higher than 1000 degrees C.

Crystallization of SiO2-CaO-Na2O Glass Using Sugarcane Bagasse Ash as Silica Source

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Briquetting of charcoal from sugar-cane bagasse fly ash (scbfa) as an alternative fuel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Reuse of sugarcane bagasse ash (SCBA) to produce ceramic materials

Sugarcane bagasse ash (SCBA) is a residue resulting from the burning of bagasse in boilers in the sugarcane/alcohol industry. SCBA has a very high silica concentration and contains aluminum, iron, alkalis and alkaline earth oxides in smaller amounts. In this work, the properties of sintered ceramic bodies were evaluated based on the concentration of SCBA, which replaced non-plastic material. The ash was mixed (up to 60 wt%) with a clayed raw material that is used to produce roof tiles. Prismatic probes were pressed and sintered at different temperatures (up to 1200 degrees C). Technological tests of ceramic probes showed that the addition of ash has little influence on the ceramic properties up to 1000 C. X-ray diffraction and thermal analysis data showed that, above this temperature the ash participates in the sintering process and in the formation of new important phases. The results reported show that the reuse of SCBA in the ceramic industry is feasible. (C) 2011 Elsevier Ltd. All rights reserved.

Thermoregulation by an Australian murine rodent, the ash-grey mouse (Pseudomys albocinereus)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Impact of coal mining on water quality of three artificial lakes in Morozini River Basin (Treviso, Santa Catarina State, Brazil)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The Chemical Percolation Devolatilization Model Applied to the Devolatilization of Coal in High Intensity Acoustic Fields

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Utilização do coque verde de petróleo da Petrobras em substituição parcial ao carvão mineral das misturas injetadas em altos fornos

The Petrobras produced green petroleum coke (GPC) is a carbon rich fuel, virtually ash-free, with low sulfur content, and is a fuel suitable to replace metallurgical coke in blast furnaces. The GPC was tested in a pulverized coal injection simulator built in the Volta Redonda research center. It presented a low burning efficiency due to low volatile material content and high substitution rate by the carbon content. The tests were carried out in blast furnaces with ≤ 50% Petrobras GPC in the coal blends. The injected coal/CVP mixtures produced no negative side effects in the blast furnace grinding systems, pneumatic conveying, or operating process. The mixture burning process inside the blast furnace showed a decrease in fuel consumption, with a significant reduction in metallurgical coke consumption. The industrial-scale tests of the GPC mixtures did not reach the 70% maximum for lack of the GPC feedstock, which is necessary to continue with standard coal mixtures.

Evolution of the mechanical properties of a tropical soil stabilized with lime and ash of rice rind

The ash of rice rind is a pozzolanic material that reacts with the calcium hydroxide (Ca (OH)2) forming bonding composites, when finely worn out and in water presence. Considering this behavior, the objective of the present work was to evaluate the potential use of this residue in the enrichment of the content of pozzolanic materials of a tropical soil stabilized with a commercial hydrated lime. The laboratory testing program incorporated unconfined compression strength tests performed on the soil and on its mixtures with contents of 8% of lime enriched with 5 and 10% of ash of rice rind in relation to the soil dry mass. The results of the testing program supported that the use of the residue was effective in increasing the degree of reactivity of the soil that was also directly related with the increase in the ash content and the period of cure of the mixtures.

Glass-ceramic material from the SiO 2-Al 2O 3-CaO system using sugar-cane bagasse ash (SCBA)

Brazil is the world's largest producer of alcohol and sugar from sugarcane. Currently, sugarcane bagasse is burned in boilers to produce steam and electrical energy, producing a huge volume of ash. The major component of the ash is SiO 2, and among the minor components there are some mineralizing agents or fluxing. Published works have shown the potential of transforming silicate-based residues into glass-ceramic products of great utility. This work reports the research results of SCBA use to produce glass-ceramics with wollastonite, rankinite and gehlenite as the major phases. These silicates have important applications as building industry materials, principally wollastonite, due to their special properties: high resistance to weathering, zero water absorption, and hardness among others. The glasses (frits) were prepared mixing ash, calcium carbonate and sodium or potassium carbonates as flux agents, in different concentrations. X-ray fluorescence was used to determine the chemical composition of the glasses and their crystallization was assessed by using thermal analysis (DTA/DSC/TGA) and X-ray diffraction. The crystallization kinetics was evaluated using the Kissinger method, giving activation energies ranging from 200 to 600 kJ/mol. © 2011 Ceramic Society of Japan.

Use of slag/sugar cane bagasse ash (SCBA) blends in the production of alkali-activated materials

Blast furnace slag (BFS)/sugar cane bagasse ash (SCBA) blends were assessed for the production of alkali-activated pastes and mortars. SCBA was collected from a lagoon in which wastes from a sugar cane industry were poured. After previous dry and grinding processes, SCBA was chemically characterized: it had a large percentage of organic matter (ca. 25%). Solutions of sodium hydroxide and sodium silicate were used as activating reagents. Different BFS/SCBA mixtures were studied, replacing part of the BFS by SCBA from 0 to 40% by weight. The mechanical strength of mortar was measured, obtaining values about 60 MPa of compressive strength for BFS/SCBA systems after 270 days of curing at 20 °C. Also, microstructural properties were assessed by means of SEM, TGA, XRD, pH, electrical conductivity, FTIR spectroscopy and MIP. Results showed a good stability of matrices developed by means of alkali-activation. It was demonstrated that sugar cane bagasse ash is an interesting source for preparing alkali-activated binders. © 2013 by the authors; licensee MDPI, Basel, Switzerland.

Estudo da combustão de carvões e misturas com o coque verde de petróleo injetadas em altos fornos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Impact strength and abrasion resistance of high strength concrete with rice husk ash and rubber tires

The paper discusses the application of High Strength Concrete (HSC) technology for concrete production with the incorporation of Rice Husk Ash (RHA) residues by replacing a bulk of the material caking and rubber tires with partial aggregate volume, assessing their influence on the mechanical properties and durability. For concrete with RHA and rubber, it was possible to reduce the brittleness by increasing the energy absorbing capacity. With respect to abrasion, the RHA and rubber concretes showed lower mass loss than the concrete without residues, indicating that this material is attractive to be used in paving. It is thus hoped that these residues may represent a technological and ecological alternative for the production of concrete in construction works.

Valorization of sugarcane bagasse ash: Producing glass-ceramic materials

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)