Tribocorrosion behaviour of hot pressed CoCrMo−Al2O3 composites for biomedical applications

Alumina/alumina wear couple can lower the wear rates and thus metallic ion releasing on load bearing metallic implant materials. However, the low fracture toughness of ceramics is still a major concern. Therefore, the present study aims to process and to triboelectrochemically characterise the 5 and 10 vol.-%Al2O3 reinforced CoCrMo matrix composites. Corrosion and tribocorrosion behaviour of the composites were investigated in 8 g L−1 NaCl solution at body temperature. Corroded and worn surfaces were investigated by a field emission gun scanning electron microscope equipped with energy dispersive X-ray spectroscopy. After tribocorrosion experiments, wear rates were calculated using a profilometer. Results suggest that Al2O3 particle addition decreased the tendency of CoCrMo alloy to corrosion under both static and tribocorrosion conditions. However, no significant influence on the corrosion and wear rates was observed in composites mainly due to increased porosity and insufficient matrix/reinforcement bonding.

Influência do tipo de conexão pilar/implante na manutenção da pré-carga de parafusos de retenção e na desadaptação vertical da coroa protética antes e após ciclagem mecânica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of recasting procedure upon corrosion behavior and metallic ion release of Co-Cr-Mo dental alloy in physiological

Recasting process influence upon corrosion behavior of Co-Cr-Mo dental alloy in simulated physiological serum has been investigated using chemical and electrochemical techniques. Recast Co-Cr-Mo alloy by induction (IND) or by blowtorch (FLAME) has exhibited similar dendritic structures. Both IND and FLAME alloys have presented good corrosion resistance in physiological serum. Passivation process provides this corrosion resistance. Codissolution makes this process difficult. Passive films, formed on these alloys, have been analyzed as a dual layer consisting of an inner barrier and an outer porous layer. Passive film protective characteristics are higher in FLAME than in IND alloy. On this last alloy, the passive film is more porous due to a higher Codissolution. ©Carl Hanser Verlag, München.