Single-phase Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 (BST:Sn) powders with perovskite structure were prepared by the soft chemical method. Infrared data indicates that the BST:Sn powder is carbonate free while Raman analysis has shown that the transversal (TO) and longitudinal (LO) optical modes tend to disappear with tin addition. The electron diffraction pattern of the BST:Sn powder showed an interplanar distance of 3.94 angstrom characteristic of the pseudo-cubic structure. (c) 2007 Elsevier B.V. All rights reserved.

Relevância:

70.00% 70.00%

Publicador:

Resumo:

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Relevância:

70.00% 70.00%

Publicador:

Resumo:

This paper focuses on the magnetoelectric coupling (ME) at room temperature in lanthanum modified bismuth ferrite thin film (BLFO) deposited on SrRuO 3-buffered Pt/TiO 2/SiO 2/Si(100) substrates by the soft chemical method. BLFO film was coherently grown at a temperature of 500 °C. The magnetoelectric coefficient measurement was performed to evidence magnetoelectric coupling behavior. Room temperature magnetic coercive field indicates that the film is magnetically soft. The maximum magnetoelectric coefficient in the longitudinal direction was close to 12 V/cmOe. Dielectric permittivity and dielectric loss demonstrated only slight dispersion with frequency due the less two-dimensional stress in the plane of the film. Polarization reversal was investigated by applying dc voltage through a conductive tip during the area scanning. We observed that various types of domain behavior such as 71 ° and 180° domain switching, and pinned domain formation occurred. Copyright © 2009 American Scientific Publishers All rights reserved.

Relevância:

70.00% 70.00%

Publicador:

Resumo:

This paper describes research on a simple low-temperature synthesis route to prepare bismuth ferrite nanopowders by the polymeric precursor method using bismuth and iron nitrates. BiFeO 3 (BFO) nanopowders were characterized by means of X-ray diffraction analyses, (XRD), Fourier transform infrared (FT-IR) spectroscopy, Raman spectroscopy (Raman), thermogravimnetric analyses (TG-DTA), ultra-violet/vis (UV/Vis) and field emission scanning electron microscopy (FE-SEM). XRD patterns confirmed that a pure perovskite BiFeO 3 structure with a rhombohedral distorted perovskite structure was obtained by heating at 850 °C for 4 hours. Typical FT-IR spectra for BFO powders revealed the formation of a perovskite structure at high temperatures due to a metal-oxygen bond while Raman modes indicated oxygen octahedral tilts induced by structural distortion. A homogeneous size distribution of BFO powders obtained at 850 °C for 4 hours was verified by FE-SEM analyses. © 2012 Elsevier Ltd and Techna Group S.r.l.

Relevância:

70.00% 70.00%

Publicador:

Resumo:

Bismuth titanate templates (Bi4Ti3O12) were synthesized by the molten salt method in Na2SO4 and K2SO4 fluxes, using an amorphous Bi4Ti 3O12 precursor and a mechanically mixed Bi 2O3+TiO2 mixture as the starting materials. The templates were characterized by means of X-Ray Diffraction, FT-IR, FT-Raman, FEG-SEM and TEM. The templates are free of secondary phases and present orthorhombic structure with orientation in the c-plane. FT-IR suggests no traces of sulfate groups revealing that the molten salt synthesis was beneficial for elimination of inorganic species and for the arrangement of individual nanocrystals into ordered lattices. FEG-SEM analyses of BIT templates revealed that most of the grains were homogeneous with a length of 3.1 μm and a width of 0.3 μm and had plate-like morphology. TEM investigations show that the c-axis of the perovskite units is parallel to the thickness direction of the grains and no liquid-phase was formed during BIT phase formation. © 2013 Elsevier Ltd and Techna Group S.r.l.

Relevância:

60.00% 60.00%

Publicador:

Resumo:

A study was undertaken about the structural and photoluminescent properties at room temperature of CaCu3Ti4O12 (CCTO) powders synthesized by a soft chemical method and heat treated between 300 and 800 °C. The decomposition of precursor powder was followed by thermogravimetric analysis (TG-DTA), X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Fourier transform Raman (FT-Raman) and photoluminescence (PL) measurements. XRD analyses revealed that the powders annealed at 800 °C are becoming ordered and crystallize in the cubic structure. The most intense PL emission was obtained for the sample calcined at 700 °C, which is not highly disordered (300-500 °C) and neither completely ordered (800 °C). From the spectrum it is clearly visible that the lowest wavelength peak is placed around 480 nm and the highest wavelength peak at about 590 nm. The UV/vis absorption spectroscopy measurements showed the presence of intermediate energy levels in the band gap of structurally disordered powders. © 2012 Elsevier Ltd and Techna Group S.r.l.

Relevância:

60.00% 60.00%

Publicador:

Resumo:

The structural and photoluminescence properties at room temperature of CeO2 nanoparticles synthesized by a microwave-assisted hydrothermal method (MAH) under different soaking times on KOH mineralizer added to a cerium ammonium nitrate aqueous solution were undertaken. X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Fourier transform Raman (FT-Raman) and photoluminescence (PL) measurements were employed. XRD revealed that the nanoparticles are free of secondary phases and crystallize in the cubic structure. The UV/vis absorption spectroscopy suggested the presence of intermediate energy levels in the band gap of structurally ordered powders. The most intense PL emission was obtained for nanoparticles which represent a lower particle size. © 2013 Elsevier Ltd and Techna Group S.r.l.

Relevância:

60.00% 60.00%

Publicador:

Resumo:

The structural and photoluminescent properties at room temperature of CeO2 nanoparticles synthesized by a Microwave-Assisted Hydrothermal Method (MAH) under different praseodymium contents was undertaken. X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM), UV-vis Spectroscopy (UV-vis), Fourier Transform Raman (FT-Raman) and Photoluminescence (PL) measurements were employed. XRD revealed that the nanoparticles are free of secondary phases and crystallize in the cubic structure while FT-Raman revealed a typical scattering mode of fluorite type. The UV/vis absorption spectroscopy suggested the presence of intermediate energy levels in the band gap of structurally ordered powders. The most intense PL emission was obtained for nanoparticles which represent a lower particle size. © 2013 Elsevier Ltd and Techna Group S.r.l.

Relevância:

60.00% 60.00%

Publicador:

Resumo:

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Relevância:

30.00% 30.00%

Publicador:

Resumo:

The fac-[RuCl3(NO)(dppb)] complex I has been prepared from solution of the correspondent mer isomer in refluxing methanol (dppb = 1,4-bis(diphenylphosphino)butane). The mer-[RuCl3(NO)(diop)] (II) has been obtained from the mer-[RuCl3(diop)(H2O)] by bubbling NO for 1 h in dichloromethane (diop = 2S,3S-O-isopropylidene-2,3-dihydroxy-1,4-bis(diphenylphosphino)butane). The complexes have been characterized by microanalysis, cyclic voltammetry (CV), IR and 31P{1H} NMR spectroscopies. The crystal and molecular structures of these two compounds have been determined from X-ray studies. The mer-[RuCl3(NO)(dppb)] isomer III was characterized in solution by NMR spectra (31P{1H}, 1H{31P}, 31P-1H HETCORR, COSY 1H-1H, HMQC 1H-13C and HMBC 1H-13C). © 2002 Elsevier Science Ltd. All rights reserved.