New insights for materials science characterisation using different complementary techniques combined with x-ray absorption spectroscopy

The combination of x-ray absorption spectroscopy (XAS) with UV-Vis and Raman spectroscopies or with Differential Scanning Calorimetry (DSC) has been recently carried out on the D44 beamline of DCI-LURE. The different set-ups used to perform such combinations are described and examples of combined investigations belonging to different field of materials science (coordination chemistry, sol-gel and catalysis) are presented. © Physica Scripta 2005.

Influence of thermal annealing treatment in oxygen atmosphere on grain boundary chemistry and non-ohmic properties of SnO2 center dot MnO polycrystalline semiconductors

The present work studied the influence of thermal treatment in oxygen rich atmosphere on heterogenous junctions in Mn-doped SnO2 polycrystalline system presenting varistor behavior. The samples were prepared by conventional oxide mixture methodology, and were submitted to heat treatment in oxygen rich atmosphere at 900 degrees C for 2h. The samples were characterized by X-ray diffraction, scanning electron microscopy, dc and ac electrical measurements. The results showed that there is an evident relationship between the microstructure heterogeneity and non-ohmic electrical properties. It was found that for this SnO2 center dot MnO-based varistor system the heat treatment in oxygen rich atmosphere does not necessarily increase the varistors properties, which was related to the decrease in the grain boundary resistance. The results are compared with Co-doped SnO2 varistors and ZnO based varistors. (C) 2008 WILEY-VCH Verlay GmbH & Co. KGaA, Weinheim.

Effect of Ta2O5 doping on the electrical properties of 0.99SnO(2)center dot 0.01CoO ceramic

The effect of Ta2O5 doping in 0.99SnO(2). 0.01CoO on the microstructure and electrical properties of this ceramic were analyzed in this study. The grain size was found to decrease from 6.87 mu m to 5.68 mu m when the Ta2O5 concentration increased from 0.050 to 0.075 mol%. DC electrical characterization showed a dramatic increase in the current loss and decrease in the non-linear coefficient with the increase of the Ta2O5 concentration. The conduction mechanism is by thermionic emission and the potential barriers are of Schottky type, separated by a thin film. (C) 2000 Kluwer Academic Publishers.

Nanostructured materials based on mesoporous silica and mesoporous silica/apatite as osteogenic growth peptide carriers

The aim of this work was the preparation of inorganic mesoporous materials from silica, calcium phosphate and a nonionic surfactant and to evaluate the incorporation and release of different concentrations of osteogenic growth peptide (OGP) for application in bone regeneration. The adsorption and release of the labeled peptide with 5,6-carboxyfluorescein (OGP-CF) from the mesoporous matrix was monitored by fluorescence spectroscopy. The specific surface area was 880 and 484 m2 g- 1 for pure silica (SiO) and silica/apatite (SiCaP), respectively; the area influenced the percentage of incorporation of the peptide. The release of OGP-CF from the materials in simulated body fluid (SBF) was dependent on the composition of the particles, the amount of incorporated peptide and the degradation of the material. The release of 50% of the peptide content occurred at around 4 and 30 h for SiCaP and SiO, respectively. In conclusion, the materials based on SiO and SiCaP showed in vitro bioactivity and degradation; thus, these materials should be considered as alternative biomaterials for bone regeneration. © 2013 Elsevier B.V.

Aprimoramento da sistemática U-Pb através do método de traços de fissão e técnicas de caracterização: termocronologia da faixa Brasília e sua correlação com a bacia do Paraná

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Production of a low young modulus titanium alloy by powder metallurgy

Titanium alloys have several advantages over ferrous and non-ferrous metallic materials, such as high strengthto-weight ratio and excellent corrosion resistance. A blended elemental titanium powder metallurgy process has been developed to offer low cost commercial products. The process employs hydride-dehydride (HDH) powders as raw material. In this work, results of the Ti-35Nb alloy sintering are presented. This alloy due to its lower modulus of elasticity and high biocompatibility is a promising candidate for aerospace and medical use. Samples were produced by mixing of initial metallic powders followed by uniaxial and cold isostatic pressing with subsequent densification by isochronal sintering between 900 up to 1600 °C, in vacuum. Sintering behavior was studied by means of microscopy and density. Sintered samples were characterized for phase composition, microstructure and microhardness by X-ray diffraction, scanning electron microscopy and Vickers indentation, respectively. Samples sintered at high temperatures display a fine plate-like alpha structure and intergranular beta. A few remaining pores are still found and density above 90% for specimens sintered in temperatures over 1500 °C is reached.

Fractal behavior throughout stretch zone of 15-5PH steel under elastic-plastic loading conditions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The influence of area/volume ratio on microstructure and non-Ohmic properties of SnO2-based varistor ceramic blocks

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Novel production method of porous surface Ti samples for biomedical application

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Design of dental implants, influence on the osteogenesis and fixation

The fixation and the bone ingrowth at the interface of porous cylindrical implants (total porosity of 37% and average pores diameter of 480 mu m) were compared in vivo to rough cylindrical implants (R-a = 5.3 mu m), both of commercially pure titanium, made by powder metallurgy. The implants were inserted into the tibias of 20 rabbits and the animals were sacrificed 4 and 8 weeks after surgery. The percentage of bone-implant contact observed in porous implant was significantly larger than in the rough ones for all of sacrifice periods, respectively, 57% vs. 46% after 4 weeks, and 59% vs. 50% after 8 weeks. The mechanical tests showed a significant increase in the shear strength of the porous implants for the two analyzed periods, 4 and 8 weeks (14 and 20 MPa), when compared with rough ones (4 and 13 MPa). These results suggest that porous implants improve the contact at the implant-bone interface and increase the fixation to the bone, improving the osseointegration. Thus, the porous implant might be an alternative to dental implant in less favorable conditions, and appear to be better fixed to bone, offering promising alternatives.

Relationship between grain-boundary capacitance and bulk shallow donors in SnO2 polycrystalline semiconductor

The relationship between grain-boundary capacitance and extrinsic shallow donors caused by Nb addition to SnO2 center dot COO binary polycrystalline system has been investigated by means of combined techniques such as I-V characteristic response, complex impedance and capacitance analysis and electrostatic force microscopy. The estimated role of the Nb doping is to increase the concentration of shallow donors that are capable of enhancing the electronic donation to grain-boundary acceptors. This effect leads to the formation of potential barriers at grain boundaries with a simultaneous increase of grain-boundary capacitance and non-Ohmic features of the polycrystalline device doped with Nb atoms.

Photoluminescence in amorphous zirconium titanate

Photoluminescence at room temperature was observed in amorphous zirconium titanate obtained from the polymeric precursor method. This was the first time in which PL was noticed in an amorphous compound made of two network formers. The PL spectra could be deconvoluted into two bands, whose center 1 was located from 540 nm to 552 nm and center 2 from 625 nm to 641 nm. The co-existence of fivefold and sixfold oxygen coordination of titanium and/or zirconium could be the origin of the radiative recombination of electron-hole pairs in amorphous ZT, which may be responsible for the emission of the photoluminescence.

Luminescence in semi-crystalline zirconium titanate doped with lanthanum

This paper aims to describe the synthesis of the semi-crystalline and crystalline powder of lanthanum doped with zirconium titanate (65/35), LZT through Pechini method. The analysis done by Raman demonstrated that semi-crystalline phase at 550 degrees C and crystalline phase after 600 degrees C were formed. The XRD pattern shows the ZrTiO4 phase formation demonstrating that La substitutions into the lattice take place. The calcined powder at different temperatures shows a semi-crystalline phase presenting photoluminescence effect when processed at low temperatures. From 300 to 400 degrees C a broadband is observed at 563 nm and 568 nm, respectively. Defects creation such as: Zr3+ center dot Vo(center dot center dot) and Ti3+ - V-O(center dot center dot), Zr and Ti replaced by La with vacancy formation, impurities and imperfections contributed to the photoluminescence effect. However, the main emission is due to a reverse Ti4+ -> O2- or/and Zr4+ -> O2- transition that occur within a regular titanate or zirconate eight-fold coordination [BO8-delta], B = Zr4+, Ti4+. (c) 2006 Elsevier B.V. All rights reserved.

The influence of aluminium on the overall properties of SnO2-based varistors

The influence of aluminium on the development of the microstructure and on the electrical behaviour of the SnO2 center dot Co3O4 center dot Nb2O5 typical varistor system was studied. Two sources of Al were used, alumina (Al2O3) and boehmite (AlO(OH)). The microstructural features were characterised with scanning (SEM) and transmission (TEM) electron microscopies. The different phases present in the studied samples were also studied with XRD, EDS and electron diffraction patterns of selected areas (SAED). Particles containing Sri, Co, Al, and O were unveiled with TEM. Impedance spectroscopy measurements and current density versus electric field characteristics revealed superior electrical properties for samples with AlO(OH). The higher non-linearity (alpha = 19) was achieved with the addition of 0.1% mol of boehmite. The influence of the secondary phases on the electrical properties is also addressed in this work.