Activity and characterization by XPS, HR-TEM, Raman spectroscopy, and BET surface area of CuO/CeO2-TiO2 catalysts

Structural and textural studies of a CuO/TiO2 System modified by cerium oxide were conducted using Raman spectroscopy, transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and N-2 absorption (BET specific surface area). The introduction of a minor amount of CeO2 (Ce0.09Ti0.82O1.91CU0.09 sample) resulted in a material with the maximum surface area value. The results of Raman spectroscopy revealed the presence of only two crystalline phases, TiO2 anatase and CeO2 cerianite, with well-dispersed copper species. TEM micrographs showed a trend toward smaller TiO2 crystallites when the cerium oxide content was increased. The XPS analysis indicated the rise of a second peak in Ti 2p spectra with the increasing amount of CeO2 located at higher binding energies than that due to the Till in a tetragonal symmetry. The CuO/TiO2 system modified by CeO2 displayed a superior performance for methanol dehydrogenation than the copper catalyst supported only on TiO2 or CeO2.

X-ray photoelectron spectroscopy, x-ray absorption spectroscopy, and x-ray diffraction characterization of CuO-TiO2-CeO2 catalyst system

X-ray photoelectron spectroscopy (XPS), x-ray diffraction (XRD), and x-ray absorption spectroscopy (XAS) techniques have been applied to characterize the surface composition and structure of a series of CuO-TiO2-CeO2 catalysts. For a small loading of cerium, ceria was mainly dispersed on the titania surface and a minor amount of CeO2 crystallite appeared. At higher loading of cerium, the CeO2 phase increased and the atomic Ce/Ti ratio values were smaller than the nominal composition, as a consequence of cerium agglomeration. This result suggests that only a fraction of cerium can be spread on the titania surface. For titanium-based mixed oxide, we observed that cerium is found as Ce3+ uniquely on the surface. The atomic Cu/(Ce+Ti) ratio values showed no influence from cerium concentration on the dispersion of copper, although the copper on the surface was shown to be dependent on the cerium species. For samples with a high amount of cerium, XPS analysis indicated the raise of second titanium species due cerium with spin-orbit components at higher binding energies than those presented by Ti4+ in a tetragonal structure. The structural results obtained by XAS are consistent with those obtained by XRD and XPS. (C) 2001 American Vacuum Society.

Síntese e caracterização textural do catalisador CeO2/TiO2 obtido via sol-gel: fotocatálise do composto modelo hidrogenoftalato de potássio

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of the substitution of Y2O3 for CeO2 on the mechanical and microstructural properties of silicon nitride

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Si3N4 ceramic cutting tool sintered with CeO2 and Al2O3 additives with AlCrN coating

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and sintering of ZrO2-CeO2 powder by use of polymeric precursor based on Pechini process

Nanocrystalline ZrO2-12 mol % CeO2 powders were synthesized using a polymeric precursor method based on the Pechini process. X-ray diffraction (XRD) patterns showed that the method was effective to synthesize tetragonal zirconia single-phase. The mean crystallite size attained ranges from 6 to 15 nm. The BET surface areas were relatively high reaching 97 m(2)/g. Studies by nitrogen adsorption/desorption on powders, dilatometry of the compacts, and transmission electron microscopy (TEM) of the powders, were also developed to verify the particles agglomeration state. Both citric acid : ethylene glycol ratio and calcination temperature affected the powder morphology, which influenced the sinterability and microstructure of the sintered material, as showed by scanning electron microscopy (SEM). (C) 2001 Kluwer Academic Publishers.

Room temperature co-precipitation of nanocrystalline CeO2 and Ce0.8Gd0.2O1.9-delta powder

This paper describes a simple method to co-precipitate CeO2 and Ce0.8Gd0.2O1.9-delta with ammonium hydroxide from solvents such as: water, ethylene glycol, ethyl alcohol and isopropyl alcohol. Characterization by Raman spectroscopy and XRD evidenced the formation of a solid solution of gadolinium-doped ceria at room temperature. Nanometric particles with crystallite size of 3.1 nm were obtained during synthesis using ethyl alcohol as solvent. This is a promising result compared with those mentioned in the literature, in which the smallest crystallite size reported was, 6.5 nm. (c) 2006 Elsevier B.V. All rights reserved.

Influence of La2O3, Pr2O3 and CeO2 on the nonlinear properties of SnO2 multicomponent varistors

The influence of La2O3, Pr2O3 and CeO2 on a new class of polycrystalline ceramics with nonlinear properties based on SnO2, was investigated. La2O3 and Pr2O3 were found to precipitate at the grain boundary region, causing a considerable increase in the nonlinear behavior. It was found that CeO2 forms a solid solution in the bulk but. unlike La2O3 and Pr2O3, it does not increase the nonlinear behavior. A higher nonlinear coefficient of similar to80 was obtained for La2O3-doped SnO2-based systems. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Characterization of an all sol-gel electrochromic device WO3/Ormolyte/CeO2-TiO2

Electrochemical lithium intercalation in thin films of CeO2-TiO2 and WO3, prepared by the sol-gel technique was investigated with cyclic voltammetry and spectroelectrochemical techniques in propylene carbonate solutions. A solid state system having the configuration WO3/Ormolyte/CeO2-TiO2 has been assembled. The solid electrolyte, an organically modified electrolyte (ormolyte), was prepared with different [O]/[Li] ratios. The transmittance variation of this system during a potentiostatic step from -0.7 V to 0.8 V was about 35% at 550 nm.

CeO2 nanoparticles synthesized by a microwave-assisted hydrothermal method: evolution from nanospheres to nanorods

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation of CeO2 by a simple microwave-hydrothermal method

Cerium carbonate hydroxide (orthorhombic Ce(OH)CO3) hexagonal-shaped microplates were synthesized by a simple and fast microwave-hydrothermal method at 150 degrees C for 30 min. Cerium nitrate, urea and cetyltrimethylammonium bromide were used as precursors. Ceria (cubic CeO2) rhombus-shape was obtained by a thermal decomposition oxidation process at 500 degrees C for 1 h using as- synthesized Ce(OH)CO3. The products were characterized by X-ray powder diffraction, field-emission scanning electron microscopy, thermogravimetric analysis and Fourier transformed infrared spectroscopy. The use of microwave-hydrothermal method allowed to obtain cerium compounds at low temperature and shorter time compared to other synthesis methods. (C) 2008 Elsevier B.V. All rights reserved.

Synthesis of PTSH-modified CeO2 nanoparticles: Effect of the modifier on structure, optical properties, and dispersibility

CeO2 nanoparticles were synthesized by the precipitation method and modified with para-toluene sulfonic acid (PTSH), either in situ or post-synthesis. The presence of PTSH in the samples was confirmed by FTIR. PXRD and FTIR analyses showed that the post-synthesis PTSH modification altered the CeO2 structure, whereas the in situ modification maintained intact the crystalline structure and UV-vis absorbance properties. For both in situ and post-synthesis modifications, TEM images revealed the presence of nanoparticles that were 5nm in size. The dispersibility of the in situ PTSH-modified material in a hydrophilic ureasil-poly(ethylene oxide) matrix was investigated using SAXS measurements, which indicated that CeO2 nanoparticles modified with PTSH in situ were less aggregated within the matrix, compared to unmodified CeO2 nanoparticles. © 2013 Elsevier B.V.

Caracterização de sistemas vítreos baseados no formador B2O3 e P2O5 dopados com CeO2

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo das propriedades óticas e fotoluminescentes das nanopartículas do CeO2 modificadas com La pelo método hidrotermal assistido por microondas

Pós-graduação em Engenharia Mecânica - FEG

Influence of solvent on the morphology and photocatalytic properties of ZnS decorated CeO2 nanoparticles

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)