Analyses of fatigue data in 4340 high strength steel after cadmium electroplating

Bending fatigue tests were carried out to clarify the effects of heat treatment parameters: temperature and time after cadmium electroplating on a high strength steel, to avoid hydrogen embrittlement. Temperatures heat of 190 degrees C, 230 degrees C, 250 degrees C and 300 degrees C at 3, 8 and 24 hours together with the base material electroplated, with and without heat treatment, resulted in 14 conditions studied with respect to fatigue behaviour. Statistical data analysis was performed to identify the best combination temperature/time regarding fatigue strength of the ABNT 4340 steel and the results obtained revealed that the fatigue strength depend on temperature/time conditions.

Evaluation on fatigue strength of AISI 4340 steel aluminum coated by electroplating and IVD processes

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of electroplated zinc-nickel alloy coatings on the fatigue strength of AISI 4340 high-strength steel

Recovered substrates have been extensively used in the aerospace field. Cadmium electroplating has been widely applied to promote protective coatings in aeronautical components, resulting in excellent corrosion protection combined with a good performance in cyclic loading. Ecological considerations allied to the increasing demands for corrosion resistance have resulted in the search for possible alternatives. Zinc-nickel (Zn-Ni) alloys have received considerable interest recently, because these coatings show advantages such as a good resistance to white and red rust, high plating rates, and acceptance in the market. In this study, the effect of electroplated Zn-Ni coatings on AISI 4340 high-strength steel was analyzed for rotating bending fatigue strength, corrosion, and adhesion resistance. The compressive residual stress field was measured by x-ray diffraction prior to fatigue tests. Optical microscopy documented coating thickness, adhesion characteristics, and coverage extent for nearly all substrates. Fractured fatigue specimens were investigated using scanning electron microscopy (SEM). Three different Zn-Ni coating thicknesses were tested, and comparisons with the rotating bending fatigue data from electroplated Cd specimens were performed. Experimental results differentiated the effects of the various coatings on the AISI 4340 steel behaviour when submitted to fatigue testing and the influence of coating thickness on the fatigue strength.

Effects of electroplated zinc-nickel alloy coatings on the fatigue strength of AISI 4340 high strength steel

It is well known that fatigue behaviour is an important parameter to be considered in mechanical components subjected to constant and variable amplitude loadings. In combination with corrosion phenomenon, fatigue effects were responsible for proximally 64% of fails that occur in metallic parts of aeronautical accidents in the last 30 years. Recovered substrates have been extensively used in the aerospace field. Cadmium electroplating has been widely applied to promote protective coatings in aeronautical components, resulting in excellent corrosion protection combined with a good performance in cyclic loading. Ecological considerations allied to the increasing demands for corrosion resistance, resulted in the search for possible alternatives. Zinc-nickel alloys received considerable interest recently, since these coatings showed some advantages such as a good resistance to white and red rust, high plating rates and acceptation in the market. In this study the effects of zinc-nickel coatings electroplated on AISI 4340 high strength steel were analysed on rotating bending and axial fatigue strength, corrosion and adhesion resistance. Compressive residual stress field was measured by a X-ray tensometry prior to fatigue tests. Optical microscopy images showed coating thicknesses, adhesion and the existence of an uniform coverage of nearly all substrates. The fractured fatigue specimens were investigated using a scanning electron microscope. Three different zinc-nickel coating thicknesses were tested and comparison with rotating bending fatigue data from specimens cadmium electroplated and heat treated at 190°C for 3, 8 and 24 hours to avoid the diffusion of hydrogen in the substrate, was performed. Experimental results showed effect of coatings on the AISI 4340 steel behaviour when submitted to fatigue testing and the existence of coating thickness influence on the fatigue strength.

Cadmium availability and accumulation by lettuce and rice

Among the toxic elements, Cd has received considerable attention in view of its association with a number of human health problems. The objectives of this study were to evaluate the Cd availability and accumulation in soil, transfer rate and toxicity in lettuce and rice plants grown in a Cd-contaminated Typic Hapludox. Two simultaneous greenhouse experiments with lettuce and rice test plants were conducted in a randomized complete block design with four replications. The treatments consisted of four Cd rates (CdCl2), 0.0; 1.3; 3.0 and 6.0 mg kg(-1), based on the guidelines recommended by the Environmental Agency of the State of São Paulo, Brazil (Cetesb). Higher Cd rates increased extractable Cd (using Mehlich-3, Mehlich-1 and DTPA chemical extractants) and decreased lettuce and rice dry matter yields. However, no visual toxicity symptoms were observed in plants. Mehlich-1, Mehlich-3 and DTPA extractants were effective in predicting soil Cd availability as well as the Cd concentration and accumulation in plant parts. Cadmium concentration in rice remained below the threshold for human consumption established by Brazilian legislation. on the other hand, lettuce Cd concentration in edible parts exceeded the acceptable limit.

Influence of shot peening and hard chromium electroplating on the fatigue strength of 7050-T7451 aluminum alloy

Chromium electrodeposition is a technique for the production of functional coatings on engineering components. These coatings are extensively micro-cracked and present high level of hardness, resistance to corrosion and wear and low coefficient of friction. In this paper the shot peening influence on the fatigue strength of aluminum 7050-T7451 alloy chromium electroplated, was investigated.The shot peening process was carried out to create residual stresses using ceramic and glass shots. A hard chromium electroplated coating of 100 mu m thickness was performed on the base material and the shot peened base material surfaces. S-N curves were obtained in axial and bending fatigue tests and compared with the 7050-T7451 aluminum alloy. In order to study the influence of residual stresses on fatigue life, the behavior of compressive residual stress field was measured by an X-ray tensometry.An increase in the axial fatigue strength of 25% and 50% of ceramic and glass shots, respectively, was observed. The lower performance in fatigue life for ceramic-shot peening may be attributed to higher surface damage, as a consequence of the overpeening intensity performed. However, in bending fatigue the behavior was practically equivalent for both processes. Fracture surface analysis by scanning electron microscopy was used to observe crack origin sites from shot peened and chromium electroplated samples. (C) 2006 Elsevier Ltd. All rights reserved.

The effect of WC-17Co thermal spray coating by HVOF and hard chromium electroplating on the fatigue life and abrasive wear resistance of AISI 4340 high strength steel

One of the most interesting alternatives for replacement of hard chrome plating is tungsten carbide thermal spray coating applied by the high velocity oxy-fuel (HVOF) process which presents a safer, cleaner and less expensive alternative to chromium plating. The objective of this research is to compare the influence of the tungsten carbide-17cobalt (WC- 17Co) coating applied by high velocity oxy fuel (HVOF) process with that of hard-chromium electroplating on the fatigue strength and abrasive wear of AISI 4340 steel.

Attachment of 2,2-bipyridine onto a silica gel for application as a sequestering agent for copper, cadmium and lead ions from an aqueous medium

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Deposition of Lead and Cadmium Released by Cigarette Smoke in Dental Structures and Resin Composite

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Oxidative stress biomarkers and aggressive behavior in fish exposed to aquatic cadmium contamination

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Early Changes Induced by Short-Term Low-Dose Cadmium Exposure in Rat Ventral and Dorsolateral Prostates

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

SPERM QUALITY IN ADULT MALE RATS EXPOSED TO CADMIUM IN UTERO and LACTATION

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The use of the oxidative stress responses as biomarkers in Nile tilapia (Oreochromis niloticus) exposed to in vivo cadmium contamination

Water contaminants have a high potential risk for the health of populations. Protection from toxic effects of environmental water pollutants primarily involves considering the mechanism of low level toxicity and likely biological effects in organisms who live in these polluted waters. The biomarkers assessment of oxidative stress and metabolic alterations to cadmium exposure were evaluated in Nile tilapia, Oreochromis niloticus. The fish were exposed to 0.35, 0.75, 1.5, and 3.0 mg/l concentrations of Cd2+ (CdCl2) in water for 60 days. Fish that survived cadmium exposure showed a metabolic shift and a compensatory development for maintenance of the body weight gain. We observed a decreased glycogen content and decreased glucose uptake in white muscle. Lactate dehydrogenase (LDH) and creatine phosphokinase (CK) activities were also decreased, indicating that the glycolytic capacity was decreased in this tissue. No alterations were observed in total protein content in white muscle due to cadmium exposure suggesting a metabolic shift of carbohydrate metabolism to maintenance of the muscle protein reserve. There was an increase in glucose uptake, CK increased activity, and a clear increase of LDH activity in red muscle of fish with cadmium exposure. Since no alterations were observed in lipoperoxide concentration, while antioxidant enzymes glutathione peroxidase (GSH-Px) and superoxide dismutase (SOD) were changed in the liver and the red and white muscle of fish with cadmium exposure, we can conclude that oxygen free radicals are produced as a mediator of cadmium toxicity. Resistance development is related with increased activities of antioxidant enzymes, which were important in the protection against cadmium damage, inhibiting lipoperoxide formation. (C) 2002 Elsevier B.V. Ltd. All rights reserved.

Effect of alpha-tocopherol on superoxide radical and toxicity of cadmium exposure

Contamination with cadmium compounds poses high potential risk for the health of populations and for this reason the treatment of their toxic effects should urgently be established. The present study was carried out to determine whether or-tocopherol intake can protect tissues against damage induced by cadmium, and to clarify the contribution of superoxide radicals (O-2(-)) in this process. Cadmium chloride was tested for tissue damage by a single intraperitoneal injection of Cd2+ ions (2 mg Kg(-1)). To determine the potential therapeutic effect of Vitamin E, a group of Cd2+-treated rats received a drinking solution of or-tocopherol (40 mg l(-1)) for 15 days. Cadmium induced increased serum creatinine and total lactate dehydrogenase, reflecting renal and cardiac damage. The increased lipoperoxide and decreased Cu-Zn superoxide dismutase levels indicated the generation of superoxide radicals in cadmium-treated rats. Tocopherol induced increased serum high-density lipoprotein and depressed the toxic effects of Ca2+ alone, since creatinine and lactate dehydrogenase determinations were recovered to the control values. Tocopherol decreased lipoperoxide and led the superoxide dismutase activities to approach those of the control values. We concluded that superoxide radicals are produced as mediators of cadmium toxicity. Tocopherol possesses a significant anti-radical activity and inhibits the cadmium effect on superoxide dismutase activity. Tocopherol also protected tissues from the toxic effects of cadmium by a direct antioxidant action which decreased lipoperoxide formation.

Risk assessment of cadmium toxicity on hepatic and renal tissues of rats

Pollution and industrial practices result in concentrations of metals and other environmental agents that are related to environmental toxicity. A rat bioassay was utilized for the identification of toxic effects of cadmium intake. This demonstrated increased total urinary proteins and increased kidney weights in rats exposed to CdCl2, for 7 days, in drinking water (100 mg/L). Serum creatinine, total and direct bilirubin concentrations and alanine transaminase activity were increased in Cd-exposed rats, indicating renal and hepatic toxicity. It was also observed that lipoperoxide concentrations were increased, while Cu-Zn superoxide dismutase activity was decreased in rats treated with cadmium. This indicated that the renal and hepatic toxicity induced by cadmium involved superoxide radicals. (C) 1998 Academic Press.