The influence of the synthesis route on the final properties of SnO2-based varistors

A comparative study of two customary routes of ceramics processing applied to the synthesis of SnO2-based varistors is reported in this paper. Devices of equivalent composition were prepared through the Pechini method and through directly mixing the oxides without the addition of anti-agglomerants or binders. The microstructures of the sintered samples were characterised with X-ray diffraction and scanning and transmission electron microscopies. The electrical behaviour of the devices was studied on the basis of the current density versus electric field (J-E) characteristics and impedance spectroscopy measurements. The Pechini method ensures the homogeneity in the distribution of the additives in the tin oxide matrix but the formation of secondary phases seems to be independent of the synthesis route. Devices with similar non-linear coefficients of 18 and 21 were obtained through the mixed oxides route and the Pechini method, respectively. (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Nucleation kinetics of crystalline phases from a kaolinitic body used in the processing of red ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Y-TZP ceramic processing from coprecipitated powders: A comparative study with three commercial dental ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of processing route on the phase formation and properties of Bi4Ti3O12 ceramics

Our efforts were directed to the preparation of bismuth titanate-Bi4Ti3O12 (BIT) by two procedures: mechanically assisted synthesis and polymeric precursor method to display a variety of their advantages. To follow the nucleation and phase formation of BIT, XRD and Rietveld refinement analysis were used and it was shown that Bi4Ti3O12 ceramic can been successfully prepared from nano-sized powders obtained by both methods. The ferroelectric properties were determined and the loops from BIT obtained by polymeric precursor method were not fully saturated with a remnant polarization of 20 mu C/cm(2) and coercitive field of 1500 kV/cm. BIT obtained from powders prepared by mechanically assisted synthesis shows a remnant polarization of 0.65 mu C/cm(2) and coercitive field of 1050 kV/cm. The grain morphology may be the factor causing the observed differences. (C) 2005 Published by Elsevier Ltd and Techna Group S.r.l.

Fractal characterization of brittle fracture in ceramics under mode I stress loading

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Sintering of tin oxide and its applications in electronics and processing of high purity optical glasses

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of powder preparation and sintering procedure on microstructure and dielectric properties of PLZT ceramics

PLZT ceramics belong to one of the very important groups of functional materials that make a basis for the production of a large range of electronic devices. The microstructure and properties of ceramics depend on the powder preparation and thermal processing conditions. Various techniques have been used to obtain chemically homogeneous and fine starting powders. PLZT powders have been prepared by two different production routes: by a modified Pechini method, using a polymeric precursor method (PMM) and by a partial oxalate method. A two-step sintering process, including a hot pressing, was carried out at 1100 and 1200degreesC Distinct phases obtained during the sintering process have been investigated by SEM and EDS techniques and dielectric properties such as permittivity and dielectric loss were measured in a frequency range from 1 to 20 kHz.. A significant difference in microstructure and dielectric properties, depending on powder origin and sintering procedure, has been noticed.

PZT ceramics obtained from mechanochemically synthesized powders

PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability. (C) 2003 Kluwer Academic Publishers.

Dielectric and piezoelectric properties of the mechanochemically prepared PZT ceramics

Mechanochemical synthesis was applied to obtain nanocrystalline powders of composition Pb(Zr0.52Ti0.48)O-3 (PZT). Milling was performed in a planetary ball mill using vials and balls made of zirconia or steel-in order to investigate influence of milling media on the electrical properties of resulting ceramics. PZT ceramics showed high values for dielectric constant (epsilon(r)), reaching 970 at room temperature, as well as low dielectric loss (tandelta) under the optimal processing conditions. High values of remanent polarization (P-r) indicate high internal polarizability. The best samples showed piezoelectric strain constant d(33) = 347 pC/N and planar coupling factor k(P) = 0.44. Milling in ZrO2 medium prevents powder contamination and provides reproducibility of milling process. Also, PZT obtained from the powders milled in ZrO2 exhibited lower values of dielectric loss, in comparison with the PTZ obtained from the powders milled in Fe. This suggests that contamination of the powder with Fe could result in an increase of conductivity in final product. (C) 2004 Kluwer Academic Publishers.

Structure, microstructure and dielectric properties of 100-x(Bi0.5Na0.5)TiO3-x[SrTiO3] composites ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microstructure of ceramics TiO2 obtained by protein consolidation

Porous ceramics can be produced by adding starch (corn, potato) and protein (animal or vegetable) to raw material as pore forming element. In this study, titanium dioxide ceramics were formed by vegetable protein consolidation. Soybean was chosen as the binding agent and pore forming. The samples, which were produced in cylindrical shape, had the following processing: material mixture, gelling, drying, pre-sintering and sintering. Heated platinum microscopy were performed by using suspensions with different compositions in order to verify protein gelling capacity and better know the temperature in which this process occurs. The samples were characterized by apparent porosity and roughness measurement. Besides, imaging by light microscopy was also performed in order to determine the sample morphology and porosity. © (2012) Trans Tech Publications, Switzerland.

Effects of thickness, processing technique, and cooling rate protocol on the flexural strength of a bilayer ceramic system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Lead-free BaBi4Ti4O15 ceramics: Effect of synthesis methods on phase formation and electrical properties

The processing of ferroelectric BaBi4Ti4O15 (BBT) ceramics from powders prepared by conventional solid state reaction (SSR) and mechanochemical activation (MA) has been investigated. It was shown that MA synthesis reduces the synthesis temperature of BBT powders, leading to smaller particles with reduced anisotropy and consequently to smaller grain size of ceramics. Dielectric properties were investigated in a wide range of temperatures (20-800 degrees C) and frequencies (1.21 kHz to 1 MHz). The relative dielectric permittivity at Curie temperature was higher for solid state obtained ceramics than for the mechanically treated ones. The conductivity of sintered samples was studied, suggesting decreasing of conductivity of BBT-MA in comparison with BBT-SS ceramics. The influence of the grain and the grain boundaries contribution to the dielectric behavior in both ceramics was analyzed through impedance spectroscopy. A well-defined ferroelectric hysteresis loop was obtained for both samples. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Piezoresponse force microscopy behaviour of Bi4Ti3O12 ceramics with various excess bismuth

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of oxidizing and reducing atmospheres on Ba(Ti0.90 Zr0.10)O3:2V ceramics as characterized by piezoresponse force microscopy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)