Marginal adaptation of class II cavities restored with bulk-fill composites

Objectives: To determine the marginal adaptation of bulk-fill composites in class II MO cavities.Methods: Standardized class II MO cavities with bevelled enamel margins were prepared in 40 extracted human molars. The teeth were randomly assigned to one of the five experimental groups (n = 8). The teeth were restored with two horizontal increments of composite (4 mm and 2 mm thickness). The experimental groups were (1st/2nd increment): Gr. A - Venus Bulk-Fill/Venus Diamond; Gr. B - Tetric EvoCeram BulkFill/Tetric EvoCeram; Gr. C - Surefil SDR/Ceram-X; Gr. D - SonicFill; Gr. E - Ceram-X/Ceram-X (control). After finishing procedures, impressions were made using a polyvinyl siloxane and epoxy resin replicas were obtained. Thermo-mechanical stressing was carried out 24 h after the restorative procedure. All specimens were submitted to 240,000 occlusal loading and simultaneous 600 thermal cycles in water at 5 degrees C and 50 degrees C. After loading, a new set of epoxy resin replicas was obtained. Scanning electron microscopy was carried out at 200x magnification. Results for the marginal adaptation were expressed as percentages of continuity relative to the exposed interface and analyzed by ANOVA and Duncan post hoc test (p < 0.05).Results: In enamel, no significant differences were detected before and after thermo-mechanical loading between groups. In dentine, the worst results were observed in Gr. A.Conclusion: By applying simple layering techniques, bulk-fill materials do not allow better marginal adaptation than a standard composite. Clinical significance: A new class of resin-base composite (bulk-fill) was recently launched on the market. The bulk-fill composites exhibited adequate marginal adaptation and similar to the results of the standard composite. (C) 2014 Elsevier Ltd. All rights reserved.

Discrepâncias de assentamento ocorrido em coroas totais metálicas, com e sem alívio interno, variando-se os términos cervicais e os agentes cimentantes

Pós-graduação em Odontologia Restauradora - ICT

Avaliação do selamento de ápices radiculares retrobturados ou recobertos com diferentes materiais mediante infiltração marginal por corante e análise da interface em microscopia eletrônica de varredura

The purpose of this study was to evaluate the apical sealing ability and the marginal adaptation of five dental materials used in retrofillings or applied to the bevelled root surface. One hundred and forty extracted single rooted human teeth were used, divided into seven groups of twenty each. ln the first, second, third and fourth groups, the teeth were apicoectomized, submitted to cavity preparations and retrofilled with one of the following materiais: zinc free silver amalgam, a dentin bonding system plus composite resin, a glass ionomer cement ora compomer. In the fifth, sixth and seventh groups, the teeth were apicoectomized and capped on the bevelled root surface with one of the following materiais: a dentin bonding system plus composite resin, a glass ionomer cement or a compomer. Two specimens of each experimental group were evaluated for the marginal adaptation using scanning electron microscopy. The remaining 126 specimens were immersed in 2% methylene blue dye, stored for one week at 37ºC and the infiltration was evaluated with a stereomicroscope. The results showed that the glass ionomer cement presented the lowest values of marginal infiltration when used as retrofilling material, with a significant statistical difference when compared with the others tested materials. When used as apical capping, the glass ionomer cement and the compomer were equivalent and significantly better than the dentin bonding system plus composite resin. Using scanning electron microscopy, all the materials showed some slight adjustment problem. ln the retrofilling, the smallest marginal gaps were observed with the compomer and the dentin bonding system plus composite resin, while the largest were observed with the glass ionomer cement and zinc free silver amalgam. ln the apical capping, the smallest marginal gaps were observed with the compomer and the dentin bonding system plus composite resin and ...