This paper discusses the results of biodegradability tests of natural fibers used by the automotive industry, namely: coir, coir with latex, and sisal. The biodegradation of coir, coir with latex, and of sisal fibers was determined by monitoring the production of carbon dioxide (CO(2)) (IBAMA-E.1.1.2, 1988) and fungal growth (DIN 53739, 1984). The contents of total extractives, lignin, holocellulose, ashes, carbon, nitrogen and hydrogen of the fibers under study were determined in order to ascertain their actual content and to understand the results of the biodegradation tests. The production of CO(2) indicated low biodegradation, i.e., about 10% in mass, for all the materials after 45 days of testing; in other words, no material inhibited glucose degradation. However, the percentage of sisal fiber degradation was fourfold higher than that of coir with latex in the same period of aging. The fungal growth test showed a higher growth rate on sisal fibers, followed by coir without latex. In the case of coir with latex, we believe the fungal growth was not intense, because natural latex produces a bactericide or fungicide for its preservation during bleeding [1]. An evaluation of the materials after 90 days of aging tests revealed breaking of the fibers, particularly sisal and coir without latex, indicating fungal attack and biodegradation processes.

Application of intelligent systems for specification of automotive equipments using LEDs

The advantages offered by the electronic component light emitting diode ( LED) have caused a quick and wide application of this device in replacement of incandescent lights. However, in its combined application, the relationship between the design variables and the desired effect or result is very complex and it becomes difficult to model by conventional techniques. This work consists of the development of a technique, through artificial neural networks, to make possible to obtain the luminous intensity values of brake lights using LEDs from design data. (C) 2005 Elsevier B.V. All rights reserved.

Influência de defeitos e diferentes processos de fabricação nas propriedades mecânicas finais de cerâmicas

Os materiais cerâmicos são atualmente cada vez utilizados como opção na engenharia mundial. Por se tratar de materiais com alta resistência mecânica, possuem muitas aplicações em diversas áreas, como por exemplo a de mancais, a automotiva (sensores, isoladores, catalisadores, pistões, válvulas, revestimentos), a de implantes biocompatíveis (dentário, substituição óssea, válvulas cardíacas), a de produtos sujeitos ao desgaste (guias), a de refratários (revestimento de equipamento bélico, componentes de fornos), a eletrônica, e outras. Nos processos de fabricação da cerâmica há uma gama de fatores que contribuem para as características do produto final. Devido a isso, muitos pesquisadores têm trabalhado no estudo da influência de determinados defeitos e técnicas de produção de cerâmicas nas características do produto final. Este trabalho tem como objetivo fazer uma revisão bibliográfica de recentes artigos que analisam a influência de fatores como velocidade de queima, surgimento de trincas, porosidade, fases cristalinas, e tamanho de partículas, nas propriedades mecânicas finais das cerâmicas. Pode-se concluir que é possível aperfeiçoar o processo de fabricação da cerâmica a fim de promover as melhores propriedades mecânicas possíveis, conhecendo-se fatores prejudiciais e métodos adequados para se obter o melhor produto final.

Development of amorphous carbon protective coatings on poly(vinyl)chloride

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of WC-17Co and WC-10Co-4Cr thermal spray coatings by HVOF on the fatigue and corrosion strength of AISI 4340 steel

It is known that chromium electroplating is related to the reduction in the fatigue strength of base metal. However, chromium results in protection against wear and corrosion combined with chemical resistance and good lubricity. Environmental requirements are an important point to be considered in the search for possible alternatives to hard chrome plating. Aircraft landing gear manufactures are considering WC thermal spray coating applied by the high-velocity oxygen-fuel (HVOF) process an alternative candidate, which shows performance at least comparable to results, obtained for hard chrome plating. The aim of this study is to compare the influence of WC-17Co and WC-10Co-4Cr coatings applied by HVOF process and hard chromium electroplating on the fatigue strength of AISI 4340 steel, with and without shot peening. S-N curves were obtained in axial fatigue test for base material, chromium plated and tungsten carbide coated specimens. Tungsten carbide thermal spray coating results in higher fatigue strength when compared to hard chromium electroplated. Shot peening prior to thermal spraying showed to be an excellent alternative to increase fatigue strength of AISI 4340 steel. Experimental data showed higher axial fatigue and corrosion resistance in salt fog exposure for samples WC-10Co-4Cr HVOF coated when compared with WC-17Co. Fracture surface analysis by scanning electron microscopy (SEM) indicated the existence of a uniform coverage of nearly all substrates. (C) 2004 Elsevier B.V. All rights reserved.

Effects of electroplated zinc-nickel alloy coatings on the fatigue strength of AISI 4340 high-strength steel

Recovered substrates have been extensively used in the aerospace field. Cadmium electroplating has been widely applied to promote protective coatings in aeronautical components, resulting in excellent corrosion protection combined with a good performance in cyclic loading. Ecological considerations allied to the increasing demands for corrosion resistance have resulted in the search for possible alternatives. Zinc-nickel (Zn-Ni) alloys have received considerable interest recently, because these coatings show advantages such as a good resistance to white and red rust, high plating rates, and acceptance in the market. In this study, the effect of electroplated Zn-Ni coatings on AISI 4340 high-strength steel was analyzed for rotating bending fatigue strength, corrosion, and adhesion resistance. The compressive residual stress field was measured by x-ray diffraction prior to fatigue tests. Optical microscopy documented coating thickness, adhesion characteristics, and coverage extent for nearly all substrates. Fractured fatigue specimens were investigated using scanning electron microscopy (SEM). Three different Zn-Ni coating thicknesses were tested, and comparisons with the rotating bending fatigue data from electroplated Cd specimens were performed. Experimental results differentiated the effects of the various coatings on the AISI 4340 steel behaviour when submitted to fatigue testing and the influence of coating thickness on the fatigue strength.

An investigation on sliding wear behavior of PVD coatings

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

On the stabilising effect of gyroscopic moments in an automotive turbocharger

Automotive turbochargers, which operate at very high speeds, exceeding 180,000 r/min, exhibit two strong sub-harmonic modes of vibrations due to oil-whirl instability. These are a conical mode and an in-phase whirl mode. The gyroscopic effects can be very important in such a rotor system. This article presents a theoretical investigation into these effects on the conical whirl instability of a turbocharger induced by the angular (tilting) motion of a rigid rotor. A simplified linear model is used to analyse the rotor-bearing system by investigating the effects of the gyroscopic moment on the internal moments. A gyroscopic coefficient, defined by the geometry of the rotor, is shown to govern the stability of the conical whirl motion. A threshold value of 1/2 is determined for this coefficient to suppress the conical whirl. This value remains unaffected if the rotor is asymmetric and is supported by floating ring bearings, which is the case in a practical turbocharger.

Preconcentration and determination of metal ions in commercial ethanol used as fuel for automotive engines

The present investigation reports the synthesis, characterization, and adsorption properties of a new nanomaterial based on organomodified silsesquioxane nanocages. The adsorption isotherms for CuCl,, CoCl2, ZnCl2, NiCl2, and FeCl3 from ethanol solutions were performed by using the batchwise method. The equilibrium condition is reached very quickly (3 min), indicating that the adsorption sites are well exposed. The results obtained in the flow experiments, showed a recovery of ca. 100% of the metal ions adsorbed in a column packed with 2 g of the nanomaterial, using 5 mL of 1.0 mol L-1 HCl solution as eluent. The sorption-desorption of the metal ions made possible the development of a method for preconcentration and determination of metal ions at trace level in commercial ethanol, used as fuel for car engines. The values determined by recommended method for plants 1, 2, and 3 indicated an amount of copper of 51, 60, and 78 mu g L-1, and of iron of 2, 15, and 13 mu g L-1, respectively. These values are very close to those determined by conventional analytical methods. Thus, these similar values demonstrated the accuracy of the determination by recommended method.

High-velocity oxyfuel Cr3C2-NiCr replacing hard chromium coatings

Comparative wear and corrosion properties of Cr3C2-NiCr (CC-TS) (a high-velocity oxyfuel [HVOF]) and hard chromium (HC) coating's obtained on a steel substrate have been studied. The structural characterization was done before and after measurements by optical microscopy, scanning electron microscopy, and scanning white light interferometry. Wear and corrosion properties were evaluated by ball on disk (ASTM G99-90), rubber wheel (ASTM G65-91), and electrochemical measurements of open circuit and polarization curves. The best corrosion and wear resistance was for the CC-TS obtained by HVOF. The open-circuit potential values measured for both samples after 18 h of immersion we're: -0.240 and -0.550 V, respectively, for CC-TS and HC, versus Ag/AgCl,KClsat. Three orders of magnitude lower volume loss were found for CC-TS (HVOF) after friction tests compared with HC.

Influence of spraying parameters on the electrochemical behaviour of HVOF thermally sprayed stainless steel coatings in 3.4% NaCl

Stainless steel coatings obtained by High Velocity Oxygen Fuel (HVOF) were characterized using optical (OM) and scanning electron microscopy (SEM), electron probe micro-analysis, X-ray diffraction (XRD), open-circuit potential (E-OC) measurements, electrochemical impedance spectroscopy (EIS) and polarisation tests. Differences among coated steels were mainly related with the gun-substrate distance parameter (310 nm for samples A and B and 260 min for C and D). The open-circuit potential values measured for all the samples after 18 h of immersion in aerated and unstirred 3.4% NaCl solution were: - 0.334, - 0.360, - 0.379 and - 0.412 V vs. Ag/AgCl,KClsat. for samples A to D, respectively. For EIS measurements, Nyquist plots showed higher capacitive semi-circle for samples sprayed at longer distance, indicating higher corrosion resistance in NaCl solution. (c) 2005 Elsevier B.V. All rights reserved.

The influence of gun transverse speed on electrochemical behaviour of thermally sprayed Cr3C2-NiCr coatings in 0.5 M H2SO4 solution

In the present study, different types of 75% Cr3C2-25% NiCr coatings were applied on a steel substrate by means of high velocity oxygen fuel spraying (HVOF), and studied using ac and dc electrochemical measurements in an aerated and unstirred 0.5 M H2SO4 solution. Structural characterization was determined before and after electrochemical tests. Differences between all sprayed systems are related to the gun transverse speed and number of deposited layers, which strongly affected the electrochemical characteristics of the coated steels. The coating obtained with a higher torch speed showed better resistance against corrosion. The electrochemical impedance results were analyzed using an equivalent circuit where porosity of the coatings and substrate oxidation were considered. (C) 2003 Elsevier Ltd. All rights reserved.

Electrochemical behavior of thermally sprayed stainless steel coatings in 3.4% NaCl solution

Four types of stainless steel coatings prepared by a high velocity oxy-fuel spraying system (HVOF) were studied. Differences among coated steels were related to the spraying parameters, which influenced the behavior of the samples against the corrosion. The electrochemical behavior of the stainless steel coatings was strongly influenced by porosity, the presence of micro- and macro-cracks, and also of un-melted particles. Once the electrolyte reached the steel substrate via these defects, the galvanic pair formed between the coating and substrate-accelerated corrosion, leading to the depletion of the coating. (C) 2004 Elsevier Ltd. All rights reserved.

Effects of thickness coating on the electrochemical behaviour of thermal spray Cr3C2-NiCr coatings

Thermally sprayed HVOF coatings are increasingly being used in industrial applications where high wear and corrosion resistance are needed [1,2]. In this paper, electrochemical ac and de experiments were used in order to obtain the corrosion resistance of coated steel with different numbers of Cr3C2-NiCr layers. This work has been performed in order to determine the role of coating thickness in the corrosion behaviour of a steel protected with cermet thermally sprayed coatings. It is known that a thicker layer protects better against corrosion when a metallic coating is evaluated. But cermet coatings, such as Cr3C2-NiCr, contain higher levels of porosity and residual stresses than metallic coatings, which really could influence the corrosion resistance of the deposited layer. Electrochemical measurements, such as Open-Circuit Potential (E-Osubset of), Polarisation Resistance (RP) and Cyclic Voltammetry (CV), were performed in an aerated 3.4 NaCI media (%wt.). Electrochemical Impedance Measurements (EIS) were also done in order to obtain a mechanism that explains the corrosion process. Structural Characterisation was carried out by means of Optical and Scanning Electron Microscopes (OM, SEM) with an Energy Dispersive Spectrometry analyser (EDS). Results show that the corrosion resistance of the complete system is mainly influenced by the substrate behaviour. The application of a higher number of deposited layers did not substantially increase their anticorrosive properties. Stress generation during the spraying deposition process plays an important role in the behaviour of the coated steel against corrosion phenomena. (C) 2002 Elsevier B.V. B.V All rights reserved.

Electrochemical behaviour of thermally sprayed Cr3C2-NiCr coatings in 0.5 M H2SO4 media

The electrochemical behaviour of coated Cr3C2-NiCr steel in aerated 0.5 M H2SO4 solution was studied by means of electrochemical a.c. and d.c. measurements. A complete structural characterization of the coated steel before and after electrochemical tests was also carried out to access the corrosion mechanism of coated steel, electrolyte penetration through the coating, and to confirm the results obtained using electrochemical techniques. Two types of Cr3C2-NiCr coatings produced by a high velocity oxy-fuel spraying system (HVOF) were studied. Differences between coated steels are related to the spraying parameters reflecting their behaviour against corrosion phenomena. The electrochemical behaviour of the coated steel was strongly influenced by porosity and the presence of microcracks in the coating. Once the electrolyte reaches the steel substrate, it corrodes in a galvanic manner resulting in coating detachment from the steel.