Silicon carbide surface modification by nitrogen plasma expander

Silicon carbide (SiC) has been employed in many different fields such as ballistic armor, thermal coating, high performance mirror substrate, semiconductors devices, among other things. Plasma application over the silicon carbide ceramics is relatively recent and it is able to promote relevant superficial modifications. Plasma expander was used in this work which was supplied by nitrogen and switched by a capacitor bank. Nitrogen plasma was applied over ceramic samples for 20 minutes, in a total medium of 1440 plasma pulses. SiC ceramics were produced by uniaxial pressing method (40 MPa) associated to isostatic pressing (300 MPa) and sintered at 1950 degrees C under argon gas atmosphere. Silicon carbide (beta-sic - BF-12) supplied by HC-Starck and sintering additive (7.6% YAG - Yttrium Aluminum Garnet) were used in order to obtain the ceramics. Before and after the plasma application, the samples were characterized by SEM, AFM, contact angle and surface energy measurement.

Estudo dos sistemas integrados de filmes finos óxidos em substratos poliméricos

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influência da potência de laser Nd: YAG na soldagem do aço inoxidável duplex UNS S32205

Pós-graduação em Engenharia Mecânica - FEIS

Jato de plasma frio em pressão atmosférica para tratamento de materiais e esterilização

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Low-temperature plasma: an effective approach against Candida albicans biofilm

This study evaluated the antifungal potential of low-temperature plasma (LTP) on a 72-hour Candida albicans biofilm. A growth inhibition zone test was conducted with agar plates inoculated with C. albicans and submitted to LTP and argon application at 3 and 10 mm for 10, 30, 60, 90, and 120 seconds. The groups for biofilm assays were 60 seconds of LTP application with a tip-to-sample distance of 3 mm (LTP-3) and 10 mm (LTP-10); –application of only argon gas for 60 seconds with a tip-to-sample distance of 3 mm (Ar-3) and 10 mm (Ar-10); and no treatment. The C. albicans biofilm was grown on saliva-coated discs. The medium was replaced every 24 hours. Confocal laser scanning microscopy revealed the proportion of live and dead cells, and variable pressure scanning electron microscopy (VPSEM) showed biofilm/cell structure. No inhibition zone was observed for control and either Ar groups. For the LTP groups, a progressively increasing of inhibition zone diameter was observed for different treatment durations. The LTP-3 and LTP-10 groups presented higher proportions of dead cells compared with the Ar-3 and Ar-10 groups. VPSEM revealed cell perforations in the LTP-3 and LTP-10 groups. A short period of LTP exposure demonstrated an antifungal effect on C. albicans biofilm.

Caracterização de Filmes a-C:H:Cl e a-C:H:Si:Cl produzidos por deposição à vapor químico assistido por plasma (PECVD) e deposição e implantação iônica por imersão em plasma (PIIID)

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Investigação das propriedades ópticas de ZnO e ZnO:Al

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Avaliação da resistência à corrosão da liga Ti-30Ta submetida a diferentes taxas de deformação visando aplicações biomédicas

This study aims to evaluate the corrosion resistance of Ti-30Ta alloy when subjected to different strain rates. Samples of the alloy Ti-30Ta were obtained from the melting of pure elements in the arc furnace in inert atmosphere (argon gas). Then, the samples were subjected to a thermal treatment and to cold worked to obtain bars. After forging, the samples were machined in accordance with ASTME9-09 standard for carried out compression tests. To microstructural characterization, samples were sectioned longitudinal and transversally and embedded in resin. After, the wet sanding and polishing were performed, followed by a chemical attack, in order to study the microstructure under an optical microscope. Microhardness was measured on the samples that were subjected to microstructural characterization by using microhardness tester. Phases were evaluated by x-rays diffraction. Corrosion tests were carried out to evaluate the influence of deformation on the corrosion resistance. Results show that microstructure was not influenced by deformation

Osseointegration assessment of chairside argon-based nonthermal plasma-treated Ca-P coated dental implants

This study investigated the effect of an Argon-based nonthermal plasma (NTP) surface treatment-operated chairside at atmospheric pressure conditions applied immediately prior to dental implant placement in a canine model. Surfaces investigated comprised: Calcium-Phosphate (CaP) and CaP + NTP (CaP-Plasma). Surface energy was characterized by the Owens-Wendt-Rabel-Kaelble method and chemistry by X-ray photoelectron spectroscopy (XPS). Six adult beagles dogs received 2 plateau-root form implants (n = 1 each surface) in each radii, providing implants that remained 1 and 3 weeks in vivo. Histometric parameters assessed were bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). Statistical analysis was performed by Kruskall-Wallis (95% level of significance) and Dunn's post-hoc test. The XPS analysis showed peaks of Ca, C, O, and P for the CaP and CaP-Plasma surfaces. Both surfaces presented carbon primarily as hydro-carbon (CAC, CAH) with lower levels of oxidized carbon forms. The CaP surface presented atomic percent values of 38, 42, 11, and 7 for C, O, Ca, and P, respectively, and the CaPPlasma presented increases in O, Ca, and P atomic percent levels at 53, 12, and 13, respectively, in addition to a decrease in C content at 18 atomic percent. At 1 week no difference was found in histometric parameters between groups. At 3 weeks significantly higher BIC and BAFO were observed for CaPPlasma treated surfaces. Surface elemental chemistry was modified by the Ar-based NTP. Ar-based NTP improved bone formation around plateau-root form implants at 3 weeks compared with CaP treatment alone. © 2012 Wiley Periodicals, Inc.