Analysis of the bioactive surface of Ti-35Nb-7Zr alloy after alkaline treatment and solution body fluid

The purpose of this work was to evaluate the Ti-35Nb-7Zr experimental alloy after surface treatment and soaking in solution body fluid (SBF) to form bonelike apatite. The Ti-35Nb-7Zr alloy was produced from commercially pure materials (Ti, Nb and Zr) by an arc melting furnace. All ingots were submitted to sequences of heat treatment (1100 °C/2 h and water quenching), cold working by swaging procedures and heat treatment (1100 °C/2 h and water quenching). Discs with 13 mm diameter and 3 mm in thickness were cut. The samples were immersed in NaOH aqueous solution with 5 M at 60 °C for 72 h, washed with distilled water and dried at 40 °C for 24 h. After the alkaline treatment, samples were heat treated in both conditions: at 450 and 600 °C for 1 h in an electrical furnace in air. Then, they were soaking in SBF for 24 h to form an apatite layer on the surface. The surfaces were investigated by using scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), infrared spectroscopy (FTIR) and contact angle measurements. The results indicate that calcium phosphate could form on surface of Ti-35Nb-7Zr experimental alloy. © Springer-Verlag Berlin Heidelberg 2013.

Membranas biológicas homólogas preservadas em solução alcalina seguida de liofilização, glicerina a 98% e por liofilização para implantação em eqüinos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Hidrólise da cana-de-açúcar com cal virgem ou cal hidratada

Objetivou-se estudar o efeito do tratamento alcalino da cana-de-açúcar com cal virgem ou cal hidratada sobre a composição bromatológica e a digestibilidade in vitro da matéria seca, da fibra em detergente neutro e da fibra em detergente ácido. Utilizou-se um delineamento inteiramente casualizado em esquema fatorial 3 × 3, composto de três formas de processamento da cana (in natura; cana hidrolisada com 0,5% de cal virgem; e cana hidrolisada com 0,5% de cal hidratada) e três tempos de armazenamento (12, 36 e 60 horas). As formas de processamento influenciaram os teores de matéria orgânica, matéria mineral, carboidratos totais e hemicelulose, assim como os teores de fibra em detergente neutro e nutrientes digestíveis totais. Os tempos de armazenamento influenciaram os teores de proteína bruta, matéria orgânica, carboidratos totais e hemicelulose. Entre os minerais, somente o teor de cálcio teve aumento com a inclusão de ambos os tipos de cal em relação à cana-de-açúcar, que não sofreu o processo de hidrólise. Os coeficientes de digestibilidade da matéria seca e da fibra em detergente neutro aumentaram com a hidrólise da cana em comparação à cana in natura. A hidrólise com cal hidratada ou com cal virgem mantém o valor nutricional da cana-de-açúcar, permitindo que possa ser utilizada depois de até 60 horas de armazenamento.

Physical properties of pectin-high amylose starch mixtures cross-linked with sodium trimetaphosphate

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

CHEMICAL MODIFICATION EFFECT on THE MECHANICAL PROPERTIES of HIPS/COCONUT FIBER COMPOSITES

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Injectable gels of anionic collagen : rhamsan composites for plastic correction: Preparation, characterization, and rheological properties

The present article describes the preparation and characterization A anionic Collagen gels obtained from porcine intestinal submucosa after 72 h of alkaline treatment and in the form of rhamsan composites to develop injectable biomaterials for plastic for construction. All materials were characterized by SDS/polyacrylamide gel electrophoresis, infrared spectroscopy, thermal stability, potentiometric titration, rheological properties, and fluidity tests. Biocompatibility was appraised after the injection of anionic collagen:rhamsan composites at 2.5% in 60 North Folk rabbits. Independently of processing, the Collagen's secondary structure was preserved in all cases, and after 72 h of hydrolysis the Collagen was characterized by a carboxyl group content of 346 :L 9, which, at physiological pH, corresponds to an increase of 106 17 negative charges, in comparison to native Collagen, due to the selective hydrolysis of asparagine and glutamine carboxyamide side chain. Rheological studies of composites at pH 7.4 in concentrations of 2, 4, and 6% (in proportions of 75:1 and 50:1) showed a viscoelastic behavior dependent on the frequency, which is independent of concentration and proportion. In both, the concentration of the storage modulus always predominated over the loss modulus (G' > G and delta < 45 degrees). The results from creep experiments confirmed this behavior and showed that anionic collagen:rhamsan composites at pH 7.4 in the proportion of 50:1 are less elastic and more susceptible to deformation in comparison to gels in the proportion of 75:1, independent of concentration. This was further confirmed by flow experiments, indicating that the necessary force for the extrusion of anionic collagen:rhamsan composites, in comparison to anionic Collagen, was significantly smaller and with a smooth flow. Biocompatibility studies showed that the tissue reaction of anionic collagen:rhamsan composites at 2.5% in the proportion of 75:1 was compatible with the application of these gels in plastic reconstruction. These results suggest that the association of Collagen with rhamsan may be a good alternative in the replacement of glutaraidehyde to stabilize the microfibril assembly of commercial Collagen gel preparations. (c) 2005 Wiley Periodicals, Inc.

Biomimetic calcium phosphate coating on Ti-7.5Mo alloy for dental application

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Rhodamine B-containing silica films from TEOS precursor: Substrate surface effects detected by photoluminescence

This work presents the study of substrate surface effects on rhodamine B-containing silica films obtained from TEOS (tetraethylorthosilicate) acid hydrolysis. Soda-lime glass substrates were treated with basic solution under different reaction times and temperatures. Rhodamine B-containing silica films were deposited on pre-treated substrates by the spin-coating method. The substrate surface directly affects film morphology and homogeneity. The films are formed by packed silica spheres which protect the dye against acid-base attack. Luminescence spectra present shifts on the dye emission maximum as expected for different pH values on the substrate surface depending on the alkaline treatment. (c) 2006 Elsevier B.V. All rights reserved.

Implants of polyanionic collagen matrix in bone defects of ovariectomized rats

In recent years, there has been a great interest in the development of biomaterials that could be used in the repair of bone defects. Collagen matrix (CM) has the advantage that it can be modified chemically to improve its mechanical properties. The aim of the present study was to evaluate the effect of three-dimensional membranes of native or anionic (submitted to alkaline treatment for 48 or 96 h) collagen matrix on the consolidation of osteoporosis bone fractures resulting from the gonadal hormone alterations caused by ovariectomy in rats subjected to hormone replacement therapy. The animals received the implants 4 months after ovariectomy and were sacrificed 8 weeks after implantation of the membranes into 4-mm wide bone defects created in the distal third of the femur with a surgical bur. Macroscopic analysis revealed the absence of pathological alterations in the implanted areas, suggesting that the material was biocompatible. Microscopic analysis showed a lower amount of bone ingrowth in the areas receiving the native membrane compared to the bone defects filled with the anionic membranes. In ovariectomized animals receiving anionic membranes, a delay in bone regeneration was observed mainly in animals not subjected to hormone replacement therapy. We conclude that anionic membranes treated with alkaline solution for 48 and 96 h presented better results in terms of bone ingrowth.

Desempenho de novilhas de corte alimentadas com cana hidrolisada

The objective of this study was to evaluate the performance, consumption and feed conversion of Angus x Nellore heifers fed hydrolyzed sugarcane. Twenty-four (1/2 Angus x Nellore crossbred) heifers were used with average body weight of 242 kg ± 23 kg, confined in individual pens with total area of 15 m2. The study consisted of six treatments distributed as follows: T1-in natura sugarcane: sugarcane was given to animals after being chopped; T2-hydrolyzed sugarcane with 0.5 % lime and 24 hours of air exposure; T3-hydrolyzed sugarcane with 0.5 % lime and 48 hours of air exposure; T4-hydrolyzed sugarcane with 1.0 % lime and 24 hours of air exposure; T5-hydrolyzed sugarcane with 1.0 % lime and 48 hours of air exposure; T6-hydrolyzed sugarcane with 1.0 % lime and 72 hours of air exposure. We used a completely randomized design with four replicates per treatment, and averages were compared by Tukey test at 5 % significant level of probability. No statistical difference was found for any of the treatments (P>0.05). The processing of sugarcane with lime did not increase the intake and performance of animals evaluated in this study.

Flexible magnetic membranes based on bacterial cellulose and its evaluation as electromagnetic interference shielding material

Flexible magnetic membranes with high proportion of magnetite were successfully prepared by previous impregnation of the never dried bacterial cellulose pellicles with ferric chloride followed by reduction with sodium bisulfite and alkaline treatment for magnetite precipitation. Membranes were characterized by Raman spectroscopy, Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), vibrating magnetometer, field emission scanning electron microscopy (FEG-SEM) and impedance spectroscopy. Microwave properties of these membranes were investigated in the X-band (8.2 to 12.4 GHz). FEG-SEM micrographs show an effective coverage of the BC nanofibers by Fe 3O4 nanoparticles. Membranes with up to 75% in weight of particles have been prepared after 60 min of reaction. Magnetite nanoparticles in the form of aggregates well adhered to the BC fibers were observed by SEM. The average crystal sizes of the magnetic particles were in the range of 10 ± 1 to 13 ± 1 nm (estimated by XRD). The magnetic particles in the BC pellicles presented superparamagnetic behavior with a saturation magnetization in the range of 60 emu g- 1 and coercive force around 15 Oe. These magnetic pellicles also displayed high electrical permittivity and a potential application as microwave absorber materials. © 2013 Elsevier B.V.

Crescimento da nanoapatita na liga Ti-30Ta, para aplicações odontológicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação de superfície bioativa na Liga Ti-7,5Mo para uso em Odontologia

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Diferentes tipos de cales na hidrólise da cana-de-açúcar in natura IAC 86-2480

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Obtenção e processamento de matrizes tridimensionais de colágeno e implantação em parede abdominal de eqüinos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)