Considerations about the welding repair effects on the structural integrity of an airframe critical to the flight-safety

Structures critical to the flight-safety are commonly submitted to several maintenance repairs at the welded joints in order to prolong the in-service life of aircrafts. The aim of this study is to analyze the effects of Tungsten Inert Gas (TIG) welding repair on the structural integrity of the AISI 4130 aeronautical steel by means of experimental fatigue crack growth tests in base-material, heat-affected zone (HAZ) and weld metal. The tests were performed on hot-rolled steel plate specimens, 0.89 mm thick, with load ratio R = 0.1, constant amplitude, at 10 Hz frequency and room temperature. Increase of the fracture resistance was observed in the weld metal but decreasing in the HAZ after repair. The results were associated to microhardness and microstructural changes with the welding sequence. (C) 2010 Published by Elsevier Ltd.

Effects of several TIG weld repairs on the axial fatigue strength of AISI 4130 aeronautical steel-welded joints

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Fatigue strength of tungsten inert gas-repaired weld joints in airplane critical structures

In this work the effect of Gas Tungsten Arc Welding (GTAW) repairs on the axial fatigue strength of an AISI 4130 steel welded joint used in airframe critical to the flight-safety was investigated. Fatigue tests were performed at room temperature on 0.89 mm thick hot-rolled plates with constant amplitude and load ratio of R = 0.1, at 20 Hz frequency. Monotonic tensile tests, optical metallography and microhardness, residual stress and weld geometric factors measurements were also performed. The fatigue strength decreased with the number of GTAW repairs, and was related to microstructural and microhardness changes, as well as residual stress field and weld profile geometry factors, which gave origin to high stress concentration at the weld toe. (C) 2011 Elsevier B.V. All rights reserved.

Analise de tensões através do método dos elementos finitos de um vaso de pressão projetado conforme código ASME

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Análise estrutural e de fadiga de juntas rebitadas de uso aeronaútico utilizando o método dos elementos finitos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fatigue Behavior of Weld Repaired AISI 4130 Aeronautic Steel Used in Critical Flight Safety Structures

Since the 1950s, fatigue is the most important project and operational consideration for both civil and military aircrafts. For some aircraft models the most loaded component is one that supports the motor: the Motor Cradle. Because they are considered critical to the flight safety the aeronautic standards are extremely rigorous in manufacturing them by imposing a zero index of defects on the final weld quality (Safe Life), which is 100% inspected by Non-Destructive Testing/NDT. This study has as objective to evaluate the effects of up to four successive TIG welding repairs on the axial fatigue strength of an AISI 4130 steel. Tests were conducted on hot-rolled steel plate specimens, 0.89 mm thick, with load ratio R = 0.1, constant amplitude, at 20 Hz frequency and in room temperature, in accordance with ASTM E466 Standard. The results were related to microhardness and microstructural and geometric changes resulting from welding cycles.