Effects of substituting ytterbium for scandium on the microstructure and age-hardening behaviour of Al-Sc alloy

In order to reduce the cost of Al-Sc alloys and maintain their mechanical properties, the microstructure and mechanical properties of Al-0.24 wt% Sc-0.07 wt% Yb in comparison with Al-0.28 wt% Sc alloys were studied. The aging behaviour, precipitate morphologies, precipitate coarsening and precipitation hardening of both alloys were investigated. The average diameter and the size distribution of nanoscale Al3Sc and Al-3(Sc,Yb) precipitates at various aging conditions were measured. Transmission electron microscopy (TEM) and high-resolution TEM were used to deeply understand the precipitate evolution. A maximum hardness around 73 (HV30) was obtained with a precipitate diameter from 4.3 to 5.6 nm for both alloys. (c) 2014 Elsevier B.V. All rights reserved.

Influence of the heat treatment in the electrochemical corrosion of Al-Zn-Mg alloys

The localized corrosion of Al-(5.03%)Zn-(1.67%)Mg-(0.23%)Cu alloys and high purity Al has been studied using electrochemical techniques, optical microscopy, SEM and EDX. The samples were previously submitted to different heat treatments in which coherent and incoherent MgZn 2 precipitates with different distribution and aggregation degree were produced. The influence of NaCl and Na 2SO 4, dissolved oxygen, immersion time and convection were studied. In NaCl solutions, pitting potentials for the alloys were more negative than for aluminium, indicating an increase in their susceptibility to localized corrosion. Moreover, annealed and cold-rolled alloys presented more negative pitting and repassivation potentials than those submitted to age hardening with direct or interrupted quenching. In annealed and cold-rolled samples, pit nucleation and propagation takes place in the zones where MgZn 2 is accumulated. In the case of the age-hardened alloys, a double pitting behaviour is observed, the first one in the magnesium and zinc enriched regions and the second in the matrix. While the cold water quenched alloy is susceptible to stress corrosion craking, the alloy submitted to the interrupted quenching process is less susceptible to intergranular attack. The sulphate ion shifts the pitting potential of aluminium and the alloys by chloride towards more positive values because it impedes local accumulations of the latter. © 1992 Chapman & Hall.

Influence of silver additions on the aging characteristics of the Cu-10.4at.%Al alloy

The influence of additions of 1.3, 2.5, 3.8, 5.1, and 6.3 at.% Ag on the aging behavior of the Cu-10.4at.%Al alloy was studied using microhardness measurements, scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) analysis. The results indicated that with silver additions it is possible to obtain a response to age hardening, and that for large aging times there is a decrease in the alloy hardness, with a process that leads to Ag and Al segregation. © 1998 Elsevier Science S.A.

Estudo do comportamento mecânico e microestrutural de um aço maraging após soldagem a laser e tratamentos térmicos

Pós-graduação em Engenharia Mecânica - FEG

Estudo da influência de adições de prata na cinética de precipitação e no comportamento eletroquímico da liga Cu-6%Al

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)