SEM analysis of internal adaptation of adhesive restorations after contamination with saliva

Purpose: This study tested the null hypothesis that different treatments of saliva-contaminated substrate would not affect microgap formation at the dentin walls of bonded restorations. Materials and Methods: Forty freshly extracted human molars received standardized Class V preparations on buccal and lingual surfaces. The specimens were assigned to four experimental groups (n = 20): [G1] no contamination (control group), [G2] saliva contamination (10 s) after etching followed by 5 s air stream; [G3] saliva contamination after etching and rinsed for 10 s; and [G4] re-etching for 10 s after saliva contamination. All specimens were restored with a one-bottle adhesive (Single Bond, 3M ESPE) and microhybrid composite resin (Filtek Z250, 3M ESPE) according to the manufacturer's instructions. The specimens were thermocycled, sectioned through the center of the restoration, and then processed for SEM. Microgaps were measured at the axial wall at 1500X magnification. The data were submitted to Kruskal-Wallis nonparametric statistical analysis at p < 0.05. Results: The data revealed that different groups resulted in a statistically significant difference (p < 0.01) in gap formation. Air drying [G2] and rinsing [G3] the saliva-contaminated dentin resulted in similar microgap values (p > 0.05). However, re-etching the dentin after saliva contamination [G4] increased microgap formation (p < 0.05) when compared with the groups G1 and G2. Although air drying and rinsing produced results comparable to noncontaminated dentin, the presence of microgaps was not completely eliminated. Conclusion: Contaminated saliva did not prevent hybrid layer formation; however, it did reduce the adaptation of the restorative material to bonded surfaces.

Rheological, Mechanical and Adhesive Properties of Surfactant-Containing Systems Designed as a Potential Platform for Topical Drug Delivery

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Loss of samples in the tissue microarray technique: comparison between slides using adhesive tape and silanized slides

The tissue microarray (TMA) technique allows multiple tissue samples in a single block. Commercial adhesive tape is used to avoid the loss of tissue samples during the immunostaining process. Few reports exist in the literature comparing the use of these adhesive tapes to other adhesive techniques. The objective of this study was to compare loss of sections adhered to slides using commercial adhesive tapes versus using silanized only slides. TMA was constructed with varying tissues using a fixed-base device (Beecher Instruments), placing 108 cylinders of 1 mm diameter in duplicate, spaced 1.2 mm apart. Section of 4 mu m were cut from the TMA block and adhered to 30 silanized slides and 30 commercial glass slides using adhesive tape, according to manufacturer's recommendations. Vimentin immunoexpression was evaluated by immunohistochemistry. Antigenic recovery was realized in citrate buffer using a microwave oven. Cylinder loss in the immunohistochemical process was quantified and expressed as: total (>80%), almost complete (75-79%), or partial (50-74%). The commercial adhesive tape group presented lesser total loss (1.1 versus 6.4%), almost complete loss (2.2 versus 3.5%), and partial loss (2.1 versus 3.8%) than the silanized slide group (ANOVA, P < 0.05). The sum of total and almost complete losses in the silanized slide group was 9.9%, greater than the losses in slides using commercial adhesive tapes (3.3%) and less than reported and considered acceptable in the literature (10-30%). In conclusion, the use of silanized only slides presents very satisfactory results, requires less training, and reduces costs significantly, thus justifying their use in research.

Influence of microgap location and configuration on the periimplant bone morphology in submerged implants. An experimental study in dogs

Objectives: The vertical location of the implant-abutment connection influences the periimplant bone morphology. It is unknown, however, whether different microgap configurations cause different bone reactions. Therefore, in this study the bone morphologies of two different implant systems were compared.Material and methods: Three months after tooth extraction in eight mongrel dogs, two grit-blasted screw implants with internal Morse taper connection (ANK group) were placed on one side whereas the contralateral side received two oxidized screw implants with external hex (TIU group). One implant on each side was placed level with the bone (equicrestal), the second implant was inserted 1.5mm below bone level (subcrestal). After 3 months the implants were uncovered. Three months after stage two surgery, histometrical evaluations were performed in order to assess the periimplant bone levels (PBL), the first bone-to-implant contact points (BICP), the width (HBD) and the steepness (SLO) of the bone defect.Results: All implants osseointegrated clinically and histologically. Bone overgrowth of the microgap was seen in ANK implants only. No significant differences between ANK and TIU could be detected in neither vertical position for PBL and BICP. However, a tendency in favor of ANK was visible when the implants were placed subcrestally. In the parameters HBD (ANK equicrestal -0.23mm; TIU equicrestal -0.51mm; ANK subcrestal +0.19mm; TIU subcrestal -0.57mm) and SLO (ANK equicrestal 35.36 degrees; TIU equicrestal 63.22 degrees; ANK subcrestal 20.40 degrees; TIU subcrestal 44.43 degrees) more pronounced and significant differences were noted.Conclusions: Within the limits of this study, it is concluded that different microgap designs cause different shapes and sizes of the periimplant ('dish-shaped') bone defect in submerged implants both in equicrestal and subcrestal positions.

Use of a cyanoacrylate ester adhesive for splinting of replanted teeth

This paper reports a case of tooth replantation in which the splinting was performed with stainless steel orthodontic wire and a widely marketed brand of quick-setting cyanoacrylate ester adhesive (Super Bonder((R))). The long-term clinical and radiographic success of the case reported in this paper indicates that the splinting technique using a quick-setting cyanoacrylate ester adhesive may be a feasible option for making a rapid, simple and efficient contention of replanted teeth in situations where the routinely used materials are not readily available.

Influence of Microgap Location and Configuration on Radiographic Bone Loss Around Submerged Implants: An Experimental Study in Dogs

Purpose: The vertical location of the implant-abutment connection influences the subsequent reaction of the peri-implant bone. It is not known, however, whether any additional influence is exerted by different microgap configurations. Therefore, the radiographic bone reactions of two different implant systems were monitored for 6 months. Materials and Methods: In eight mongrel dogs, two implants with an internal Morse-taper connection (INT group) were placed on one side of the mandible; the contralateral side received two implants with an external-hex connection (EXT group). on each side, one implant was aligned at the bone level (equicrestal) and the second implant was placed 1.5 mm subcrestal. Healing abutments were placed 3 months after submerged healing, and the implants were maintained for another 3 months without prosthetic loading. At implant placement and after 1, 2, 3, 4, 5, and 6 months, standardized radiographs were obtained, and peri-implant bone levels were measured with regard to microgap location and evaluated statistically. Results: All implants osseointegrated clinically and radiographically. The overall mean bone loss was 0.68 +/- 0.59 mm in the equicrestal INT group, 1.32 +/- 0.49 mm in the equicrestal EXT group, 0.76 +/- 0.49 mm in the subcrestal INT group, and 1.88 +/- 0.81 mm in the subcrestal EXT group. The differences between the INT and EXT groups were statistically significant (paired t tests). The first significant differences between the internal and external groups were seen at month 1 in the subcrestal groups and at 3 months in the equicrestal groups. Bone loss was most pronounced in the subcrestal EXT group. Conclusions: Within the limits of this study, different microgap configurations can cause different amounts of bone loss, even before prosthetic loading. Subcrestal placement of a butt-joint microgap design may lead to more pronounced radiographic bone loss. INT J ORAL MAXILLOFAC IMPLANTS 2011;26:941-946

Influence of Microgap Location and Configuration on Radiographic Bone Loss in Nonsubmerged Implants: An Experimental Study in Dogs

Purpose: The implant-abutment connection (microgap) influences the pen-implant bone morphology. However, it is unclear if different microgap configurations additionally modify bone reactions. This preliminary study aimed to radiographically monitor pen-implant bone levels in two different microgap configurations during 3 months of nonsubmerged healing. Materials and Methods: Six dogs received two implants with internal Morse taper connection (INT group) on one side of the mandible and two implants with external-hex connection (EXT group) on the other side. One implant on each side was positioned at bone level (equicrestal); the second implant was inserted 1.5 mm below the bone crest (subcrestal). Healing abutments were attached directly after implant insertion, and the implants were maintained for 3 months without prosthetic loading. At implant placement and 1, 2, and 3 months, standardized radiographs were taken to monitor pen-implant bone levels. Results: All implants osseointegrated. A total bone loss of 0.48 +/- 0.66 mm was measured in the equicrestal INT group, 0.69 +/- 0.43 mm in the equicrestal EXT group, 0.79 +/- 0.93 mm in the subcrestal INT group, and 1.56 +/- 0.53 mm in the subcrestal EXT group (P>.05, paired t tests). Within the four groups, bone loss over time became significantly greater in the EXT groups than in the INT groups. The greatest bone loss was noted in the subcrestal EXT group. Conclusion: Within the limits of this animal study, it seems that even without prosthetic loading, different microgap configurations exhibit different patterns of bone loss during nonsubmerged healing. Subcrestal positioning of an external butt joint microgap may lead to faster radiographic bone loss. Int J Prosthodont 2011;24:445-452.

Influence of Microgap Location and Configuration on Peri-implant Bone Morphology in Nonsubmerged Implants: An Experimental Study in Dogs

Purpose: It is unknown whether different micro gap configurations can cause different pen-implant bone reactions. Therefore, this study sought to compare the peri-implant bone morphologies of two implant systems with different implant-abutment connections. Materials and Methods: Three months after mandibular tooth extractions in six mongrel dogs, two oxidized screw implants with an external-hex connection were inserted (hexed group) on one side, whereas on the contralateral side two grit-blasted screw implants with an internal Morse-taper connection (Morse group) were placed. on each side, one implant was inserted level with the bone (equicrestal) and the second implant was inserted 1.5 mm below the bony crest (subcrestal). Healing abutments were inserted immediately after implant placement. Three months later, the peri-implant bone levels, the first bone-to-implant contact points, and the width and steepness of the peri-implant bone defects were evaluated histometrically. Results: All 24 implants osseointegrated clinically and histologically. No statistically significant differences between the hexed group and Morse group were detected for either the vertical position for peri-implant bone levels (Morse equicrestal -0.16 mm, hexed equicrestal -0.22 mm, Morse subcrestal 1.50 mm, hexed subcrestal 0.94 mm) or for the first bone-to-implant contact points (Morse equicrestal -2.08 mm, hexed equicrestal -0.98 mm, Morse subcrestal -1.26 mm, hexed subcrestal -0.76 mm). For the parameters width (Morse equicrestal -0.15 mm, hexed equicrestal -0.59 mm, Morse subcrestal 0.28 mm, hexed subcrestal -0.70 mm) and steepness (Morse equicrestal 25.27 degree, hexed equicrestal 57.21 degree, Morse subcrestal 15.35 degree, hexed subcrestal 37.97 degree) of the pen-implant defect, highly significant differences were noted between the Morse group and the hexed group. Conclusion: Within the limits of this experiment, it can be concluded that different microgap configurations influence the size and shape of the peri-implant bone defect in nonsubmerged implants placed both at the crest and subcrestally. INT J ORAL MAXILLOFAC IMPLANTS 2010;25:540-547

Management of a complicated crown-root fracture using adhesive fragment reattachment and orthodontic extrusion

Dental trauma is more common in young patients and its sequelae may impair the establishment and accomplishment of an adequate treatment plan. This paper reports a case of complicated crown-root fracture in a young adult that was treated using adhesive tooth fragment reattachment and orthodontic root extrusion. Considering the time elapsed to follow up, the fracture extension, the amount of remaining root portion and the patient's low socioeconomic status, the treatment approach proposed for this case provided good functional and aesthetic outcomes. Clinical and radiographic results after 2 years were successful. This case report demonstrates the importance of establishing a multidisciplinary approach for a successful dental trauma management.

Etch and rinse versus self-etching adhesives systems: Tridimensional micromechanical analysis of dentin/adhesive interface

The purpose of this study was to evaluate stress distribution in the hybrid layer produced by two adhesive systems using three-dimensional finite element analysis (FEA). Four FEA models (M) were developed: Mc, a representation of a dentin specimen (41 x 41 x 82 mu m) restored with composite resin, exhibiting the adhesive layer, hybrid layer (HL), resin tags, peritubular dentin, and intertubular dentin to simulate the etch-and-rinse adhesive system; Mr, similar to Mc, with lateral branches of the adhesive; Ma, similar to Mc, however without resin tags and obliterated tubule orifice, to simulate the environment for the self-etching adhesive system; Mat, similar to Ma, with tags. A numerical simulation was performed to obtain the maximum principal stress (sigma(max)). The highest sigma(max) in the HL was observed for the etch-and-rinse adhesive system. The lateral branches increased the sigma(max) in the HL. The resin tags had a little influence on stress distribution with the self-etching system. (C) 2012 Elsevier Ltd. All rights reserved.

THE EFFECT of DENTIN PRETREATMENT on THE MICROTENSILE BOND STRENGTH of SELF-ADHESIVE RESIN CEMENTS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of different adhesive systems on microleakage in class II composite resin restorations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Short-term in situ/ex vivo study of the anticariogenic potential of a resin-modified glass-ionomer cement associated with adhesive systems

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Hybrid layer thickness and resin tag length of a self-etching adhesive bonded to sound dentin

Objectives: the purpose of this study is to employ optical microscopy to measure the thickness of the hybrid layer and the penetration (tags) of an aggressive self-etching adhesive system into sound dentin.Methods: occtusat cavities were prepared in 40 extracted human posterior teeth. The prepared teeth were randomly assigned to four experimental groups with 10 specimens each. The self-etching adhesive system Adper Prompt L-Pop was applied to the dentin surface as follows: Group 1: cavosurface enamel was etched for 60 s and dentin for 20 s with 35% phosphoric acid get, immediately followed by application of the self -etching adhesive with a brush to the entire cavity for 15 s; Groups 2, 3, and 4: no pre-etching was performed, and the self -etching adhesive was applied to both enamel and dentin for 15, 30 and 45 s, respectively. After curing, the cavities were fitted with composite resin Fittek Z250. Afterwards, the teeth were decalcified and the restorations were carefully removed for later embedding in paraffin. The specimens were serially sectioned at 6 mu m of thickness and sequentially mounted in glass slides. These sections were stained with Brown and Brenn staining for posterior analysis and measurement of the hybrid layer and resin tags on a tight microscope with a micrometric ocular 40/075. The results were submitted to analysis of variance at the 5% level.Results: whenever there was significance, the Tukey test was applied at the 5% level. The specimens receiving application of acid etching before the selfetching. adhesive displayed a larger thickness of the hybrid layer; on the other hand, specimens receiving only application of the self -etching adhesive on dentin for 15, 30 and 45 s exhibited similar thickness of the hybrid layer. As regards the resin tags, no statistically significant differences could be found between the study groups.Conclusions: it could be concluded that the increase in the time of application of the self-etching adhesive Adper Prompt L-Pop did not significantly influence the formation and thickness of hybrid layer, as well as its penetration into the sound dentin surface. (c) 2005 Elsevier Ltd. All rights reserved.

The influence of temperature of three adhesive systems on bonding to ground enamel

This study evaluated the microtensile bond strength test (mu T), micromorphology of resin-enamel interface (RET) and etching patterns (EP) promoted by the etch-and-rinse adhesive, Prime&Bond NT (PB), and two self-etching adhesives, Clearfil SE Bond (SE) and Adper Prompt L-Pop (APR), to ground bovine enamel surfaces' when applied at temperatures of 5 degrees C (C), 40 degrees C (H) and 20 degrees C (R). Materials and Methods. Sixty-three bovine incisors were randomly divided into nine experimental groups (n=7) according to adhesive systems and temperatures. The buccal enamel surfaces were flattened with 600-grit SiC paper and abraded with a diamond bur under water-cooling. The adhesive systems were applied according to the manufacturer's instructions. After the restorative procedures, the specimens were sectioned into five slabs. Four slabs were prepared for mu T and one for interface analysis. For etching pattern analysis, the remaining 16 bovine enamel fragments were used (n=2). The adhesives were applied and the surfaces were rinsed with organic solvents after application. The specimens for RET and EP analysis were prepared for SEM analysis. Results. No significant differences among the adhesives were found at R temperature. However, at 5 degrees C, PB and APR presented lower bond strength than SE. At H temperature, higher bond strength was observed for PB than for APR and SE. At C and H temperature, formation of the interdiffusion zone was impaired and the treated enamel surfaces presented an undefined EP.