New method to assess the pozzolanic reactivity of mineral admixtures by means of pH and electrical conductivity measurements in lime:pozzolan suspensions

A very simple method based on electrical conductivity and pH measurements was proposed for assessing reactivity of pozzolans. Calcium hydroxide: pozzolan water suspensions were monitored by means of measurements of electrical conductivity and pH values. In these suspensions, Ca(OH)(2) in solid state was initially present, being them, thus, saturated in this reagent. Three testing temperatures were selected (40, 50 and 60 degrees C). In the experiments carried out, calcium hydroxide was suspended in deionized water for yielding a lime saturated suspension. The addition of siliceous pozzolan (two types of rice husk ash RHA and two types of densified silica fume DSF were tested) to the saturated lime suspension can produce the unsaturation of the system, depending on the testing time, testing temperature and reactivity of pozzolan. When unsaturation was reached, the loss of electrical conductivity was higher than 30% and the variation of pH was higher than 0.15 units. These threshold values were selected for characterizing the reactivity of pozzolans by means of a proposed template, classifying the pozzolan in three different reactivity levels.

Influência da adição no comportamento reológico da pasta autoadensável de alto desempenho

Influence of admixture on the rheological behavior of high performance self-compacting paste. This research proposes to study the influence of the specific area, mould and surface texture of admixtures on the rheological behavior of high performance self-compacting paste (HPSCP). The selected admixtures are calcareous filler and basalt filler, which are industrial residues, thus contributing to sustainable development. The paste is made up of cement, silica fume, calcareous filler or basalt filler, water and superplasticizer additive. For this study, the water/cement ratios are fixed = 0.40 L kg(-1); silica fume/cement = 0.10 kg kg(-1); the filler/cement and superplasticizer/cement ratios are determined through Marsh cone and mini-slump tests. The results show that for same filler/cement ratios, the ratios of superplasticizer to paste with calcareous filler are significantly lower than those of paste with basalt filler. The results show that the specific area, mould and surface texture of these admixtures significantly influence the rheological behavior of HPSCP.

Estudo dos efeitos do nitrato de lítio na expansão de argamassas sujeitas a reação álcali-sílica

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Determinação de parâmetros reológicos de argamassas e concreto através de técnicas alternativas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)