Evaluation of the radiopacity of calcium hydroxide- and glass-ionomer-based root canal sealers

Aim To evaluate the radiopacity of calcium hydroxide-based root canal sealers (Acroseal, Sealapex and Sealer 26), a glass-ionomer-based sealer (Activ GP Sealer) and a zinc oxide and eugenol-based sealer (Intrafill).Methodology Five disc-shaped specimens (10 x 1 mm) were fabricated from each material, according to the International Organization for Standardization (ISO) 6876/2001 standard. After setting of the materials, radiographs were taken using occlusal films and a graduated aluminum step-wedge varying from 2 to 16 mm in thickness. The dental X-ray unit (GE1000) was set at 50 Kvp, 10 mA, 18 pulses s(-1) and distance of 33.5 cm. The radiographs were digitized and the radiopacity compared with that of the aluminum step-wedge, using WIXWIN-2000 software (Gendex). Data (mm Al) were submitted to ANOVA and Tukey test.Results Intrafill was the most radiopaque material (7.67 mm Al) followed by Sealer 26 (6.33 mm Al), Sealapex (6.05 mm Al) and Acroseal (4.03 mm Al). Activ GP was the least radiopaque material (1.95 mm Al, P < 0.05).Conclusions The sealers evaluated in this study had different radiopacities. However, except for the glass-ionomer-based sealer, all materials had radiopacity values above the minimum recommended by the ISO standard.

Comparative assessment of the flow rate of root canal sealers

OBJETIVO: Este estudo avaliou o escoamento do Acroseal, AH Plus, Endomethasone N, Sealapex e ActiV GP de acordo com a especificação ISO 6876/2001. METODOLOGIA: Um volume de 0,05 mL do cimento manipulado de acordo com as recomendações do fabricante foi colocado numa placa de vidro. Aos 180±5 s após o início da espatulação, uma segunda placa de vidro foi colocada sobre o cimento, seguida por um peso de massa de 100 g para fazer um total de 120±2 g. Dez minutos após o começo da manipulação o peso foi removido e o valor do diâmetro do disco de cimento foi mensurado. A média de 3 mensurações para cada cimento foi tomada como o escoamento do material. Os dados foram comparados estatisticamente pelos testes ANOVA e Tukey. RESULTADOS: Os escoamentos obtidos foram: Acroseal 21.,4 mm, AH Plus 22,72 mm, ActiV GP 24,90 mm, Endomethasone N 18,76 mm e Sealapex 25,15 mm. CONCLUSÃO: Apenas o Endomethasone N não se enquadrou na especificação ISO a qual requer que o cimento tenha um diâmetro não inferior a 20 mm. O Sealapex alcançou o melhor escoamento, mas não foi estatisticamente diferente do Activ GP e AH Plus (P>0,05).

Thermoplasticity of microseal and TC gutta-percha (Tanaka de Castro) and three gutta-percha cones

Aim: The aim of this study was to assess the thermoplasticity of materials used in root canal filling. Methods: Specimens with standardized dimensions were fabricated using Tanari, Roeko and Activ Point gutta-percha cones, as well as Microseal and TC gutta-percha. After 24 hours, the specimens were placed in water at 70 °C for 60 seconds and positioned between two glass slabs. Each set was compressed by a 5 g weight. Digital images of the specimens before and after compression were obtained and analyzed. The thermoplasticity was evaluated based on the difference between the final and initial areas. Data were statistically analyzed using ANOVA and Tukey's tests at a 5% significance level. Results: TC and Microseal gutta-percha presented the highest thermoplasticity (p < 0.05). Among the gutta-percha cones, Tanari and Roeko presented the highest thermoplasticity and differed when compared to Activ Point (p < 0.05). Conclusions: The results of the present study showed that TC and Microseal gutta-percha filling systems present better thermoplastic properties.

Antibiofilm activity, pH and solubility of endodontic sealers

Aim: To evaluate antibiofilm activity against Enterococcus faecalis, pH and solubility of AH Plus, Sealer 26, Epiphany SE, Sealapex, Activ GP, MTA Fillapex (MTA-F) and an experimental MTA-based Sealer (MTA-S). Methodology: Sealer samples were manipulated and stored for 2 or 7 days. Prepared sealers were evaluated by a modified direct contact test (DCT) for 5 h, 10 h or 15 h with biofilm previously induced on bovine dentine for 14 days. In the control group, the biofilm was not exposed to the sealers. The number of colony-forming units (CFU mL-1) in the remaining biofilm was determined. Sealer solubility was assessed by the percentage of mass loss after 15 h of immersion in distilled water. Sealer pH was measured at 5 h, 10 h and 15 h. Statistical analysis was performed using Kruskal-Wallis and Dunn or anova and Tamhane's T2 tests, at 5% significance. Results: At 2 days post-manipulation, the DCT showed that Sealapex and MTA-F were associated with a reduction in the number of bacteria in all 3 contact periods evaluated, compared with the control group (P < 0.05). At 7 days, Sealapex had the greatest antibiofilm action at 10 h and 15 h. Sealapex had the highest pH values 2 and 7 days post-manipulation. Regarding the solubility, at 2 days the highest values were observed for MTA-F, MTA-S, Sealapex and Activ GP (P < 0.05). At 7 days, MTA-S and MTA-F had greater solubility than the other materials (P < 0.05). AH Plus had the lowest solubility for both post-manipulation periods (P < 0.05). Conclusion: Sealapex and MTA-F were associated with a reduction in the number of bacteria in biofilms and had greater solubility. The high solubility and pH may be related to the antibacterial activity of these materials. © 2012 International Endodontic Journal.

Adesividade de cimentos endodônticos às paredes do canal radicular

Pós-graduação em Odontologia - FOAR

Infiltração bacteriana em obturações realizadas com diferentes cimentos endodônticos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação do desenvolvimento de biofilme e da atividade antibiofilme, pH e solubilidade de cimentos endodônticos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Atividade antimicrobiana de cimentos endodônticos

The antimicrobial activity is a fundamental property of root-canal sealers due to persistence of residual microorganisms in the root canal system, even after the chemo-mechanical preparation and using of intracanal dressing. The aim of this study is to review the literature about the antimicrobial properties of some of the main root-canal sealers. Although there is controversy regarding this property, probably due to differences in the methodologies used in the studies, it was concluded that the sealers with the best antimicrobial activity were (in ascending order): Endofill, Ketac Endo, Sealapex, AH Plus, Endo CPM Sealer, Sealer 26 and Epiphany. Activ GP still needs scientific research to evaluate this property.