Pre-resonant Raman effect of CrO2- 4 in a metasilicate glass

Pre-resonant Raman effect of chromate ion, CrO2- 4, was observed in a metasilicate glass with molar composition 2Na2O · 1CaO · 3SiO2 containing 1.0 wt% of Cr2O3. Raman spectra were measured by the conventional 90° scattering geometry and by the microprobe Raman spectroscopic techniques. The presence of chromate ions in the glass is favoured by the glass composition and oxidizing conditions during the glass melting, and they are responsible for optical absorption bands at 370 and 250 nm. Raman spectrum of the undoped glass presents bands at 625, 860 and 980 cm-1, and the presence of chromate ions gives rise to additional bands at 365, 850 and a shoulder at 890 cm-1. An enhancement of the 850 cm-1 Raman band is observed with decreasing laser exciting wavelength. The exciting frequency dependence of the intensity of this band is discussed in terms of theoretical models given in the literature.

Photodegradation of dichloroacetic acid and 2,4-dichlorophenol by ferrioxalate/H2O2 system

The photo-Fenton process using potassium ferrioxalate as a mediator in the photodegradation reaction of organochloride compounds in an aqueous medium was investigated. The influence of parameters such as hydrogen peroxide and ferrioxalate concentrations and initial pH, was evaluated using dichloroacetic acid (DCA) as a model compound under black-light lamp irradiation. An upflow annular photoreactor, operating in a single pass or recirculating mode was used during photodegradation experiments with artificial light. The extent of the release of chloride ions was used to evaluate the photodegradation reaction. The optimum pH range observed was 2.5-2.8. The efficiency of DCA dechlorination increased with increasing concentrations of H2O2 and potassium ferrioxalate, reaching a plateau after the addition of 6 and 1.5 mmol/L of those reagents, respectively. The total organic carbon (TOC) content in DCA and 2,4-dichlorophenol (DCP) solutions was compared with the chloride released after photodegradation. The influence of natural solar light intensity, measured at 365 nm, was evaluated for the dechlorination of DCA on typical summer's days showing a linear dependency. The photodegradation of DCA using black-light lamp and solar irradiation was compared.