Structural evolution of aerogels prepared from TEOS sono-hydrolysis upon heat treatment up to 1100 degrees C

The structural evolution of aerogels prepared from TEOS sono-hydrolysis was studied as a function of the temperature of heat treatment up to 1100 degreesC by means of small angle X-ray scattering (SAXS) and density measurements. The mass fractal structure of the original wet sonogel (with scattering exponent alpha similar to 2.2) apparently transforms to a surface fractal structure in a length scale lesser than similar to1.5 nm, upon the process resulting in aerogel. Such a structural transformation is interpreted by the formation of new particles with characteristic dimension of similar to1.5 nm, with rough boundaries or electronic density fluctuations (or ultra-micropores) in their interior. The structural arrangement of these particles seem to preserve part of mass fractal characteristics of the original wet sonogel, now in a length scale greater than similar to1.5 nm. The electronic density heterogeneities in the particles start to be eliminated at around 800 degreesC and, at 900 degreesC, the particles become perfectly homogeneous, so the structure can be described as a porous structure with a porosity of similar to68% with similar to9.0 nm mean size pores and similar to4.3 nm mean size solid particles. Above 900 degreesC, a vigorous viscous flux sintering process sets in, eliminating most of the porosity and increasing rapidly the bulk density in an aerogel-glass transformation. (C) 2003 Elsevier B.V. All rights reserved.

A SAXS study of the nanostructural characteristics of TEOS-derived sonogels upon heat treatment up to 1100 degrees C

Xerogels obtained from the acid-catalyzed and ultrasound stimulated hydrolysis of TEOS were submitted to heat treatment at temperatures ranging from 60 to 1100 degreesC and studied by small-angle X-ray scattering (SAXS). The SAXS intensity as a function of the modulus of the scattering vector q was obtained in the range from q(0) = 0.19 to q(m) = 4.4 nm(-1). At 60 degreesC the xerogels exhibit an apparent surface fractal structure with a fractal dimension D-s similar to 2.5 in a length scale ranging from 1/q(1) similar to 1 to 1/q(m) similar to 0.22 nm. This structure becomes extremely rough at 120 degreesC (D-s similar to 3) and at 150 degreesC, it apparently converts to a mass fractal with a fractal dimension D similar to 2.4. This may mean an emptying of the pores with preservation of a share of the original mass fractal structure of the wet aged gel, for it had presented a mass fractal dimension D similar to 2.2. A well characterized porous structure formed by 2.0 nm mean size pores with smooth surface of about 380 m(2)/g is formed at 300 degreesC and remains stable until approximately 800 degreesC. At 900 degreesC the SAXS intensity vanishes indicating the disappearance of the pores in the probed length scale. The elimination of the nanopores occurs by a mechanism in which the number of pores diminishes keeping constant their mean size. The xerogels exhibit a foaming phenomenon above 900 degreesC and scatter following Porod's law as does a surface formed by a coarse structure. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Structural evolution up to 1100 degrees C of xerogels prepared from TEOS sonohydrolysis and liquid phase exchanged by acetone

Silica xerogels were prepared from sonohydrolysis of tetraethoxysilane and exchange of the liquid phase of the wet gel by acetone. Monolithic xerogels were obtained by slow evaporation of acetone. The structural characteristics of the xerogels were studied as a function of temperature up to 1100 degrees C by means of bulk and skeletal density measurements, linear shrinkage measurements and thermal analyses (DTA, TG and DL). The results were correlated with the evolution in the UV-Vis absorption. Particularly, the initial pore structure of the dried acetone-exchanged xerogel was studied by small-angle X-ray scattering and nitrogen adsorption. The acetone-exchanged xerogels exhibit greater porosity in the mesopore region presenting greater mean pore size (similar to 4 nm) when compared to non-exchanged xerogels. The porosity of the xerogels is practically stable in the temperature range between 200 degrees C and 800 degrees C. Evolution in the structure of the solid particles (silica network) is the predominant process upon heating up to about 400 degrees C and pore elimination is the predominant process above 900 degrees C. At 1000 degrees C the xerogels are still monolithic and retain about 5 vol.% pores. The xerogels exhibited foaming phenomenon after hold for 10 h at 1100 degrees C. This temperature is even higher than that found for foaming of non-exchanged xerogels. (c) 2005 Elsevier B.V. All rights reserved.

Longitudinal evaluation of fluoride levels in nails of 18-30-month-old children that were using toothpastes with 500 and 1100 mu g F/g

ObjectivesThis study aimed to evaluate the fluoride concentration in the fingernails and toenails of children aged 18-30months during use of fluoride-containing toothpastes supplemented with calcium glycerophosphate (CaGP) or sodium trimetaphosphate (TMP).MethodsAccording to the toothpaste used, children (n=56) were randomly assigned into three groups: 500gF/g with 1% TMP, 500gF/g with 0.25% CaGP, and 1100gF/g. Fingernails and toenails were collected monthly over a period of 330days, from the beginning of toothpaste use. Fluoride concentration in the water consumed by the volunteers and fluoride intake from diet and toothpaste were also determined. Fluoride analyses were performed with the electrode after hexamethyldisiloxane-facilitated diffusion or by the direct method, according to the samples. Data passed normality and homoscedasticity tests and were analyzed by 2-way analysis of variance (anova) and 1-way anova followed by Student-Newman-Keuls test (P<0.05).ResultsFluoride levels in the fingernails and toenails as well as fluoride intake from toothpaste were similar for the groups treated with 500gF/g with 1% TMP and 500gF/g with 0.25% CaGP toothpastes, but significantly lower than the 1100 gF/g group (P<0.05). No significant differences were noted among the groups regarding fluoride intake from diet and that by water consumed by the volunteers (P>0.05).ConclusionThe results of the longitudinal study suggest that the level of fluoride present in nails was lower with the use of toothpastes with a low fluoride concentration.