Peel bond strength of resilient liner modified by the addition of antimicrobial agents to denture base acrylic resin

In order to prolong the clinical longevity of resilient denture relining materials and reduce plaque accumulation, incorporation of antimicrobial agents into these materials has been proposed. However, this addition may affect their properties. Objective: This study evaluated the effect of the addition of antimicrobial agents into one soft liner (Soft Confort, Dencril) on its peel bond strength to one denture base (QC 20, Dentsply). Material and Methods: Acrylic specimens (n=9) were made (75x10x3 mm) and stored in distilled water at 37 degrees C for 48 h. The drug powder concentrations (nystatin 500,000U - G2; nystatin 1,000,000U - G3; miconazole 125 mg - G4; miconazole 250 mg - G5; ketoconazole 100 mg - G6; ketoconazole 200 mg - G7; chlorhexidine diacetate 5% - G8; and 10% chlorhexidine diacetate - G9) were blended with the soft liner powder before the addition of the soft liner liquid. A group (G1) without any drug incorporation was used as control. Specimens (n=9) (75x10x6 mm) were plasticized according to the manufacturers' instructions and stored in distilled water at 37 degrees C for 24 h. Relined specimens were then submitted to a 180-degree peel test at a crosshead speed of 10 mm/min. Data (MPa) were analyzed by analysis of variance (alpha=0.05) and the failure modes were visually classified. Results: No significant difference was found among experimental groups (p=0.148). Cohesive failure located within the resilient material was predominantly observed in all tested groups. Conclusions: Peel bond strength between the denture base and the modified soft liner was not affected by the addition of antimicrobial agents.

Bond strength of adhesive restorations to Er : YAG laser-treated dentin

Background and Objective: evaluate the adhesion of adhesive restorations with and without a base of resin-modified glass-ionomer cement (RMGIC) to dentin irradiated with Er:YAG laser.Study Design/Materials and Methods: Twenty-four human molar teeth were divided into 6 groups (n=4): G1) 37% Phosphoric acid (PA) + Adhesive system (Ad) + Composite resin (CR); G2) RMGIC + CR; G3) Laser (60mJ-5Hz-20s) + PA + Ad + CR; G4) Laser (60 mJ-5 Hz-20 s) + RMGIC + CR; G5) Laser (100mJ-5Hz-20s) + PA + Ad + CR; G6) Laser (100mJ-5Hz-20s) + RMGIC + CR. Teeth were prepared, restored and cut into specimens, according to the treatment proposed and to methodology for microtensile test. Data were submitted to ANOVA and Tukey statistical tests (alpha=5%).Results:. The mean values for adhesion (MPa) and standard deviation (+/- SD) were: G1) 26.30(+/- 4.50), G2) 5.34(+/- 2.87), G3) 21.16(+/- 6.01), G4) 5.22(+/- 1.52), G5) 22.23(+/- 4.98), G6) 5.25(+/- 3.08).Conclusion: the use of Er:YAG laser did not influence on the restorations adhesion.

Influence of Er,Cr: YSGG laser on bond strength of self-adhesive resin cement

The purpose of this study was to investigate the bond strength of fiber post previously laser treated root canals. Forty single-rooted bovine teeth were endodontically treated, randomly and equally divided into two main groups according to the type of pretreatment: G1: 2.5% NaOCl (control group); and G2: Er,Cr:YSGG laser. Each group was further subdivided into 2 groups based on the category of adhesive systems/ luting materials used: a: an etch-and-rinse resin cement (Single Bond/RelyX ARC; 3M ESPE), and b: a self-adhesive resin cement (Rely X Unicem; 3M ESPE). Three 1.5 mm thick slabs were obtained per root and the push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. Data were analyzed by ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. Analysis of variance showed no statistically significant difference (p > 0.05) among the groups G1a (25.44 ± 2.35) and G1b (23.62 ± 3.48), G2a (11.77 ± 2.67) and G2b (9.93 ± 3.37). Fractures were observed at the interface between the dentin and the resin in all groups. The Er,Cr:YSGG laser irradiation did not influence on the bond strength of the resin cements and the etch-and-rinse resin cement had better results on bond strength than self-adhesive resin cement.

Microtensile bond strength of different adhesive systems in dentin irradiated with Er : YAG laser

The objective this study was to evaluate in vitro the bond strength of two etch-and-rise and one self-etching adhesive system after dentin irradiation with Er:YAG (erbium: yttrium aluminum garnet) laser using microtensile test. The results revealed that the groups treated with laser Er:YAG presented less tensile bond strength, independently to the adhesive system used. The prompt L-pop adhesive presented less microtensile bond strength compared to the other adhesives evaluated. There was no difference between single bond and excite groups. The adhesive failures were predominant in all the experimental groups. The Er:YAG laser influenced negatively bond strength values of adhesive systems tested in dental substrate.

Bond strength of an adhesive system irradiated with Nd : YAG laser in dentin treated with Er : YAG laser

The purpose of this in vitro study was to verify through micro tensile bond test the bond strength of an adhesive system irradiated with Nd:YAG laser in dentine previously treated with Er:YAG laser. Twenty caries free extracted human third molars were used. The teeth were divided in four experimental groups (n = 5): (G1) control group; (G2) irradiation of the adhesive system with the Nd:YAG laser; (G3) dentin treatment with Er:YAG laser; (G4) dentin treatment with Er:YAG laser followed by the irradiation of the adhesive system with Nd:YAG laser. The Er:YAG laser fluency parameter for the dentin treatment was of 60 J/cm(2). ne adhesive system was irradiated with the Nd:YAG laser with fluency of 100 J/cm(2). Dental restorations were performed with Adper Single Bond 2/Z250. One tooth from each group was prepared for the evaluation of the adhesive interface under SEM and bond failure tests were also performed and evaluated. The statistical analysis showed statistical significant difference between the groups G1 and G3, G1 and G4, G2 and G3, and G2 and G4; and similarity between the groups G1 and G2, and G3 and G4. The adhesive failures were predominant in all the experimental groups. The SEM analysis showed an adhesive interface with features confirming the results of the mechanical tests. The Nd:YAG laser on the adhesive system did not influence the bond strength in dentin treated or not with the Er:YAG laser.

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS).Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM).Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM.Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

Effect of conditioning methods on the microtensile bond strength of phosphate monomer-based cement on zirconia ceramic in dry and aged conditions

The objective of this study was to evaluate the durability of bond strength between a resin cement and aluminous ceramic submitted to various surface conditioning methods. Twenty-four blocks (5 X 5 X 4 mm 3) of a glass-in filtrated zirconia-alumina ceramic (inCeram Zirconia Classic) were randomly divided into three surface treatment groups: ST1-Air-abrasion with 110-mu m Al2O3 particles + silanization; ST2-Laboratory tribochemical silica coating method (110-mu m Al2O3, ilO-PM Silica) (Rocatec) + silanization; ST3-Chairside tribochemical silica coating method (30-mu m SiOx) (CoJet) + silanization. Each treated ceramic block was placed in its silicone mold with the treated surface exposed. The resin cement (Panavia F) was prepared and injected into the mold over the treated surface. Specimens were sectioned to achieve nontrimmed bar specimens (14 sp/block) that were randomly divided into two conditions: (a) Dry-microtensile test after sectioning; (b) Thermocycling (TC)-(6,000X, 5-55 degrees C) and water storage (150 days). Thus, six experimental groups were obtained (11 = 50): Gr1-ST1 + dry; Gr2-ST1 + TC. Gr3-ST2 + dry; Gr4-ST2 + TC; Gr5-ST3 + dry; Gr6ST3 + TC. After microtensile testing, the failure types were noted. ST2 (25.1 +/- 11) and ST3 (24.1 +/- 7.4) presented statistically higher bond strength (MPa) than that of STI (17.5 +/- 8) regardless of aging conditions (p < 0.0001). While Gr2 revealed the lowest results (13.3 +/- 6.4), the other groups (21.7 +/- 7.4-25. 9 +/- 9.1) showed statistically no significant differences (two-way ANOVA and Tukey's test, a 0.05). The majority of the failures were mixed (82%) followed by adhesive failures (18%). Gr2 presented significantly higher incidence of ADHESIVE failures (54%) than those of other groups (p = 0.0001). Both laboratory and chairside silica coating plus silanization showed durable bond strength. After aging, airabrasion with 110-mu m Al2O3 + silanization showed the largest decrease indicating that aging is fundamental for bond strength testing for acid-resistant Arconia ceramics in order to estimate their long-term performance in the mouth. (c) 2007 Wiley Periodicals, Inc.

INFLUENCE of DIFFERENT SURFACE CONDITIONING PROTOCOLS on MICROTENSILE BOND STRENGTH of SELF-ADHESIVE RESIN CEMENTS TO DENTIN

Statement of problem. According to manufacturers, bonding with self-adhesive resin cements can be achieved without any pretreatment steps such as etching, priming, or bonding. However, the benefit of saving time with these simplified luting systems may be realized at the expense of compromising the bonding capacity.Purpose. The purpose of this study was to assess whether different dentin conditioning protocols influence the bond performance of self-adhesive resin cements to dentin.Material and methods. Flat dentin surfaces from 48 human molars were divided into 4 groups (n=12): 1) control, no conditioning; 2) H(3)PO(4), etching with 37% H(3)PO(4) for 15 seconds; 3) SEBond, bonding with self-etching primer adhesive (Clearfil SE Bond); and 4) EDTA, etching with 0.1M EDTA for 60 seconds. The specimens from each dentin pre-treatment were bonded using the self-adhesive cements RelyX Unicem, Maxcem or Multilink Sprint (n=4). The resin-cement-dentin specimens were stored in water at 37 degrees C for 7 days, and serially sectioned to produce beam specimens of 1.0 mm(2) cross-sectional area. Microtensile bond strength (mu TBS) testing was performed at 1.0 mm/min. Data (MPa) were analyzed by 2-way ANOVA and Tukey multiple comparisons test (alpha=.05). Fractured specimens were examined with a stereomicroscope (x40) and classified as adhesive, mixed, or cohesive. Additional bonded interfaces were evaluated under a scanning electron microscope (SEM).Results. Cement-dentin mu TBS was affected by the dentin conditioning approach (P <.001). RelyX Unicem attained statistically similar bond strengths to all pre-treated dentin surfaces. H(3)PO(4)-etching prior to the application of Maxcem resulted in bond strength values that were significantly higher than the other groups. The lowest mu TBS were attained when luting Multilink Sprint per manufacturers' recommendations, while H(3)PO(4)-etching produced the highest values followed by Clearfil SE bonding and EDTA. SEM observations disclosed an enhanced potential of the self-adhesive cements to form a hybrid layer when applied following manufacturer's instructions.Conclusions. When evaluated self-adhesive resin cements are used, selectively etching dentin with H(3)PO(4) prior to luting results in the most effective bonding. (J Prosthet Dent 2011;105:227-235)

Microshear Bond Strength of Self-etching Bonding Systems to Ultrasound Diamond Bur-prepared Dentin

Purpose: The aim of this study was to evaluate the influence of dentin abrasion on the microshear bond strength of two self-etching adhesive systems, using either an ultrasound diamond bur or a high-speed diamond bur.Materials and Methods: Twenty noncarious human third molars were sectioned mesiodistally into halves. The enamel was ground to expose a flat dentin surface on both sections. The dentinal surfaces were randomly assigned to two groups, depending on the method of smear layer preparation: ultrasound diamond bur (UB) or conventional diamond bur (CB). The prepared dentin surfaces received one of two self-etching systems: Clearfil SE Bond (CF) and One-Up Bond F (OB). A composite cylinder with a 0.95-mm diameter was bonded to each specimen and the microshear bond test was performed. The results were expressed in MPa and were subjected to two-way analysis of variance (ANOVA) and Tukey's test (alpha = 0.05).Results: There was no significant difference in dentin bond strength when comparing the conventional and ultrasonic abrasion methods. When the adhesive systems were compared, Clearfil SE Bond achieved higher bond strength means than did One-Up Bond F.Conclusion: The dentin surface preparation method did not influence the microshear bond strength and the Clearfil SE Bond adhesive system, independent of bur type used, Clearfil SE Bond showed higher bond strengths than did the One-Up Bond F adhesive system.

Resin Bonding to a Feldspar Ceramic After Different Ceramic Surface Conditioning Methods: Evaluation of Contact Angle, Surface pH, and Microtensile Bond Strength Durability

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond Strength of Two Resin Cements on Dentin Using Different Cementation Strategies

Purpose:This study evaluated the microtensile bond strength of two resin cements to dentin either with their corresponding self-etching adhesives or employing the three-step etch-and-rinse technique. The null hypothesis was that the etch-and-rinse adhesive system would generate higher bond strengths than the self-etching adhesives.Materials and Methods:Thirty-two human molars were randomly divided into four groups (N = 32, n = 8/per group): G1) ED Primer self-etching adhesive + Panavia F; G2) All-Bond 2 etch-and-rinse adhesive + Panavia F; G3) Multilink primer A/B self-etching adhesive + Multilink resin cement; G4) All-Bond 2 + Multilink. After cementation of composite resin blocks (5 x 5 x 4 mm), the specimens were stored in water (37 degrees C, 24 hours), and sectioned to obtain beams (+/- 1 mm2 of adhesive area) to be submitted to microtensile test. The data were analyzed using 2-way analysis of variance and Tukey's test (alpha = 0.05).Results:Although the cement type did not significantly affect the results (p = 0.35), a significant effect of the adhesive system (p = 0.0001) was found on the bond strength results. Interaction terms were not significant (p = 0.88751). The etch-and-rinse adhesive provided significantly higher bond strength values (MPa) with both resin cements (G2: 34.4 +/- 10.6; G4: 33.0 +/- 8.9) compared to the self-etching adhesive systems (G1: 19.8 +/- 6.6; G3: 17.8 +/- 7.2) (p < 0.0001). Pretest failures were more frequent in the groups where self-etching systems were used.Conclusion:Although the cement type did not affect the results, there was a significant effect of changing the bonding strategy. The use of the three-step etch-and-rinse adhesive resulted in significantly higher bond strength for both resin cements on dentin.CLINICAL SIGNIFICANCEDual polymerized resin cements tested could deliver higher bond strength to dentin in combination with etch-and-rinse adhesive systems as opposed to their use in combination with self-etching adhesives.(J Esthet Restor Dent 22:262-269, 2010).

Effect of Acid Neutralization and Mechanical Cycling on the Microtensile Bond Strength of Glass-ceramic Inlays

Objectives: To evaluate the hypothesis that a process of hydrofluoric acid precipitate neutralization and fatigue load cycling performed on human premolars restored with ceramic inlays had an influence on microtensile bond strength results (MTBS). Methods: MOD inlay preparations were performed in 40 premolars (with their roots embedded in acrylic resin). Forty ceramic restorations were prepared using glass-ceramic (IPS Empress). The inner surfaces of all the restorations were etched with 10% hydrofluoric acid for 60 seconds, rinsed with water and dried. The specimens were divided into two groups (N=20): 1-without neutralization; 2-with neutralization. All the restorations were silanized and adhesively cemented (self-curing and self-etching luting composite system, Multilink). Ten premolars from each group were submitted to mechanical cycling (1,400,000 cycles, 50N, 37 degrees C). After cycling, the samples were sectioned to produce non-trimmed beam specimens (vestibular dentin-restoration-lingual dentin set), which were submitted to microtensile testing. Results: Bond strength was significantly affected by the surface treatment (p<0.0001) (no neutralization > neutralization) and mechanical cycling (p<0.0001) (control > cycling) (2-way ANOVA and Tukey test, alpha=.05). Conclusion: Hydrofluoric acid precipitate neutralization appears to significantly damage the resin bond to glass-ceramic and should not be recommended. The clinical simulation of the specimens, by using mechanical cycling, is important when evaluating the ceramic-dentin bond.

Effect of adhesive system type and tooth region on the bond strength to dentin

Purpose: This study evaluated the bond strength of two etch-and-rinse adhesive systems (two- and three-step) and a self-etching system to Coronal and root canal dentin.Materials and Methods: The root canals of 30 human incisors and canines were instrumented and prepared with burs. The posts used for luting were duplicated with dual resin cement (Duo-link) inside Aestheti Plus #2 molds. Thus, three groups were formed (n = 10) according to the adhesive system employed: All-Bond 2 (TE3) + resin cement post (rcp) + Duo-link (DI); One-Step Plus (TE2) + rcp + DI; Tyrian/One-Step Plus (SE) + rcp + DI. Afterwards, 8 transverse sections (1.5 mm) were cut from 4 mm above the CEJ up to 4 mm short of the root canal apex, comprising coronal and root canal dentin. The sections were submitted to push-out testing in a universal testing machine EMIC (1 mm/min). Bond strength data were analyzed with two-way repeated measures ANOVA and Tukey's test (p < 0.05).Results: The relationship between the adhesives was not the same in the different regions (p < 0.05). Comparison of the means achieved with the adhesives in each region (Tukey; p < 0.05) revealed that TE3 (mean standard deviation: 5.22 +/- 1.70) was higher than TE2 (2.60 +/- 1.74) and SE (1.68 +/- 1.85).Conclusion: Under the experimental conditions, better bonding to dentin was achieved using the three-step etch-and-rinse system, especially in the coronal region. Therefore, the traditional etch-and-rinse three-step adhesive system seems to be the best choice for teeth needing adhesive endodontic restorations.

Bond strength durability of a resin composite on a reinforced ceramic using various repair systems

Objectives. This study compared the durability of repair bond strength of a resin composite to a reinforced ceramic after three repair systems.Methods. Alumina-reinforced feldspathic ceramic blocks (Vitadur-alpha(R)) (N=30) were randomly divided into three groups according to the repair method: PR-Porcelain Repair Kit (Bisco) [etching with 9.5% hydrofluoric acid + silanization + adhesive]; CJ-CoJet Repair Kit (3M ESPE) [(chairside silica coating with 30 mu m SiO2 + silanization (ESPE(R)-Sil) + adhesive (Visio(TM)-Bond)]; CL-Clearfil Repair Kit [diamond surface roughening, etching with 40% H3PO4 + Clearfil Porcelain Bond Activator + Clearfil SE Bond)]. Resin composite was photo-polymerized on each conditioned ceramic block. Non-trimmed beam specimens were produced for the microtensile bond strength (mu TBS) tests. In order to study the hydrolytic durability of the repair methods, the beam specimens obtained from each block were randomly assigned to two conditions. Half of the specimens were tested either immediately after beam production (Dry) or after long-term water storage (37 degrees C, 150 days) followed by thermocyling (12,000 cycles, 5-55 degrees C) in a universal testing machine (1 mm/min). Failure types were analyzed under an optical microscope and SEM.Results. mu TBS results were significantly affected by the repair method (p=0.0001) and the aging conditions (p=0.0001) (two-way ANOVA, Tukey's test). In dry testing conditions, PR method showed significantly higher (p < 0.001) repair bond strength (19.8 +/- 3.8 MPa) than those of CJ and CL (12.4 +/- 4.7 and 9.9 +/- 2.9, respectively). After long-term water storage and thermocycling, CJ revealed significantly higher results (14.5 +/- 3.1 MPa) than those of PR (12.1 +/- 2.6 MPa) (p < 0.01) and CL (4.2 +/- 2.1 MPa) (p < 0.001). In all groups when tested in dry conditions, cohesive failure in the composite accompanied with adhesive failure at the interface (mixed failures), was frequently observed (76%, 80%, 65% for PR, CJ and CL, respectively). After aging conditions, while the specimens treated with PR and CJ presented primarily mixed failure types (52% and 87%, respectively), CL group presented mainly complete adhesive failures at the interface (70%).Significance. Hydrolytic stability of the repair method based on silica coating and silanization was superior to the other repair strategies for the ceramic tested. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of Carbamide Peroxide Bleaching Gel Concentration on the Bond Strength of Dental Substrates and Resin Composite

Purpose: This study evaluated the effect of bleaching gel containing 10%, 15% and 20% carbamide peroxide (CP) on the bond strength of dental enamel or dentin and resin composite restorations.Methods: The buccal surfaces of 12 bovine tooth crowns were conditioned with 37% phosphoric acid, and the adhesive resin Single Bond 2 and the resin composite Filtek Z350 were used to perform the restorations. The blocks were sectioned to obtain bar specimens. Each specimen group (enamel-E, dentin-D) was divided into four subgroups (n=15): S-artificial saliva; 10-10% CP bleaching; 15-15% CP bleaching; 20-20% CP bleaching. CP was applied for six hours daily for two weeks. The specimens were submitted to the a test in a universal testing machine. The data were analyzed by one-way ANOVA and the Tukey post-hoc test and a correlation analysis (r) was performed.Results: For Group E, the mean value (+/- standard-deviation) was 21.86 (+/- 6.03)a, 18.91 (+/- 8.31)ab, 15.43 (+/- 7.44)b and 10.6 (+/- 4.94)c for ES, E10, E15 and E20, respectively. For Group D, the alpha values were 34.73 (+/- 4.68)a, 35.12 (+/- 13.43)a, 29.67 (+/- 6.84)ab and 24.56 (+/- 6.54)b for DS, D10, D15 and D20, respectively. A negative correlation between the CP concentration and mean values was observed for both the enamel (r=-0.95) and dentin (r=-0.85) groups.Conclusion: In the current study, the bond strength of the restoration to enamel and the restoration to dentin were influenced by the application of CP and was dependent on the CP concentration in the bleaching gel.